Method of providing an adherent metal coating on an epoxy surface
Assignee: AT&T Inc
•
Filing: 1983-10-20
•
Granted: 1986-04-15
•
Expires: 2003-10-20
Abstract
Abstract A method of forming adherent metallized coatings on a substrate which is useful for the manufacture of printed circuit boards as well as other metal coated articles involves providing the substrate with a rubber-modified epoxy surface or coating, sputter etching at least 50 A. from the surface followed by vacuum depositing an adherent thin metal film of Cr, Ni, Ni-V alloy, Pt, Pd or Ti onto the substrate. Another metal layer is then provided over the adherent thin film.
Inventors
- 👤 Daniel J. Shanefield
- 👤 Fred W. Verdi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:50
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; C23C14/02; C23C14/021; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381; H05K3/386; H05K3/388; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0133; H05K2203/00; H05K2203/09; H05K2203/095; H05K3/10; H05K3/108; H05K3/40; H05K3/4038; H05K3/4076; H05K3/42; H05K3/425; H05K3/426
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
95 words
A method of metallizing an article having a surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprises the steps of: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing a thin adherent base metal film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the surface of the epoxy resin; and (c) depositing a primary metal film over the thin base metal film.
Claim 2
Independent Claim
95 words
A method of metallizing an article having a surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprises the steps of: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing a thin adherent base metal film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the surface of the epoxy resin; and (c) depositing a primary metal film over the thin base metal film.
Claim 3
Dependent Claim
37 words
The method recited in claim 1 wherein the adherent base metal film is vacuum deposited without breaking the vacuum after sputter etching and further wherein the thicker primary metal is also deposited by means of vacuum deposition.
Claim 4
Dependent Claim
17 words
The method recited in claim 1 wherein the thin base metal film is from 100A. to 10,000A.
Claim 5
Dependent Claim
18 words
The method recited in claim 14 wherein the thin base metal film is in the order of 1,000A.
Claim 6
Dependent Claim
16 words
The method recited in claim 1 wherein metallization is in the form of a predetermined pattern.
Claim 7
Dependent Claim
23 words
The method recited in claim 1 wherein a final thick metal coating is applied to the substrate by means of electroless or electroplating.
Claim 8
Dependent Claim
32 words
The method recited in claim 2 wherein the thin base metal film is applied by means of magnetron sputter etching and wherein said base metal film consists essentially of a nickel-vanadium alloy.
Claim 9
Independent Claim
119 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing a thin film of a metal base selected from the group consisting of Cr, NI, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; and (d) forming a circuit pattern by means of etching unwanted portions of the previously applied metal films.
Claim 10
Independent Claim
119 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing a thin film of a metal base selected from the group consisting of Cr, NI, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; and (d) forming a circuit pattern by means of etching unwanted portions of the previously applied metal films.
Claim 11
Dependent Claim
18 words
The method recited in claim 8 wherein said thin base metal film is from 100A. to 10,000A. thick.
Claim 12
Independent Claim
159 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging an developing a photoresist in the form of said pattern over the substrate surface; (e) etching away the exposed metal portions not covered by photoresist; and (f) electroplating a thick layer of copper over the remaining metal, the thickness of which is at least sufficient to provide good electrical conductivity.
Claim 13
Independent Claim
159 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging an developing a photoresist in the form of said pattern over the substrate surface; (e) etching away the exposed metal portions not covered by photoresist; and (f) electroplating a thick layer of copper over the remaining metal, the thickness of which is at least sufficient to provide good electrical conductivity.
Claim 14
Independent Claim
163 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromtic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging and developing a photoresist in the form of said pattern over the substrate surface; (e) electroplating a thick copper layer over the expose metal; (f) applying a tin alloy etch resist over the thick copper layer; (g) stripping the photoresist; and (h) etching away the underlying primary metal layer and thin base metal film.
Claim 15
Independent Claim
163 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromtic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging and developing a photoresist in the form of said pattern over the substrate surface; (e) electroplating a thick copper layer over the expose metal; (f) applying a tin alloy etch resist over the thick copper layer; (g) stripping the photoresist; and (h) etching away the underlying primary metal layer and thin base metal film.
Claim 16
Independent Claim
147 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging and developing a photoresist in the form of said pattern over the substrate surface; (e) electrolessly plating a thick copper layer over the exposed metal; (f) stripping the photoresist; and (g) etching away the metal underlying the photoresist.
Claim 17
Independent Claim
147 words
A method of forming a circuit pattern on a substrate having a plurality of spaced through-holes and a substrate surface comprising a rubber-modified epoxy resin or an epoxy resin having a high degree of unsaturation excluding aromatic unsaturation comprising the steps: (a) sputter etching the substrate so as to remove at least 50A. from the surface of the substrate; (b) vacuum depositing an adherent thin film of a metal selected from the group consisting of Cr, Ni, Ni-V alloy, Pd, Pt and Ti onto the major surfaces and through-holes; (c) depositing a thicker primary metal over the thin base metal film; (d) defining a circuit pattern by applying, imaging and developing a photoresist in the form of said pattern over the substrate surface; (e) electrolessly plating a thick copper layer over the exposed metal; (f) stripping the photoresist; and (g) etching away the metal underlying the photoresist.
Claim 18
Dependent Claim
36 words
The method recited in claim 11 wherein the adherent thin metal film is in the order of about 1 microinch thick and the thicker primary metal layer is in the order of about 40 microinches thick.
References Cited (Backward Citations)
US29820A
Cited
US3296099A
Cited
US3770571A
Cited
US3679472A
Cited
USRE29820E
Cited
US4113578A
Cited
US3925138A
Cited
US4166018A
Cited
US4031313A
Cited
US4148945A
Cited
DE2536152A1
Cited
US4153529A
Cited
US4121007A
Cited
US4129848A
Cited
US4100312A
Cited
US4085022A
Cited
US4110147A
Cited
US4056642A
Cited
US4105118A
Cited
US4193849A
Cited
JPS53140577A
Cited
US4115185A
Cited
JPS5441990A
Cited
US4135988A
Cited
US4353954A
Cited
US4160045A
Cited
JPS56153796A
Cited
US4389268A
Cited
US4354911A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-14 | 1989-10-14 | 1990-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-14 | 1993-10-14 | 1994-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-14 | 1997-10-14 | 1998-04-15 | $7700.00 | Window Closed / Lapsed |