Combinations of sparingly soluble calcium phosphates in slurries and pastes as mineralizers and cements

Claim 2

A .[.dental restorative.]. slurry .[.comprising.]. .Iadd.consisting essentially of .Iaddend.an aqueous mixture of Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 , and modified Ca 3 (PO 4 ) 2 ,.]. both calcium phosphates being present in the slurry in excess such that hydroxyapatite is substantially continuously precipitated from the slurry .Iadd.at an ambient temperature.Iaddend..

Claim 3

The slurry of claim 1 wherein the other calcium phosphate is CaHPO 4 .2H 2 O.

Claim 4

The slurry of claim 1 wherein the other calcium phosphate is CaHPO 4 . .[.4. The slurry of claim 1 wherein the other calcium phosphate is Ca 8 H 2 (PO 4 ) 6 .5H 2 O..]. .[.5. The slurry of claim 1 wherein the other calcium phosphate is β--Ca 3

Claim 5

(PO 4 ) 2 ..]. 6. The slurry of claim 1 wherein at least one of the calcium phosphates is in crystalline, cryptocrystalline or amorphous form.

Claim 6

. The slurry of claim 1 further .[.comprising.]. .Iadd.including .Iaddend.up to approximately 10% by weight of additional calcium or phosphate containing compounds .Iadd.in an amount sufficient to alter the

Claim 7

pH of the slurry.Iaddend.. 8. The slurry of claim 7 wherein the additional calcium containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.CaCl 2 .[.or.]. .Iadd.and

Claim 8

.Iaddend.Ca(C 2 H 3 O 2 ) 2 . 9. The slurry of claim 7 wherein the additional phosphate containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.NaH 2

Claim 9

PO 4 .[.or.]. .Iadd.and .Iaddend.(NH 4 )H 2 PO 4 . 10. The slurry of claim 1 further .[.comprising.]. .Iadd.including .Iaddend.fluoride containing compounds such that the fluoride content of the slurry is up to approximately 3.8% by weight .Iadd.in an amount sufficient to increase the rate of precipitation of hydroxyapatite from

Claim 10

the slurry.Iaddend.. 11. The slurry of claim 10 wherein the fluoride containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.CaF 2 , SnF 2 , NaF, Na 2 SiF 6

Claim 11

.[.or.]. .Iadd.and .Iaddend.NaPO 3 F. 12. The slurry of claim 1 further .[.comprising.]. .Iadd.including .Iaddend.a gelling agent .Iadd.in

Claim 12

an amount sufficient to form an aqueous gel.Iaddend.. 13. A .[.dental restorative.]. paste .[.comprising.]. .Iadd.consisting essentially of .Iaddend.a nonaqueous mixture of a nontoxic organic solvent, Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 and modified Ca 3 (PO 4 ) 2 , the paste being capable of hardening.]. .Iadd.which nonaqueous mixture hardens .Iaddend.into a cement upon contact with an aqueous medium .Iadd.at an ambient

Claim 13

an amount sufficient to form an aqueous gel.Iaddend.. 13. A .[.dental restorative.]. paste .[.comprising.]. .Iadd.consisting essentially of .Iaddend.a nonaqueous mixture of a nontoxic organic solvent, Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 and modified Ca 3 (PO 4 ) 2 , the paste being capable of hardening.]. .Iadd.which nonaqueous mixture hardens .Iaddend.into a cement upon contact with an aqueous medium .Iadd.at an ambient

Claim 14

temperature.Iaddend.. 14. The paste of claim 13 wherein the other calcium

Claim 15

phosphate is CaHPO 4 .2H 2 O. 15. The paste of claim 13 wherein the other calcium phosphate is CaHPO 4 . .[.16. The paste of claim 13 wherein the other calcium phosphate is Ca 8 H 2 (PO 4 ) 6 .5H 2 O..]. .[.17. The paste of claim 13 wherein the

Claim 16

other calcium phosphate is β--Ca 3 (PO 4 ) 2 ..]. 18. The paste of claim 13 wherein at least one of the calcium phosphates is in

Claim 17

crystalline, cryptocrystalline or amorphous form. 19. The paste of claim 13 further .[.comprising.]. .Iadd.including .Iaddend.up to approximately 10% by weight of additional calcium or phosphate containing compounds

Claim 18

.Iadd.in an amount sufficient to alter the pH of the paste.Iaddend.. 20. The paste of claim 19 wherein the additional calcium containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.CaCl 2 .[.or.]. .Iadd.and .Iaddend.Ca(C 2 H 3

Claim 19

O 2 ) 2 . 21. The paste of claim 19 wherein the additional phosphate containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.NaH 2 PO 4 .[.or.]. .Iadd.and

Claim 20

.Iaddend.(NH 4 )H 2 PO 4 . 22. The paste of claim 13 further .[.comprising.]. .Iadd.including .Iaddend.fluoride containing compounds such that the fluoride content of the .[.slurry.]. .Iadd.paste .Iaddend.is up to approximately 3.8% by weight .Iadd.in an amount sufficient to increase the rate of precipitation of hydroxyapatite from the

Claim 21

paste.Iaddend.. 23. The paste of claim 22 wherein the fluoride containing compounds .[.comprise.]. .Iadd.are selected from the group consisting of .Iaddend.CaF 2 , SnF 2 , NaF, Na 2 SiF 6 .[.or.]. .Iadd.and

Claim 22

.Iaddend.NaPO 3 F. 24. The paste of claim 13 further .[.comprising.]. .Iadd.including .Iaddend.a seed crystal compound selected from the group consisting of hydroxyapatite and fluorapatite .Iadd.in an amount

Claim 23

sufficient to reduce the setting time of the cement.Iaddend.. 25. The paste of claim 13 wherein the aqueous medium is humid air or a dilute

Claim 24

aqueous solvent. 26. A .[.dental restorative.]. powder .[.comprising.]. .Iadd.consisting essentially of .Iaddend.a mixture of Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 , and modified Ca 3 (PO 4 ) 2 ,.]. the powder .[.being capable of.]. forming .[.a.]. slurry .Iadd.of claim 1 .Iaddend.upon contact with an appropriate aqueous solvent.[., the slurry being capable of substantially continuously precipitating hydroxyapatite.]. .Iadd.at an ambient

Claim 25

temperature.Iaddend.. 27. The powder of claim 26 wherein the solvent is

Claim 26

water or saliva. 28. A .[.dental restorative.]. powder .[.comprising.]. .Iadd.consisting essentially of .Iaddend.a mixture of Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 , and modified Ca 3 (PO 4 ) 2 ,.]. the powder .[.being capable of forming a hardenable.]. .Iadd.hardening into a .Iaddend.cement upon contact with an appropriate aqueous solvent .Iadd.at an ambient

Claim 27

water or saliva. 28. A .[.dental restorative.]. powder .[.comprising.]. .Iadd.consisting essentially of .Iaddend.a mixture of Ca 4 (PO 4 ) 2 O and at least one other calcium phosphate selected from the group consisting of CaHPO 4 .2H 2 O.[.,.]. .Iadd.and .Iaddend.CaHPO 4 , .[.Ca 8 H 2 (PO 4 ) 6 .5H 2 O, α--Ca 3 (PO 4 ) 2 , β--Ca 3 (PO 4 ) 2 , and modified Ca 3 (PO 4 ) 2 ,.]. the powder .[.being capable of forming a hardenable.]. .Iadd.hardening into a .Iaddend.cement upon contact with an appropriate aqueous solvent .Iadd.at an ambient

Claim 28

temperature.Iaddend.. 29. The powder of claim 28 wherein the solvent is

Claim 29

water or saliva. .Iadd.30. The slurry of claim 1 additionally including up to approximately 5% by weight of a high molecular weight crystal growth inhibitor selected from the group consisting of proteoglycans, glycoproteins, polylysine and protamine in an amount sufficient to inhibit

Claim 30

the growth of hydroxyapatite crystals. .Iaddend. .Iadd.31. The slurry of claim 1 wherein the slurry is slightly basic. .Iaddend. .Iadd.32. The slurry of claim 1 wherein the slurry is slightly acidic. .Iaddend. .Iadd.33. The slurry of claim 1 wherein the slurry is incorporated into a chewing gum. .Iaddend. .Iadd.34. The slurry of claim 1 where in the slurry

Claim 31

is incorporated into a toothpaste. .Iaddend. .Iadd.35. The paste of claim 24 wherein the seed crystal compound is hydroxyapatite, the hydroxyapatite being present in an amount up to 43% by weight and in an amount sufficient to reduce the setting time of the cement. .Iaddend. .Iadd.36. The paste of claim 13 additionally including up to approximately 5% by weight of a high molecular weight crystal growth inhibitor selected from the group consisting of proteoglycans, glycoproteins, polylysine and protamine in an amount sufficient to inhibit the growth of hydroxyapatite crystals. .Iaddend. .Iadd.37. The paste of claim 13 additionally including β--Ca 3 (PO 4 ) 2 in an amount sufficient to achieve setting expansion of the cement. .Iaddend. .Iadd.38. The paste of claim 13 additionally including up to 1% by weight of a crystal habit modifier selected from the group consisting of Mg 2+ , Sr 2+ , citrate, phosphonates, carbonate, polyphosphates, sucrose phosphate, and phosphocitrate in an amount sufficient to achieve setting expansion of the

Claim 32

cement. .Iaddend. .Iadd.39. The paste of claim 13 additionally including Ca 5 (PO 4 ) 2 SiO 4 or silicocarnotite in an amount sufficient to improve the setting properties of the cement. .Iaddend. .Iadd.40. The paste of claim 13 wherein the nontoxic organic solvent is selected from the group consisting of glycerin, ethanol and glycol. .Iaddend. .Iadd.41. The paste of claim 13 additionally including granular sugar, the sugar being present in an amount up to 20% by weight and in an amount sufficient to form a porous cement upon removal of the sugar by application of hot water to the cement. .Iaddend. .Iadd.42. The powder of claim 28 wherein the other calcium phosphate is CaHPO 4 .2H 2 O. .Iaddend. .Iadd.43. The powder of claim 28 wherein the other calcium phosphate is CaHPO 4 . .Iaddend. .Iadd.44. The powder of claim 28 wherein at least one of the calcium phosphates is in crystalline, cryptocrystalline or amorphous form. .Iaddend. .Iadd.45. The powder of claim 28 further including up to approximately 10% by weight of additional calcium or phosphate containing compounds in an amount sufficient to alter the pH of the accent. .Iaddend. .Iadd.46. The powder of claim 45 wherein the additional calcium containing compounds are selected from the group consisting of CaCl 2 and Ca(C 2 H 3 O 2 ) 2 . .Iaddend. .Iadd.47. The powder of claim 45 wherein the additional phosphate containing compounds are selected from the group consisting of NaH 2 PO 4 and (NH 4 )H 2 PO 4 . .Iaddend. .Iadd.48. The powder of claim 28 further including fluoride containing compounds such that the fluoride content is up to approximately 3.8% by weight in an amount sufficient to increase the rate of precipitation of hydroxyapatite from the cement. .Iaddend. .Iadd.49. The powder of claim 48 wherein the fluoride containing compounds are selected from the group consisting of CaF 2 , SnF 2 , NaF, Na 2 SiF 6 and NaPO 3 F. .Iaddend. .Iadd.50. The powder of claim 28 further including a seed crystal compound selected from the group consisting of hydroxyapatite and fluorapatite in an amount sufficient to reduce the setting time of the cement. .Iaddend. .Iadd.51. The powder of claim 50 wherein the seed crystal compound is hydroxyapatite, the hydroxyapatite being present in an amount up to 43% by weight and in an amount sufficient to reduce the setting time of the

Claim 33

cement. .Iaddend. .Iadd.52. The powder of claim 28 additionally including up to approximately 5% by weight of a high molecular weight crystal growth inhibitor selected from the group consisting of proteoglycans, glycoproteins, polylysine and protamine in an amount sufficient to inhibit the growth of hydroxyapatite crystals. .Iaddend. .Iadd.53. The powder of claim 28 additionally including β-Ca 3 (PO 4 ) 2 in an amount sufficient to achieve setting expansion of the cement. .Iaddend. .Iadd.54. The powder of claim 13 additionally including up to 1% by weight of a crystal habit modifier selected from the group consisting of Mg 2+ , Sr 2+ , citrate, phosphonates, carbonate, polyphosphates, sucrose phosphate, and phosphocitrate in an amount sufficient to achieve setting expansion of the cement. .Iaddend. .Iadd.55. The powder of claim 28 additionally including Ca 5 (PO 4 ) 2 SiO 4 or silicocarnotite in an amount sufficient to improve the setting properties of the cement. .Iaddend. .Iadd.56. The powder of claim 28 additionally including granular sugar, the sugar being present in an amount up to 20% by weight and in an amount sufficient to form a porous cement upon removal of the sugar by application of hot water to the cement. .Iaddend.