Process of preparing thermoset resin substrates to improve adherence of electrolessly plated metal deposits
Assignee: MacDermid Inc
•
Filing: 1977-01-03
•
Granted: 1978-08-29
•
Expires: 1997-01-03
Abstract
Abstract A process is disclosed comprising laminating an anodically treated aluminum surface against a thermoset plastic substrate, whereby the surface of the substrate after chemically removing the aluminum has an improved affinity for the adherence thereon of electrolessly deposited metal films.
Inventors
- 👤 John J. Grunwald
- 👤 Eugene D. D'Ottavio
- 👤 Harold L. Rhodenizer
- 👤 Michael S. Lombardo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:26
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B15/20; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381; B32B2262/00; B32B2262/10; B32B2262/101; B32B2305/00; B32B2305/07; B32B2305/076; B32B2363/00; B32B2457/00; B32B2457/08; H05K2203/00; H05K2203/11; H05K2203/1152; H05K3/10; H05K3/18; H05K3/181; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31529
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
133 words
In a process of preparing an intermediate article of commerce comprising a laminate of aluminum foil and a thermoset resin substrate, which article is particularly adapted for use in producing printed circuit boards by additive electroless plating techniques after the aluminum foil has been chemically stripped from said resin substrate, the steps which comprise anodizing said aluminum foil in a phosphoric electrolyte to develop an aluminum oxide film on the surface of the foil which is to confront the surface of the substrate in said article; placing said aluminum foil with its anodized surface confronting the surface of a substrate comprising a plurality of glass fiber reinforced, B-stage epoxy resin prepregs; and applying sufficient heat and pressure to complete the cure of said substrate and bond said foil thereto to produce said laminate.
Claim 2
Dependent Claim
133 words
In a process of preparing an intermediate article of commerce comprising a laminate of aluminum foil and a thermoset resin substrate, which article is particularly adapted for use in producing printed circuit boards by additive electroless plating techniques after the aluminum foil has been chemically stripped from said resin substrate, the steps which comprise anodizing said aluminum foil in a phosphoric electrolyte to develop an aluminum oxide film on the surface of the foil which is to confront the surface of the substrate in said article; placing said aluminum foil with its anodized surface confronting the surface of a substrate comprising a plurality of glass fiber reinforced, B-stage epoxy resin prepregs; and applying sufficient heat and pressure to complete the cure of said substrate and bond said foil thereto to produce said laminate.
Claim 3
Dependent Claim
43 words
The process as defined in claim 1, wherein said thermoset resin substrate is cured and bonded to said anodized foil under pressure of from 5 p.s.i.g. to 1000 p.s.i.g. for 5 minutes to 3 hours at a temperature of 250° to 450° F.
Claim 4
Dependent Claim
52 words
The process as defined in claim 1, wherein said aluminum foil is anodized in a phosphoric electrolyte containing the equivalent of from 10% to 60% by weight phosphoric acid at temperatures from 70° to 130° F. for from 1 to 30 minutes at current densities of from 10 a.s.f. to 75 a.s.f.
Claim 5
Dependent Claim
46 words
The process as defined in claim 3, wherein the anodizing conditions comprise phosphoric electrolyte concentration equivalent to 20% to 40% by weight phosphoric acid, anodizing temperature of from 90° to 110° F, and an anodizing time of 1 to 7 minutes at 25 to 55 a.s.f.
Claim 6
Dependent Claim
37 words
The process as defined in claim 3, wherein the anodizing conditions comprise phosphoric electrolyte concentration equivalent to 30% by weight phosphoric acid, anodizing temperature of 90° F., and an anodizing time of 1 minute at 40 a.s.f.
References Cited (Backward Citations)
US2552285A
Cited
US2798037A
Cited
US2768923A
Cited
US2932599A
Cited
US3305416A
Cited
US3617613A
Cited
US3697319A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |