Extrusion process of polytetrafluoroethylene tubing materials and apparatus therefor
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1978-09-22
•
Granted: 1980-09-30
•
Expires: 1998-09-22
Abstract
Abstract This application relates to a paste extrusion process using a ram type extruder wherein at least one, preferably both, of the die and mandrel of the extruder are rotated, in opposite directions when both are rotated. In preferred embodiments, the material being extruded is polytetrafluoroethylene, the mandrel has a smooth surface and the end portion of the die is heated.
Inventors
- 👤 Koichi Okita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:48
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/36; B01D39/00; B01D39/14; B01D39/16; B01D39/1692; B01D63/00; B01D63/06; B01D63/061; B01D67/00; B01D67/0002; B01D67/002; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/09; B29C48/25; B29C48/30; B29C48/32; B29C48/33; B29C48/36; B29C48/475; B29C55/00; B29C55/22; B29C67/00; B29C67/0003; B29C67/02; B29C67/04; F; F16; F16L; F16L11/00; F16L11/04; F16L11/06; B01D2239/00; B01D2239/04; B01D2239/0407; B01D2239/06; B01D2239/065; B01D2239/069; B01D2239/0695; B01D2239/10; B29K; B29K2027/00; B29K2027/12; B29K2027/18
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
165 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel having a constant diameter approximately equal to the inside diameter of the extruded tubing material and a die connected to a cylinder along and within which a ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, with the opening diameter of said die-land being smaller than the opening diameter of said die insert terminating into said die-land, rotating at least an end portion of the die in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 2
Independent Claim
165 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel having a constant diameter approximately equal to the inside diameter of the extruded tubing material and a die connected to a cylinder along and within which a ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, with the opening diameter of said die-land being smaller than the opening diameter of said die insert terminating into said die-land, rotating at least an end portion of the die in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 3
Dependent Claim
39 words
An extrusion method as set forth in claim 1, wherein the difference between the temperature of the mixture in the cylinder and the temperature of said heated portion of the die is equal to or larger than 50° C.
Claim 4
Dependent Claim
19 words
An extrusion method as set forth in claim 1, wherein said center mandrel is rotated in the opposite direction.
Claim 5
Dependent Claim
39 words
An extrusion method as set forth in claim 3, wherein the difference between the temperature of the mixture in the cylinder and the temperature of said heated portion of the die is equal to or larger than 50° C.
Claim 6
Independent Claim
176 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel having a portion tapering from a large diameter above a die to a relatively smaller diameter approximately equal to the inside diameter of the extruded tubing material, said die connected to a cylinder along and within which a ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, with the opening diameter of said die-land being smaller than the opening diameter of said die insert terminating into said die-land, rotating at least an end portion of the die in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 7
Independent Claim
176 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel having a portion tapering from a large diameter above a die to a relatively smaller diameter approximately equal to the inside diameter of the extruded tubing material, said die connected to a cylinder along and within which a ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, with the opening diameter of said die-land being smaller than the opening diameter of said die insert terminating into said die-land, rotating at least an end portion of the die in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 8
Dependent Claim
25 words
An extrusion method as set forth in claim 5, wherein said central mandrel is rotated in the direction opposite to that of the die rotation.
Claim 9
Dependent Claim
39 words
An extrusion method as set forth in claim 5, wherein the difference between the temperature of the mixture in the cylinder and the temperature of said heated portion of the die is equal to or larger than 50° C.
Claim 10
Dependent Claim
39 words
An extrusion method as set forth in claim 6, wherein the difference between the temperature of the mixture in the cylinder and the temperature of said heated portion of the die is equal to or larger than 50° C.
Claim 11
Independent Claim
127 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel and a die connected to a cylinder along and within which the ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, rotating at least the smooth central mandrel in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 12
Independent Claim
127 words
A method of extruding a tubing material from a mixture of polytetrafluoroethylene and a lubricant using a ram type extruding apparatus having a smooth central mandrel and a die connected to a cylinder along and within which the ram is slidable to force the mixture into the die, comprising the steps of employing said die having a die insert terminating into a die-land, rotating at least the smooth central mandrel in one direction during the extrusion of the mixture into a tubing material and thermally expanding said tubing material in the die by heating at least a portion of the die to a temperature higher than the temperature of the mixture in the cylinder, whereby fibrous-state formation in the direction perpendicular to the extrusion direction is accelerated.
Claim 13
Dependent Claim
39 words
An extrusion method as set forth in claim 9, wherein the difference between the temperature of the mixture in the cylinder and the temperature of said heated portion of the die is equal to or larger than 50° C.
Claim 14
Dependent Claim
40 words
An extrusion method as set forth in claim 9, said smooth central mandrel having a portion tapering from a large diameter above the die to a relatively smaller diameter approximately equal to the inside diameter of the extruded tubing material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-30 | 1984-03-31 | 1984-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-30 | 1988-03-31 | 1988-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-30 | 1992-03-31 | 1992-09-30 | $7700.00 | Window Closed / Lapsed |