Abstract
Abstract The present invention provides porous polytetrafluoroethylene ("PTFE") products having fine pores and high porosity, the pore diameter being less than about 1,500A, generally ranging from about 100A to 1,000A. The process for the manufacture of these products comprises: (a) shaping of a lubricated PTFE mixture, by extrusion and/or rolling; (b) a first stretching of the shaped mass while in an unsintered state; (c) free sintering of the stretched mass at a temperature above 327 DEG C; and (d) a second stretching of the sintered mass. These porous PTFE products are suitable for use as gas separators, diaphragms, filters, and other applications.
Inventors
- 👤 Etsuo Yamazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 23:10
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/07; B29C48/08; B29C55/00; B29C55/005; B29C55/02; B29C55/04; B29C55/06; B29C55/065; B29C48/09; B29C48/10; B29K; B29K2027/00; B29K2027/12; B29K2027/18; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18; Y; Y10; Y10S; Y10S264/00; Y10S264/47
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
144 words
A process for producing a porous product of sintered polytetrafluoroethylene, having a pore size of less than 2000A, which comprises the following steps performed in sequence: (a) shaping an unsintered polytetrafluoroethylene mixture, containing a liquid lubricant, by extrusion, below the crystalline melt point of the polytetrafluoroethylene, to form a shaped extrudate; (b) a first stretching of said shaped extrudate in at least one direction at a temperature below about 327° C; (c) free sintering by heating said stretched shaped extrudate to a temperature above 327° C, said stretched shaped article being unrestrained and allowed to shrink to almost the same size it had been before stretching; and (d) a second stretching of said sintered, stretched, shaped extrudate at a temperature below the crystalline melt point at a speed in the range of about 1 × 10 2 to about 2 × 10 6 mm/min.
Claim 2
Dependent Claim
144 words
A process for producing a porous product of sintered polytetrafluoroethylene, having a pore size of less than 2000A, which comprises the following steps performed in sequence: (a) shaping an unsintered polytetrafluoroethylene mixture, containing a liquid lubricant, by extrusion, below the crystalline melt point of the polytetrafluoroethylene, to form a shaped extrudate; (b) a first stretching of said shaped extrudate in at least one direction at a temperature below about 327° C; (c) free sintering by heating said stretched shaped extrudate to a temperature above 327° C, said stretched shaped article being unrestrained and allowed to shrink to almost the same size it had been before stretching; and (d) a second stretching of said sintered, stretched, shaped extrudate at a temperature below the crystalline melt point at a speed in the range of about 1 × 10 2 to about 2 × 10 6 mm/min.
Claim 3
Dependent Claim
23 words
The process according to claim 1 in which said first stretching is carried out at a temperature between about 20° and 200° C.
Claim 4
Dependent Claim
34 words
The process according to claim 1 in which said shaped extrudate is stretched in said first stretching to a final length of about 1.2 to 3.5 times the initial length of said shaped extrudate.
Claim 5
Dependent Claim
21 words
The process according to claim 1 in which said sintering is carried out at a temperature between 327° and 400° C.
Claim 6
Dependent Claim
27 words
The process according to claim 1 in which said second stretching imparts an increase in length of said shaped, stretched, sintered extrudate of from 100 to 1,000%.
Claim 7
Dependent Claim
18 words
The process according to claim 1 in which said shaping of an unsintered polytetrafluoroethylene mixture is by rolling.
References Cited (Backward Citations)
US2776465A
Cited
DE2413221A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |