Process for preparing hydrophilic polymer films and apparatus thereof

Claim 2

A process for preparing a hydrophilic polymer film which comprises the steps of: coating the surface of a polymer film pre-treated with 60-110 KHz high frequency radiation with a photopolymerization solution containing 1 to 40% by weight of a hydrophilic monomer, a photo-initiating agent, a photo-enhancing agent, a cross-linking agent and 0.01 to 10% by weight of a UV stabilizer, wherein said hydrophilic monomer is selected from the group consisting of acrolein, acrylonitrile, acryloylchloride and a mixture thereof, said photo-enhancing agent is selected from the group consisting of n-butyl amine, diethyl amine, ethylmethacrylate, triethylene, tetramine, ethanol amine, ethyl amine, trimethyl amine and mixture thereof, and said UV stabilizer is selected from the group consisting of formula (I), (II) and a mixture thereof, ##STR2## wherein R 1 is a hydrogen or t-butyl group, and R 2 is methyl or t-butyl group, and photopolymerizing said photopolymerization solution and forming a hydrophilic polymer layer on the surface of said polymer film by a photo-reaction.

Claim 3

A process for preparing a hydrophilic polymer film by coating the surface of a polymer film with a photopolymerization solution consisting essentially of a hydrophilic monomer, a photo-initiating agent, a photo-enhancing agent selected from the group consisting of n-butyl amine, diethyl amine, ethylmethacrylate, triethylene, tetramine, ethanol amine, ethyl amine, trimethyl amine and a mixture thereof, a crosslinking agent and a UV stabilizer, drying said photopolymerization solution coated on the film, and photopolymerizing said photopolymerization solution to form a hydrophilic polymer layer on the surface of said polymer film by a photo-reaction carried out by irradiation to a UV light, the improvement which comprises the successive steps of: pre-treating the surface of the polymer film with 60-110 KHz of high frequency radiation before coating the photopolymerization solution; coating the pre-treated surface of the polymer film with the photopolymerization solution which contains 1 to 40% by weight of the hydrophilic monomer selected from the group consisting of acrolein, acrylonitrile, acryloylchloride and a mixture thereof and 0.01 to 10% by weight of the UV stabilizer selected from the group consisting of formula (II) and a mixture thereof ##STR3## wherein R 1 is a hydrogen or t-butyl group, and R 2 is methyl or t-butyl group; drying the coated photopolymerization solution by uniformly supplied air at a rate of 0.01 to 3 m/sec at a distance of 5 to 20 cm from a pair of air supply hoppers having a number of apertures with a diameter of 1 to 3 mm in a ratio of 1 aperture/cm 2 ; and photopolymerizing by irradiating 30 to 160 W/cm of the UV light at a distance of 5 to 50 cm from the film surface.

Claim 4

A process for preparing a hydrophilic polymer film by coating the surface of a polymer film with a photopolymerization solution consisting essentially of a hydrophilic monomer, a photo-initiating agent, a photo-enhancing agent selected from the group consisting of n-butyl amine, diethyl amine, ethylmethacrylate, triethylene, tetramine, ethanol amine, ethyl amine, trimethyl amine and a mixture thereof, a crosslinking agent and a UV stabilizer, drying said photopolymerization solution coated on the film, and photopolymerizing said photopolymerization solution to form a hydrophilic polymer layer on the surface of said polymer film by a photo-reaction carried out by irradiation to a UV light, the improvement which comprises the successive steps of: pre-treating the surface of the polymer film with 60-110 KHz of high frequency radiation before coating the photopolymerization solution; coating the pre-treated surface of the polymer film with the photopolymerization solution which contains 1 to 40% by weight of the hydrophilic monomer selected from the group consisting of acrolein, acrylonitrile, acryloylchloride and a mixture thereof and 0.01 to 10% by weight of the UV stabilizer selected from the group consisting of formula (II) and a mixture thereof ##STR3## wherein R 1 is a hydrogen or t-butyl group, and R 2 is methyl or t-butyl group; drying the coated photopolymerization solution by uniformly supplied air at a rate of 0.01 to 3 m/sec at a distance of 5 to 20 cm from a pair of air supply hoppers having a number of apertures with a diameter of 1 to 3 mm in a ratio of 1 aperture/cm 2 ; and photopolymerizing by irradiating 30 to 160 W/cm of the UV light at a distance of 5 to 50 cm from the film surface.