Porous fluoropolymer alloy and process of manufacture
Assignee: Memron Inc
•
Filing: 1988-11-17
•
Granted: 1990-11-27
•
Expires: 2008-11-17
Abstract
Abstract A porous fluoropolymer alloy material and method of fabrication is provided. The alloy material is fabricated by forming a compressed extrusion billet from two or more fluoropolymer resins capable of being stretched after extrusion and having different stretch characteristics. The fluoropolymer alloy billet is then extruded, stretched and sintered. The resulting material has a microstructure of large nodes interconnected by fibrils all oriented in the direction of stretch and has a higher tensile strength than produceable from previous porous fluoropolymer materials. Also, the resulting material can be made at lower stretch rates and at higher stretch ratios than previously possible without degradation of the material's strength. In one embodiment the resulting product is a self-supporting, tunable asymmetric porous fluoropolymer alloy material having a microstructure comprised of relatively small nodes, short fibrils and small pore size on one surface and relatively large nodes, long fibrils and large pore size on the opposite surface. The microstructure of the material gradually changes from the microstructure of the one surface to the microstructure of the opposite surface through the cross-section of the material's thickness, and all of the fibrils throughout the material are oriented in the direction of stretch.
Inventors
- 👤 Ronnie Browne
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:23
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/12; B; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/09; B29C55/00; B29C55/005; C08L27/18; B29K; B29K2027/00; B29K2027/12; B29K2027/18; C08L2205/00; C08L2205/02
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
63 words
A porous fluoropolymer alloy material, comprising: a first fluoropolymer resin capable of being highly stretched after extrusion; at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluoropolymer resin; wherein said first and second fluoropolymer resins are mechanically bonded to form an alloy; and wherein the material has a microstructure comprising nodes and interconnected by fibrils.
Claim 2
Dependent Claim
63 words
A porous fluoropolymer alloy material, comprising: a first fluoropolymer resin capable of being highly stretched after extrusion; at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluoropolymer resin; wherein said first and second fluoropolymer resins are mechanically bonded to form an alloy; and wherein the material has a microstructure comprising nodes and interconnected by fibrils.
Claim 3
Dependent Claim
15 words
The porous fluoropolymer alloy material of claim 1, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 4
Dependent Claim
28 words
The porous fluoropolymer alloy material of claim 1, wherein said first fluoropolymer resin is a polytetrafluoroethylene resin and at least one second fluoropolymer resin is a perfluoroalkoxytetrafluoroethylene resin.
Claim 5
Dependent Claim
100 words
An asymmetric porous fluoropolymer alloy material, comprising: a first layer of a fluoropolymer resin capable of being highly stretched after extrusion; a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; wherein said first and second layers are mechanically bonded to form an alloy; and wherein the material has a microstructure comprising nodes interconnected by fibrils, and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material.
Claim 6
Dependent Claim
100 words
An asymmetric porous fluoropolymer alloy material, comprising: a first layer of a fluoropolymer resin capable of being highly stretched after extrusion; a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; wherein said first and second layers are mechanically bonded to form an alloy; and wherein the material has a microstructure comprising nodes interconnected by fibrils, and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material.
Claim 7
Dependent Claim
16 words
The asymmetric porous fluoropolymer alloy material of claim 4, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 8
Dependent Claim
33 words
The asymmetric porous fluoropolymer alloy material of claim 4, wherein said resin of said first layer is a polytetrafluoroethylene resin and at least one resin of said second layer is a perfluoroalkoxytetrafluoroethylene resin.
Claim 9
Dependent Claim
48 words
The asymmetric porous fluoropolymer alloy material of claim 4 further comprising: a third layer, disposed between said first and second layers, of a mixture of said resins of said first and second layer; and wherein said first, second and third layers are mechanically bonded to form an alloy.
Claim 10
Dependent Claim
16 words
The asymmetric porous fluoropolymer alloy material of claim 7, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 11
Dependent Claim
100 words
A porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first fluoropolymer resin capable of being highly stretched after extrusion and at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluoropolymer resin; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 12
Dependent Claim
100 words
A porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first fluoropolymer resin capable of being highly stretched after extrusion and at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluoropolymer resin; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 13
Dependent Claim
15 words
The porous fluoropolymer alloy material of claim 9, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 14
Dependent Claim
28 words
The porous fluoropolymer alloy material of claim 9, wherein said first fluoropolymer resin is a polytetrafluoroethylene resin and at least one second fluoropolymer resin is a perfluoroalkoxtytetrafluoroethylene resin.
Claim 15
Dependent Claim
136 words
An asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion and a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said extrudate by heating said at a temperature above the crystalline melting point of said extrudate.
Claim 16
Dependent Claim
136 words
An asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion and a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said extrudate by heating said at a temperature above the crystalline melting point of said extrudate.
Claim 17
Dependent Claim
16 words
The asymmetric porous fluoropolymer alloy material of claim 12, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 18
Dependent Claim
33 words
The asymmetric porous fluoropolymer alloy material of claim 12, wherein said resin of said first layer is a polytetrafluoroethylene resin and at least one resin of said second layer is a perfluoroalkoxytetrafluoroethylene resin.
Claim 19
Dependent Claim
158 words
An asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion, a second layer of a fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer, and a third layer, disposed between said first and second layers, of a mixture of said resins of said first and second layers; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 20
Dependent Claim
158 words
An asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, manufactured from a process comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion, a second layer of a fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer, and a third layer, disposed between said first and second layers, of a mixture of said resins of said first and second layers; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 21
Dependent Claim
16 words
The asymmetric porous fluoropolymer alloy material of claim 15, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 22
Independent Claim
100 words
A method of manufacturing a porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils, comprising the steps of: forming an extrusion billet comprising a first fluoropolymer resin capable of being highly stretched after extrusion and at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluorocarbon resin; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 23
Independent Claim
100 words
A method of manufacturing a porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils, comprising the steps of: forming an extrusion billet comprising a first fluoropolymer resin capable of being highly stretched after extrusion and at least one second fluoropolymer resin capable of being stretched to a lesser degree than said first fluorocarbon resin; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 24
Dependent Claim
12 words
The method of claim 17, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 25
Dependent Claim
25 words
The method of claim 17, wherein said first fluoropolymer resin is a polytetrafluorethylene resin and at least one second fluoropolymer resin is a perfluoroalkoxytetrafluorethylene resin.
Claim 26
Independent Claim
139 words
A method of manufacturing an asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion and a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 27
Independent Claim
139 words
A method of manufacturing an asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion and a second layer of at least one second fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 28
Dependent Claim
12 words
The method of claim 20, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
Claim 29
Dependent Claim
29 words
The method of claim 20 wherein said resin of said first layer is a polytetrafluoroethylene resin and at least one resin of said second layer is a perfluoroalkoxytetrafluoroethelyne resin.
Claim 30
Independent Claim
159 words
A method of manufacturing an asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion, a second layer of a fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer, and a third layer, disposed between the said first and second layers, of a mixture of said resins of said first and second layers; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 31
Independent Claim
159 words
A method of manufacturing an asymmetric porous fluoropolymer alloy material having a microstructure comprising nodes interconnected by fibrils and wherein the size and length of the fibrils change through the cross-section of the material from one surface of the material to the opposite surface of the material, comprising the steps of: forming an extrusion billet comprising a first layer of a fluoropolymer resin capable of being highly stretched after extrusion, a second layer of a fluoropolymer resin capable of being stretched to a lesser degree than said resin of said first layer, and a third layer, disposed between the said first and second layers, of a mixture of said resins of said first and second layers; extruding said extrusion billet to form an extrudate; stretching said extrudate at a temperature below the crystalline melting point of said extrudate; and sintering said stretched extrudate by heating said stretched extrudate to a temperature above the crystalline melting point of said extrudate.
Claim 32
Dependent Claim
12 words
The method of claim 23, wherein said fluoropolymer resins are polytetrafluoroethylene resins.
References Cited (Backward Citations)
US3484503A
Cited
US3764363A
Cited
US3953566A
Cited
US3962153A
Cited
US3936335A
Cited
US3933653A
Cited
US4209480A
Cited
US4049589A
Cited
US4096227A
Cited
US4116892A
Cited
US4061134A
Cited
US4217399A
Cited
US4031283A
Cited
US4225547A
Cited
US4082893A
Cited
US4208745A
Cited
US4025679A
Cited
US4193138A
Cited
US4248924A
Cited
US4277429A
Cited
US4177334A
Cited
US4250138A
Cited
US4110392A
Cited
US4304010A
Cited
US4332035A
Cited
US4283448A
Cited
US4473617A
Cited
US4596837A
Cited
US4482516A
Cited
US4598011A
Cited
US4629650A
Cited
US4546043A
Cited
US4584240A
Cited
US4650815A
Cited
US4737526A
Cited
JPS62201943A
Cited
US4716073A
Cited
US4742085A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-26 | 1994-05-28 | 1994-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-26 | 1998-05-28 | 1998-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-26 | 2002-05-28 | 2002-11-27 | $7700.00 | Window Closed / Lapsed |