Soluble covering for cardiac pacing electrode
Assignee: Cardiac Pacemakers Inc
•
Filing: 1988-11-18
•
Granted: 1989-10-24
•
Expires: 2008-11-18
Abstract
Abstract A biocompatible covering, soluble in body fluids, surrounds the fixation helix of an implantable cardiac electrode as the electrode, and its adjoining lead, are inserted intravenously to a selected cardiac chamber. The covering size and shape are selected for protection of blood vessels and other body tissues during insertion, and for exposure of the fixation element shortly after its proper positioning. The covering may be applied to the fixation element by a dip coating process, or formed separately by casting or injection molding, for later attachment to the lead distal end using an adhesive.
Inventors
- 👤 David W. Mayer
- 👤 Byron L. Gilman
- 👤 Susan M. Walgren
- 👤 June M. Berglund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 03:35
CPC Classifications
A; A61; A61B; A61B5/00; A61B5/68; A61B5/6846; A61B5/6847; A61B5/6852; A61B5/24; A61B5/25; A61B5/279; A61B5/28; A61B5/283; A61B5/288; A61B5/29; A61B5/43; A61B5/4306; A61B5/4343; A61B5/4362; A61N; A61N1/00; A61N1/02; A61N1/04; A61N1/05; A61N1/056; A61N1/0565; A61N1/057; A61N1/0573
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
162 words
A process for coating a fixation element of a body implantable electrode, including the steps of: (a) selecting a biocompatible, non-pyrogenic material soluble in bodily fluids and having a melting point substantially above normal body temperature, and heating said material to a temperature slightly above its melting point; (b) dipping a fixation element of a body implantable electrode into a solution of said material maintained at said temperature; (c) removing said fixation member, along with an initial portion of said material adhering to said fixation member, from said solution and permitting them to cool a sufficient time to allow said first portion to at least partially solidify; (d) dipping said fixation member and material portion, after said cooling, into said solution for a time sufficient to permit a subsequent portion of said material to adhere to said initial portion; and (e) removing said fixation member, initial portion and subsequent portion from said solution, and permitting them to cool to an ambient temperature.
Claim 2
Dependent Claim
162 words
A process for coating a fixation element of a body implantable electrode, including the steps of: (a) selecting a biocompatible, non-pyrogenic material soluble in bodily fluids and having a melting point substantially above normal body temperature, and heating said material to a temperature slightly above its melting point; (b) dipping a fixation element of a body implantable electrode into a solution of said material maintained at said temperature; (c) removing said fixation member, along with an initial portion of said material adhering to said fixation member, from said solution and permitting them to cool a sufficient time to allow said first portion to at least partially solidify; (d) dipping said fixation member and material portion, after said cooling, into said solution for a time sufficient to permit a subsequent portion of said material to adhere to said initial portion; and (e) removing said fixation member, initial portion and subsequent portion from said solution, and permitting them to cool to an ambient temperature.
Claim 3
Dependent Claim
33 words
The process of claim 1 including the further steps of: repeating steps (d) and (e) until the combined thickness of said initial portion and all subsequent portions is at least a predetermined value.
Claim 4
Dependent Claim
85 words
The process of claim 1 including the further steps of: providing means defining a cavity having a selected size and shape, and heating a wall forming said cavity to a preselected temperature at least as high as the melting point of said material; and with the combined thickness of said material portions being at least said predetermined value to form a tip larger than said cavity, momentarily inserting said tip into said cavity to melt excess material; and draining said excess material from said cavity.
References Cited (Backward Citations)
US3591482A
Cited
US4524087A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-23 | 1993-04-24 | 1993-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-23 | 1997-04-24 | 1997-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-23 | 2001-04-24 | 2001-10-24 | $7700.00 | Window Closed / Lapsed |