Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1979-04-20
•
Granted: 1981-07-07
•
Expires: 1999-04-20
Abstract
Abstract Porous film materials composed of polytetrafluoroethylene having an asymmetric structure are produced by stretching the film using a pair of revolving rolls which are heated to a temperature lower than the melting point of the film. Stretching is produced by revolving the two rolls at different speeds which also tends to produce a compressive force in the thickness of the film. The rolls are heated to different temperatures to produce a temperature difference of preferably 50 DEG C. or more. The combination of the compressive force and the temperature gradient in the thickness of the film is believed to produce the asymmetric structure in the resulting porous film materials which are characterized by a fiber structure in the surface which is different from that in the back.
Inventors
- 👤 Koichi Okita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:12
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/36; B01D39/00; B01D39/08; B01D39/083; B01D39/14; B01D39/16; B01D39/1607; B01D69/00; B01D69/02; B29; B29C; B29C55/00; B29C55/005; C; C08; C08J; C08J5/00; C08J5/18; B29K; B29K2027/00; B29K2027/12; B29K2027/18; B29K2105/00; B29K2105/04; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/14; C08J2327/18; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/249921; Y10T428/249953; Y10T428/249961; Y10T428/31504; Y10T428/3154; Y10T428/31544
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
108 words
A process for producing asymmetric porous film materials which comprises molding a polytetrafluoroethylene containing a liquid lubricating agent by a paste method to form a film, removing the liquid lubricating agent, and generating a temperature difference simultaneously with a compressive force in the thickness direction of the film during stretching the film at a temperature lower than the sintering temperature of the polytetrafluoroethylene using rolls which have a different revolving ratio and which have a temperature difference between each other, whereby tension is caused by the stretching direction of the film while a compressive force corresponding to the tension is caused in the thickness direction of the film.
Claim 2
Dependent Claim
108 words
A process for producing asymmetric porous film materials which comprises molding a polytetrafluoroethylene containing a liquid lubricating agent by a paste method to form a film, removing the liquid lubricating agent, and generating a temperature difference simultaneously with a compressive force in the thickness direction of the film during stretching the film at a temperature lower than the sintering temperature of the polytetrafluoroethylene using rolls which have a different revolving ratio and which have a temperature difference between each other, whereby tension is caused by the stretching direction of the film while a compressive force corresponding to the tension is caused in the thickness direction of the film.
Claim 3
Dependent Claim
51 words
A process for producing asymmetric porous film materials as set forth in claim 1, wherein the step of stretching is carried out at least twice using rolls having a different revolving ratio, and at least one stretching step is carried out with the rolls having a temperature difference between each other.
Claim 4
Dependent Claim
39 words
A process for producing asymmetric porous film materials as set forth in claim 1, wherein the step of stretching is carried out using rolls having a different revolving ratio which have a temperature difference of at least 50° C.
Claim 5
Dependent Claim
56 words
A process for producing asymmetric porous film materials as set forth in claim 1, wherein the temperature of the low speed roll in the rolls having a different revolving ratio is 230° C. or less and the temperature of the high-speed roll is 250° C. or more but lower than the sintering temperature of the polytetrafluoroethylene.
References Cited (Backward Citations)
US2642625A
Cited
US3281511A
Cited
US3953566A
Cited
US3816886A
Cited
US3796785A
Cited
US4049589A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-06 | 1985-01-05 | 1985-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-06 | 1989-01-05 | 1989-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-06 | 1993-01-05 | 1993-07-07 | $7700.00 | Window Closed / Lapsed |