Very highly stretched polytetrafluoroethylene and process therefor
Assignee: Gore Enterprise Holdings Inc
•
Filing: 1973-06-14
•
Granted: 1976-06-08
•
Expires: 1993-06-14
Abstract
Abstract This invention provides a tetrafluoroethylene polymer in a porous form which has an amorphous content exceeding about 5% and which has a micro-structure characterized by nodes interconnected by fibrils. The material has high porosity and high strength. It can be used to produce all kinds of shaped articles such as films, tubes, rods, and continuous filaments. Laminations can be employed and impregnation and bonding can readily be used to produce a large variety of articles. Compressed articles of very high strength can also be produced from these porous forms.
Inventors
- 👤 Robert Walton Gore
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 19:26
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/0025; B01D67/0027; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/36; B29; B29C; B29C55/00; B29C55/005; B29C55/02; B29C55/10; B29C55/12; B29C55/18; C; C08; C08J; C08J5/00; C08J5/12; C08J5/124; C08J5/18; H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/44; H01B3/443; H01B3/445; B29K; B29K2027/00; B29K2027/12; B29K2027/18; B29K2105/00; B29K2105/04; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2973; Y10T428/2975; Y10T428/31504; Y10T428/3154; Y10T428/31544
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
101 words
A porous product consisting essentially of polytetrafluoroethylene produced by a process comprising: a. stretching an unsintered extrudate of said polymer made by a paste-forming extrusion technique, said stretching being performed after removal of lubricant extrusion aid from said extrudate; b. said stretching being performed at a rate exceeding about 2000% per second; c. said stretching being performed at an elevated temperature but below the melt point of said polymer; and, d. said extrudate being stretched to such an extent that the final length of the stretched product after stretching exceeds 50 times the original length of said extrudate prior to stretching.
Claim 2
Dependent Claim
101 words
A porous product consisting essentially of polytetrafluoroethylene produced by a process comprising: a. stretching an unsintered extrudate of said polymer made by a paste-forming extrusion technique, said stretching being performed after removal of lubricant extrusion aid from said extrudate; b. said stretching being performed at a rate exceeding about 2000% per second; c. said stretching being performed at an elevated temperature but below the melt point of said polymer; and, d. said extrudate being stretched to such an extent that the final length of the stretched product after stretching exceeds 50 times the original length of said extrudate prior to stretching.
Claim 3
Dependent Claim
19 words
The product produced according to claim 1 in which said final length is about 56.5 times said original length.
Claim 4
Dependent Claim
18 words
The product produced according to claim 1 in which said final length exceeds 100 times said original length.
Claim 5
Dependent Claim
19 words
The product produced according to claim 1 in which said final length is about 120 times said original length.
Claim 6
Dependent Claim
18 words
The product produced according to claim 1 in which said final length exceeds 200 times said original length.
Claim 7
Dependent Claim
19 words
The product produced according to claim 1 in which said final length is about 240 times said original length.
Claim 8
Dependent Claim
18 words
The product produced according to claim 1 in which said final length exceeds 1500 times said original length.
Claim 9
Dependent Claim
19 words
The product produced according to claim 1 in which said final length is about 1760 times said original length.
Claim 10
Dependent Claim
23 words
The product of claim 1 which has never been heated to a temperature above 327°C and has a crystallinity greater than about 98%.
Claim 11
Dependent Claim
23 words
The product of claim 1 which has been heated following stretching to a temperature above 327°C and has a crystallinity below about 98%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |