US5201992A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making tapered microminiature silicon structures
Assignee: STANFORD UNIVERSITY OTL LLC
•
Filing: 1991-10-08
•
Granted: 1993-04-13
•
Expires: 2011-10-08
Abstract
Abstract Tapered silicon structures, of interest for use, e.g., in atomic force microscopes, in field-emission devices, and in solid state devices are made using silicon processing technology. Resulting tapered structures have, at their tip, a radius of curvature of 10 nanometers or less. Such preferred silicon structures are particularly suited as electron emitters in display devices.
Inventors
- 👤 Nicholas C. Andreadakis
- 👤 Robert B. Marcus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:38
CPC Classifications
G; G01; G01Q; G01Q70/00; G01Q70/08; G01Q70/10; B; B82; B82Y; B82Y35/00; G01Q60/00; G01Q60/24; G01Q60/38; H; H01; H01J; H01J9/00; H01J9/02; H01J9/022; H01J9/025; H01J2209/00; H01J2209/02; H01J2209/022; H01J2209/0223; H01J2209/0226
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
106 words
A method of making a tapered silicon structure which terminates in an apex whose radius of curvature is less than 10 nanometers comprising the steps of providing a silicon protuberance having a tapered shape comprising an essentially flat top portion whose width is of the order of 500 nanometers or less and having concave sidewalls such that, at a distance equal to said width from said flat top portion, tangents to first and second facing sidewalls form an angle of the order of 30 degrees or less, and exposing said silicon protuberance to an essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C.
Claim 2
Independent Claim
106 words
A method of making a tapered silicon structure which terminates in an apex whose radius of curvature is less than 10 nanometers comprising the steps of providing a silicon protuberance having a tapered shape comprising an essentially flat top portion whose width is of the order of 500 nanometers or less and having concave sidewalls such that, at a distance equal to said width from said flat top portion, tangents to first and second facing sidewalls form an angle of the order of 30 degrees or less, and exposing said silicon protuberance to an essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C.
Claim 3
Dependent Claim
62 words
The method of claim 1 wherein said environment consists essentially of an atmosphere in which oxygen pressure is at least 50 percent and water vapor pressure is less than 1 percent of total pressure and comprising the further steps of removing oxide formed by exposing said protuberance to said environment and again exposing said protuberance to said environment subsequent to said removing.
Claim 4
Dependent Claim
26 words
The method of claim 2 further comprising the step of exposing said protuberance to a second oxidizing environment at a temperature greater tan 1050 degrees C.
Claim 5
Independent Claim
79 words
A method of making a silicon structure comprising an array of a plurality of apices of uniform sharpness having radii of curvature of less than 10 nanometers comprising the steps of exposing an array of silicon protuberances to an essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C., stripping surface oxides from said protuberances, and subsequently repeating said steps of exposing and stripping to attain the enhanced sharpness and uniformity of said apices in said array.
Claim 6
Independent Claim
79 words
A method of making a silicon structure comprising an array of a plurality of apices of uniform sharpness having radii of curvature of less than 10 nanometers comprising the steps of exposing an array of silicon protuberances to an essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C., stripping surface oxides from said protuberances, and subsequently repeating said steps of exposing and stripping to attain the enhanced sharpness and uniformity of said apices in said array.
Claim 7
Dependent Claim
45 words
The method of claim 4 further comprising the step of exposing said array of protuberances to a humid oxidizing environment at a temperature above 1050 degrees centigrade prior to said dry oxidizing exposure step to provide an initial uniformity of said protuberances in said array.
Claim 8
Dependent Claim
39 words
The method of claim 4 comprising the further step of decreasing apex sharpness without loss of uniformity of said apices in said array be exposing said array to an oxidizing environment at a temperature which exceeds 1050 degrees C.
Claim 9
Independent Claim
98 words
A method for making a tapered silicon structure, comprising a step of exposing a silicon protuberance to a first, essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C., said silicon protuberance, prior to said step, having a tapered shape comprising an essentially flat top portion whose width, here called delta, is of the order of 500 nanometers or less, and said silicon protuberance having concave sidewalls such that, at a distance delta from said flat top portion, tangents to first and second facing sidewalls form an angle of the order of 30 degrees or less.
Claim 10
Independent Claim
98 words
A method for making a tapered silicon structure, comprising a step of exposing a silicon protuberance to a first, essentially dry oxidizing environment at a temperature not exceeding 1050 degrees C., said silicon protuberance, prior to said step, having a tapered shape comprising an essentially flat top portion whose width, here called delta, is of the order of 500 nanometers or less, and said silicon protuberance having concave sidewalls such that, at a distance delta from said flat top portion, tangents to first and second facing sidewalls form an angle of the order of 30 degrees or less.
Claim 11
Dependent Claim
36 words
The method of claim 7, wherein said environment consists essentially of an atmosphere in which oxygen pressure is greater than or equal to 50 percent and water-vapor pressure is less than 1 percent of total pressure.
Claim 12
Dependent Claim
21 words
The method of claim 7, further comprising a step of removing oxide formed by exposing said protuberance to said first environment.
Claim 13
Dependent Claim
21 words
The method of claim 9, comprising a further step of exposing said protuberance to said first environment subsequent to said removing.
Claim 14
Dependent Claim
14 words
The method of claim 10 wherein said steps of exposing and removing are repeated.
Claim 15
Dependent Claim
15 words
The method of claim 9, further comprising a step of replacing surface silicon by tungsten.
Claim 16
Dependent Claim
26 words
The method of claim 9, further comprising a step of exposing said protuberance to a second oxidizing environment at a temperature greater than 1050 degrees C.
References Cited (Backward Citations)
US2817002A
Cited
US3852595A
Cited
US3970887A
Cited
SU549039A1
Cited
US4307507A
Cited
US4578614A
Cited
US4513308A
Cited
US4766340A
Cited
US4685996A
Cited
US4721885A
Cited
US4940916A
Cited
US4940916B1
Cited
US4968382A
Cited
US5100355A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-12 | 1996-10-12 | 1997-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-12 | 2000-10-12 | 2001-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-12 | 2004-10-12 | 2005-04-13 | $7700.00 | Window Closed / Lapsed |