Biodegradable mesh and film stent
Assignee: Abbott Cardiovascular Systems Inc
•
Filing: 1994-06-27
•
Granted: 1997-05-13
•
Expires: 2014-06-27
Abstract
Abstract The biodegradable mesh and film stent for use in blood vessels is formed of a sheet of a composite mesh material formed of biodegradable high strength polymer fibers bonded together with a second biodegradable adhesive polymer, and laminated on at least one side with a thin film of a third biodegradable polymer. The biodegradable mesh and film material is formed as a sheet and cut in a shape that can be used as a stent, such as a "belt-buckle" type shape, the ends of which can be joined in a contractible, expandable loop. In the method of making the biodegradable composite mesh and film stent, the composite mesh is preferably formed from a weave formed of high strength biodegradable polymeric fibers, and a plurality of low temperature melting biodegradable polymeric fibers. In an alternate embodiment, the high strength fibers are commingled with the low temperature melting fibers. In another alternate embodiment, the high strength fibers are coated with the low temperature melting polymer. The composite mesh is covered on at least one side by a laminating film, and is then cut into the shape of the stent.
Inventors
- 👤 Todd H. Turnlund
- 👤 Robert P. Eury
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:18
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/82; A61F2/92; A61F2/93; A61L; A61L31/00; A61L31/04; A61L31/06; A61L31/14; A61L31/148; B; B32; B32B; B32B37/00; B32B37/04; A61F2/0077; A61F2/02; A61F2/04; A61F2/06; A61F2/07; A61F2002/072; A61F2002/075; A61F2210/00; A61F2210/0004; A61F2210/0076; A61F2220/00; A61F2220/0025; A61F2220/005; A61F2240/00; A61F2240/001; A61F2250/00; A61F2250/0058; A61F2250/0067; B32B2367/00; Y; Y10; Y10S; Y10S623/00; Y10S623/90; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1036; Y10T156/1038; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1369; Y10T442/00; Y10T442/10; Y10T442/102; Y10T442/164
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
101 words
A biodegradable laminated fibrous mesh, comprising: a woven mesh layer having first and second sides, said woven mesh layer being formed from a plurality of fibers of a first biodegradable polymer, said plurality of fibers of said first biodegradable polymer being heat bonded together with a second biodegradable polymer, said second biodegradable polymer melting at a temperature lower than said first biodegradable polymer; and at least one layer of a film of a biodegradable polymer bonded to said woven mesh layer on at least one side of said mesh layer to form a sheet of biodegradable oven mesh and film material.
Claim 2
Dependent Claim
101 words
A biodegradable laminated fibrous mesh, comprising: a woven mesh layer having first and second sides, said woven mesh layer being formed from a plurality of fibers of a first biodegradable polymer, said plurality of fibers of said first biodegradable polymer being heat bonded together with a second biodegradable polymer, said second biodegradable polymer melting at a temperature lower than said first biodegradable polymer; and at least one layer of a film of a biodegradable polymer bonded to said woven mesh layer on at least one side of said mesh layer to form a sheet of biodegradable oven mesh and film material.
Claim 3
Dependent Claim
28 words
The mesh of claim 1, wherein said first biodegradable polymer is selected from the group consisting of polyglycolic acid, poly-L-lactic acid, polyorthoesters, polyanhydrides, polyiminocarbonates, and inorganic calcium phosphate.
Claim 4
Dependent Claim
34 words
The mesh of claim 1, wherein said second biodegradable polymer is selected from the group consisting of polycaprolactone, poly-DL-lactic acid, a combination of poly-L-lactic acid and polycaprolactone, polyorthoesters, aliphatic polycarbonates, polyphosphazenes, and combinations thereof.
Claim 5
Dependent Claim
30 words
The mesh of claim 1, wherein said woven mesh layer of fibers of a first biodegradable polymer has a weave density of from about 10 to about 200 per inch.
Claim 6
Dependent Claim
23 words
The mesh of claim 1, wherein said mesh layer is laminated with a layer of film on both sides to encapsulate the mesh.
Claim 7
Dependent Claim
28 words
The mesh of claim 1, wherein said laminating layer of film is formed from a biodegradable polymer selected from the group consisting of poly-DL-lactic acid and poly-L-lactic acid.
Claim 8
Independent Claim
88 words
A method of making a biodegradable laminated fibrous mesh, comprising the steps of: forming a woven mesh of a plurality of fibers of a first biodegradable polymer heat bonded together with a second biodegradable polymer, said second biodegradable polymer melting at a temperature lower than said first biodegradable polymer; and laminating the woven mesh with at least one laminating film to melt the second low temperature melting biodegradable polymer at a temperature of from about 120° to about 330° F. to form a woven mesh and film laminate.
Claim 9
Independent Claim
88 words
A method of making a biodegradable laminated fibrous mesh, comprising the steps of: forming a woven mesh of a plurality of fibers of a first biodegradable polymer heat bonded together with a second biodegradable polymer, said second biodegradable polymer melting at a temperature lower than said first biodegradable polymer; and laminating the woven mesh with at least one laminating film to melt the second low temperature melting biodegradable polymer at a temperature of from about 120° to about 330° F. to form a woven mesh and film laminate.
Claim 10
Dependent Claim
33 words
The method of claim 7, wherein said step of forming a woven mesh comprises coweaving a fiber of said first biodegradable polymer and a fiber of said second lower temperature melting biodegradable polymer.
Claim 11
Dependent Claim
37 words
The method of claim 7, wherein said step of forming a woven mesh comprises coweaving said plurality of fibers of said first biodegradable polymer and a plurality of fibers of said second low temperature melting biodegradable polymer.
Claim 12
Dependent Claim
37 words
The method of claim 9, wherein said step of coweaving comprises coweaving pairs of said fibers of said first biodegradable polymer and said fibers of said second lower temperature melting biodegradable polymer in a plain weave pattern.
Claim 13
Dependent Claim
59 words
The method of claim 7, wherein said step of forming a woven mesh comprises commingling said plurality of fibers of said first biodegradable polymer and a plurality of fibers of said second lower temperature melting biodegradable polymer to form a plurality of commingled fibers of said first and second polymers, and weaving said commingled fibers in a woven mesh.
Claim 14
Dependent Claim
55 words
The method of claim 7, wherein said step of forming a woven mesh comprises coating said plurality of fibers of said first biodegradable polymer with said second low temperature melting biodegradable polymer, and weaving a woven mesh of said plurality of said first biodegradable polymeric fibers coated with said second low temperature melting biodegradable polymer.
Claim 15
Dependent Claim
27 words
The method of claim 7, wherein said step of laminating said woven mesh is carried out at a temperature of from about 180° to about 270° F.
References Cited (Backward Citations)
US3900632A
Cited
US4110497A
Cited
US4346028A
Cited
EP0108171A1
Cited
EP0144534A2
Cited
US5197977A
Cited
US4633873A
Cited
US4879135A
Cited
US4718907A
Cited
US4768507A
Cited
US4740207A
Cited
US5059211A
Cited
US5085629A
Cited
US5062829A
Cited
US5108755A
Cited
EP0397500A2
Cited
US5084065A
Cited
WO1991017789A1
Cited
US5236447A
Cited
EP0464755B1
Cited
GB2247696A
Cited
US5385580A
Cited
WO1992010218A1
Cited
US5163951A
Cited
WO1993006792A1
Cited
US5167614A
Cited
EP0554082A1
Cited
US5383925A
Cited
EP0621017A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-12 | 2000-11-11 | 2001-05-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-12 | 2004-11-11 | 2005-05-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-12 | 2008-11-11 | 2009-05-13 | $7700.00 | Window Closed / Lapsed |