US7396484B2
Expired / Lapsed
US
⏱️ 0.0 years remaining
Methods of fabricating complex blade geometries from silicon wafers and strengthening blade geometries
Assignee: Beaver Visitec International US Inc
•
Filing: 2005-04-29
•
Granted: 2008-07-08
•
Expires: 2025-04-29
Abstract
Abstract Ophthalmic surgical blades are manufactured from either a single crystal or poly-crystalline material, preferably in the form of a wafer. The method comprises preparing the single crystal or poly-crystalline wafers by mounting them and etching trenches into the wafers using one of several processes. Methods for machining the trenches, which form the bevel blade surfaces, include a diamond blade saw, laser system, ultrasonic machine, a hot forge press and a router. Other processes include wet etching (isotropic and anisotropic) and dry etching (isotropic and anisotropic, including reactive ion etching), and combinations of these etching steps. The wafers are then placed in an etchant solution which isotropically etches the wafers in a uniform manner, such that layers of crystalline or poly-crystalline material are removed uniformly, producing single, double or multiple bevel blades. Nearly any angle can be machined into the wafer, and the machined angle remains after etching. The resulting radii of the blade edges is 5-500 nm, which is the same caliber as a diamond edged blade, but manufactured at a fraction of the cost. A range of radii may be 30 to 60 nm, with a specific implementation being about 40 nm. The blade profile may have an angle of, for example, about 60°. The ophthalmic surgical blades can be used for cataract and refractive surgical procedures, as well as microsurgical, biological and non-medical, non-biological purposes. Surgical and non-surgical blades and mechanical devices manufactured as described herein can also exhibit substantially smoother surfaces than metal blades.
Inventors
- 👤 Vadim M. Daskal
- 👤 Joseph F. Keenan
- 👤 James Joseph Hughes
- 👤 Attila E. Kiss
- 👤 Susan M. Chavez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:20
CPC Classifications
A; A61; A61B; A61B17/00; A61B17/32; A61B17/3209; A61B17/3211
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
73 words
A method for manufacturing a cutting device from a wafer of crystalline material, comprising: forming a trench in the wafer of crystalline material on a first side of a crystalline material, the trench comprising at least one blade profile of a blade; and isotropically etching at least the first side of the crystalline material to form at least one cutting edge comprising at least a portion of the at least one blade profile.
Claim 2
Independent Claim
73 words
A method for manufacturing a cutting device from a wafer of crystalline material, comprising: forming a trench in the wafer of crystalline material on a first side of a crystalline material, the trench comprising at least one blade profile of a blade; and isotropically etching at least the first side of the crystalline material to form at least one cutting edge comprising at least a portion of the at least one blade profile.
Claim 3
Dependent Claim
45 words
The method according to claim 1 , further comprising forming at least one side edge of the blade in the crystalline material; and wherein the etching of the at least the first side of the crystalline material comprises etching the at least one side edge.
Claim 4
Dependent Claim
18 words
The method according to claim 2 , wherein the at least one side edge comprises a non-linear portion.
Claim 5
Dependent Claim
14 words
The method according to claim 3 , wherein the non-linear portion is horseshoe shaped.
Claim 6
Dependent Claim
55 words
The method according to claim 1 , wherein: the forming of the trench comprises forming a first patterns comprising a first bevel; and the etching of the at least the first side of the crystalline material comprises etching the first bevel to form at least a first portion of the at least one cutting edge.
Claim 7
Dependent Claim
53 words
The method according to claim 5 , wherein the forming of the trench comprises forming a second pattern comprising a second bevel; and the etching of the at least the first side of the crystalline material comprises etching the second bevel to form at least a second portion of a second cutting edge.
Claim 8
Dependent Claim
36 words
The method according to claim 6 , wherein the first pattern and the second pattern are positioned on the first side of the crystalline material, whereby the first bevel and the second bevel are spaced apart.
Claim 9
Dependent Claim
35 words
The method according to claim 7 , wherein at least one of the first and second patterns comprises a plurality of bevels formed on the first side of the crystalline material in a snowflake pattern.
Claim 10
Dependent Claim
32 words
The method according to claim 1 , further comprising forming at least one slot in the crystalline material, the slot comprising at least a portion of a non-cutting edge of the blade.
Claim 11
Dependent Claim
27 words
The method according to claim 9 , wherein the forming of the at least one slot comprises maximizing the length of the non-cutting edge of the blade.
Claim 12
Dependent Claim
90 words
The method according to claim 1 , wherein the etching step comprises: placing the wafer of crystalline material with at least one blade profile on a wafer boat; immersing the wafer boat and wafer of crystalline material with at least one blade profile in an isotropic acid bath; and etching the crystalline material in a uniform manner such that the crystalline material is removed in a uniform manner on an exposed surface, whereby a sharp cutting device edge is etched in the shape of the at least one blade profile.
Claim 13
Dependent Claim
23 words
The method according to claim 11 , wherein the isotropic acid bath comprises: a mixture of hydrofluoric acid, nitric acid and acetic acid.
Claim 14
Dependent Claim
22 words
The method according to claim 11 , wherein the isotropic acid bath comprises: a mixture of hydrofluoric acid, nitric acid and water.
Claim 15
Dependent Claim
93 words
The method according to claim 1 , wherein the etching step comprises: placing the wafer of crystalline material with at least one blade profile in a wafer boat; spraying a spray etchant at the wafer boat and wafer of crystalline material with at least one blade profile; and etching the crystalline material in a uniform manner with the spray etchant such that the crystalline material is removed in a uniform manner on an exposed surface, whereby a sharp cutting device edge is etched in the shape of the at least one blade profile.
Claim 16
Dependent Claim
108 words
The method according to claim 1 , wherein the etching step comprises: placing the wafer of crystalline material with at least one blade profile on a wafer boat; immersing the wafer boat and wafer of crystalline material with at least one blade profile in an isotropic xenon difluoride, sulfur hexafluoride or similar fluorinated gas environment; and etching the crystalline material in a uniform manner with the isotropic xenon difluoride, sulfur hexafluoride or similar fluorinated gas such that the crystalline material is removed in a uniform manner on an exposed surface, whereby a sharp cutting device edge is etched in the shape of the at least one blade profile.
Claim 17
Dependent Claim
93 words
The method according to claim 1 , wherein the etching step comprises: placing the wafer of crystalline material with at least one blade profile in a wafer boat; immersing the wafer boat and wafer of crystalline material with at least one blade profile in an electrolytic bath; and etching the crystalline material in a uniform manner with the electrolytic bath such that the crystalline material is removed in a uniform manner on an exposed surface, whereby a sharp cutting device edge is etched in the shape of the at least one blade profile.
Claim 18
Dependent Claim
36 words
The method according to claim 2 , wherein the forming of the at least one side edge comprises delivering energy to the crystalline material from a laser beam from an excimer laser or a laser waterjet.
Claim 19
Dependent Claim
35 words
The method according to claim 9 , wherein the forming of the at least one slot comprises delivering energy to the crystalline material from a laser beam from an excimer laser or a laser waterjet.
Claim 20
Dependent Claim
13 words
The method according to claim 1 , wherein the crystalline material comprises silicon.
Claim 21
Dependent Claim
90 words
The method according to claim 1 , wherein the forming of the trench comprises: forming a photoresist layer on the first side of the crystalline material; patterning the photoresist layer, whereby at least a portion of the photoresist layer is removed from at least a first portion of the first side of the crystalline material; partially etching the first portion of the first side of the crystalline material to form the trench; and removing the photo-resist layer before the etching of the at least first side of the crystalline material.
Claim 22
Dependent Claim
43 words
The method according to claim 20 , wherein the partially etching comprises at least one of an isotropic reactive ion etching of the first portion of the crystalline material and an anisotropic reactive ion etching of the first portion of the crystalline material.
Claim 23
Independent Claim
130 words
A method for manufacturing a cutting device from a crystalline material, the method comprising: making at least one blade profile in a wafer of a first material; and isotropically etching the wafer to form at least one blade comprising the at least one blade profile; wherein the making of the at least one blade profile comprises: forming a photoresist layer on the first side of the crystalline material; patterning the photoresist layer, whereby at least a portion of the photoresist layer is removed from at least a first portion of the first side of the crystalline material; partially etching the first portion of the first side of the crystalline material to form the at least one blade profile; and removing the photo-resist layer before the isotropically etching of the wafer.
Claim 24
Independent Claim
130 words
A method for manufacturing a cutting device from a crystalline material, the method comprising: making at least one blade profile in a wafer of a first material; and isotropically etching the wafer to form at least one blade comprising the at least one blade profile; wherein the making of the at least one blade profile comprises: forming a photoresist layer on the first side of the crystalline material; patterning the photoresist layer, whereby at least a portion of the photoresist layer is removed from at least a first portion of the first side of the crystalline material; partially etching the first portion of the first side of the crystalline material to form the at least one blade profile; and removing the photo-resist layer before the isotropically etching of the wafer.
Claim 25
Dependent Claim
43 words
The method according to claim 22 , wherein the partially etching comprises at least one of an isotropic reactive ion etching of the first portion of the crystalline material and an anisotropic reactive ion etching of the first portion of the crystalline material.
Claim 26
Dependent Claim
80 words
The method according to claim 22 , wherein the isotropic etching comprises: placing the wafer comprising the at least one blade profile on a wafer boat; immersing the wafer boat and the wafer comprising the at least one blade profile in an isotropic acid bath; and etching the wafer such that the first material of the wafer is removed on any exposed surface, whereby a sharp blade edge is etched in the shape of the at least one blade profile.
Claim 27
Dependent Claim
23 words
The method according to claim 24 , wherein the isotropic acid bath comprises at least one of a hydrofluoric acid and nitric acid.
Claim 28
Dependent Claim
22 words
The method according to claim 25 , wherein the isotropic acid bath further comprises at least one of acetic acid and water.
Claim 29
Dependent Claim
83 words
The method according to claim 22 , wherein the isotropic etching comprises: placing the wafer comprising the at least one blade profile in a wafer boat; spraying a spray etchant at the wafer boat and the wafer comprising the at least one blade profile; and etching the wafer with the spray etchant such that the first material of the wafer is removed on any exposed surface, whereby a sharp blade edge is etched in the shape of the at least one blade profile.
Claim 30
Dependent Claim
15 words
The method according to claim 22 , further comprising singulating the at least one blade.
References Cited (Backward Citations)
US3543402A
Cited
US3803963A
Cited
US3831466A
Cited
US3894337A
Cited
GB1393611A
Cited
US3857488A
Cited
US3834265A
Cited
US3942231A
Cited
US4091813A
Cited
US4122602A
Cited
US4232676A
Cited
US4219025A
Cited
US4248231A
Cited
US4231371A
Cited
US4579022A
Cited
US4318537A
Cited
US4409659A
Cited
US4413970A
Cited
US4688570A
Cited
US4444102A
Cited
US4611400A
Cited
US4468282A
Cited
US4566465A
Cited
US4629373A
Cited
US4551192A
Cited
US4509651A
Cited
US4534827A
Cited
US4581969A
Cited
US4697489A
Cited
US4955894A
Cited
WO1986002868A1
Cited
US4634496A
Cited
US4777096A
Cited
US4587202A
Cited
JPS61210179A
Cited
US4719915A
Cited
US4671849A
Cited
DE3526951A1
Cited
US4790812A
Cited
US4735920A
Cited
US4686980A
Cited
US4735202A
Cited
JPS6392345U
Cited
US4872947A
Cited
US4798000A
Cited
US4846250A
Cited
US4934103A
Cited
US4740410A
Cited
US4793218A
Cited
US4808260A
Cited
US4862890A
Cited
US4958539A
Cited
US4911782A
Cited
US4850353A
Cited
US5032243A
Cited
US4922903A
Cited
US4916002A
Cited
US4980021A
Cited
US5019035A
Cited
US5193311A
Cited
US5082254A
Cited
US4948461A
Cited
US5176628A
Cited
US5021364A
Cited
US5121660A
Cited
US5077901A
Cited
US5048191A
Cited
US5201992A
Cited
US5056277A
Cited
US5100506A
Cited
US5142785A
Cited
US5166520A
Cited
US5266528A
Cited
US5317938A
Cited
US5217477A
Cited
US5295305A
Cited
US5295305B1
Cited
US5222967A
Cited
US5222967B1
Cited
US5258002A
Cited
US5579583A
Cited
US5683592A
Cited
US5342370A
Cited
US5651782A
Cited
US5728089A
Cited
US5627109A
Cited
US5619889A
Cited
US5842387A
Cited
US5474532A
Cited
US5879326A
Cited
US5609778A
Cited
US5742026A
Cited
US5972154A
Cited
US5562693A
Cited
US5998234A
Cited
US6151786A
Cited
US5893846A
Cited
US6117347A
Cited
US6687990B2
Cited
US6401580B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2011-07-08 | 2012-01-07 | 2012-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2015-07-08 | 2016-01-07 | 2016-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2019-07-08 | 2020-01-07 | 2020-07-08 | $7700.00 | Window Closed / Lapsed |