US4749397A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of coating glass
Assignee: Pilkington Group Ltd
•
Filing: 1987-01-29
•
Granted: 1988-06-07
•
Expires: 2007-01-29
Abstract
Abstract Bent and/or toughened silver coated glass having high light transmission is produced by depositing layers of additional metal over, or both under and over, the silver layer. When the additional metal is used over the silver layer, it it selected from aluminium, titanium, zinc and tantalum. When the additional metal is used both under and over the silver, it is selected from aluminium, titanium, zinc, tantalum and zirconium. The additional metal is used in an amount such that the light transmission of the coated glass increases on bending and/or toughening. The bent and/or toughened coated glass is useful for architectural glazing and as vehicle windows.
Inventors
- 👤 Peter Chesworth
- 👤 Martin Lowe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:35
CPC Classifications
C; C03; C03C; C03C21/00; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3615; B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10165; B32B17/10174; C03C17/3618; C03C17/3644; C03C17/3647; C03C17/3652; C03C17/3681; C03C17/3689
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
108 words
A process for the production of a bent and/or toughened silver coated glass substrate which comprises depositing a coating comprising a silver layer 5 nm to 30 nm thick, a layer of a predetermined amount of an additional metal selected from aluminium, titanium, zinc and tantalum over the silver layer, and an anti-reflection metal oxide layer over said layer of additional metal on a glass substrate and subjecting the coated glass substrate to a bending and/or toughening cycle in which it is heated to a temperature above the softening point of the glass, wherein the coated glass develops an increased light transmission during the bending and/or toughening cycle.
Claim 2
Dependent Claim
108 words
A process for the production of a bent and/or toughened silver coated glass substrate which comprises depositing a coating comprising a silver layer 5 nm to 30 nm thick, a layer of a predetermined amount of an additional metal selected from aluminium, titanium, zinc and tantalum over the silver layer, and an anti-reflection metal oxide layer over said layer of additional metal on a glass substrate and subjecting the coated glass substrate to a bending and/or toughening cycle in which it is heated to a temperature above the softening point of the glass, wherein the coated glass develops an increased light transmission during the bending and/or toughening cycle.
Claim 3
Dependent Claim
35 words
A process according to claim 1 which comprises depositing the additional metal in an amount such that the coated glass develops an increased light transmission of at least 70% during the bending and/or toughening cycle.
Claim 4
Dependent Claim
43 words
A process according to claim 1 which comprises depositing the additional metal in an amount such that the coated glass develops an increased light transmission of at least 80% of the light transmission of the uncoated glass during the bending and/or toughening cycle.
Claim 5
Dependent Claim
52 words
A process according to claim 1 which comprises depositing the coating on a soda lime silica glass substrate and heating the coated glass substrate in air at a temperature in the range 570° C. to 620° C., allowing it to sag in a mold of desired curvature, and annealing the bent glass.
Claim 6
Dependent Claim
49 words
A process according to claim 1 which comprises depositing the coating on a soda lime silica glass substrate and heating the coated glass substrate in air at a temperature in the range 600° C. to 670° C., optionally bending the glass, and rapidly cooling the glass to toughen it.
Claim 7
Dependent Claim
18 words
A process according to claim 5 which comprises cooling the glass by blowing air onto the glass surface.
Claim 8
Dependent Claim
51 words
A process according to claim 1 which comprises regulating the amount of additional metal deposited in accordance with the temperature to which the glass is heated and the duration of the heating cycle employed in the bending and/or toughening cycle, to maximise the light transmission of the toughened and/or bent product.
Claim 9
Dependent Claim
37 words
A process according to claim 1 which comprises depositing said additional metal in an amount such that the light transmission of the coated glass increases by at least 10% of its original value on bending and/or toughening.
Claim 10
Dependent Claim
33 words
A process according to claim 1 which comprises depositing said additional metal in an amount sufficient to provide a single metal layer having a thickness in the range 4 nm to 15 nm.
Claim 11
Dependent Claim
16 words
A process according to claim 1 which comprises depositing aluminium or zinc as the additional metal.
Claim 12
Dependent Claim
27 words
A process according to claim 10 which comprises depositing aluminium in an amount equivalent to a layer 5 nm to 10 nm thick as the additional metal.
Claim 13
Dependent Claim
134 words
A process for the production of a bent and/or toughened silver coated glass substrate which comprises depositing a coating comprising a layer of a first predetermined amount of additional metal selected from aluminium, titanium, zinc, tantalum and zirconium over the substrate, a silver layer 5 nm to 30 nm thick over said layer of additional metal, a further layer of a further predetermined amount of additional metal selected from aluminium, titanium, zinc, tantalum and zirconium over the silver layer, and an anti-reflection metal oxide layer over said further layer of additional metal, and subjecting the coated glass substrate to a bending and/or toughening cycle in which it is heated to a temperature above the softening point of the glass, wherein the coated glass develops an increased light transmission during the bending and/or toughening cycle.
Claim 14
Dependent Claim
134 words
A process for the production of a bent and/or toughened silver coated glass substrate which comprises depositing a coating comprising a layer of a first predetermined amount of additional metal selected from aluminium, titanium, zinc, tantalum and zirconium over the substrate, a silver layer 5 nm to 30 nm thick over said layer of additional metal, a further layer of a further predetermined amount of additional metal selected from aluminium, titanium, zinc, tantalum and zirconium over the silver layer, and an anti-reflection metal oxide layer over said further layer of additional metal, and subjecting the coated glass substrate to a bending and/or toughening cycle in which it is heated to a temperature above the softening point of the glass, wherein the coated glass develops an increased light transmission during the bending and/or toughening cycle.
Claim 15
Dependent Claim
34 words
A process according to claim 12 which comprises depositing the additional metal in amounts such that the coated glass develops an increased light transmission of at least 70% during the bending and/or toughening cycle.
Claim 16
Dependent Claim
42 words
A process according to claim 12 which comprises depositing the additional metal in amounts such that the coated glass develops an increased light transmission of at least 80% of the light transmission of the uncoated glass during the bending and/or toughening cycle.
Claim 17
Dependent Claim
52 words
A process according to claim 12 which comprises depositing the coating on a soda lime silica glass substrate and heating the coated glass substrate in air at a temperature in the range 570° C. to 620° C., allowing it to sag in a mold of desired curvature, and annealing the bent glass.
Claim 18
Dependent Claim
49 words
A process according to claim 12 which comprises depositing the coating on a soda lime silica glass substrate and heating the coated glass substrate in air at a temperature in the range 600° C. to 670° C., optionally bending the glass, and rapidly cooling the glass to toughen it.
Claim 19
Dependent Claim
18 words
A process according to claim 16 which comprises cooling the glass by blowing air onto the glass surface.
Claim 20
Dependent Claim
51 words
A process according to claim 12 which comprises regulating the amounts of additional metal deposited in accordance with the temperature to which the glass is heated and the duration of the heating cycle employed in the bending and/or toughening cycle, to maximise the light transmission of the toughened and/or bent product.
Claim 21
Dependent Claim
37 words
A process according to claim 12 which comprises depositing said additional metal in an amount such that the light transmission of the coated glass increases by at least 10% of its original value on bending and/or toughening.
Claim 22
Dependent Claim
33 words
A process according to claim 12 which comprises depositing additional metal in a total amount sufficient to provide a single metal layer having a thickness in the range 4 nm to 15 nm.
Claim 23
Dependent Claim
22 words
A process according to claim 12 wherein the additional metal deposited in each layer of additional metal is aluminium, zinc or titanium.
References Cited (Backward Citations)
US25711A
Cited
USRE25711E
Cited
CH400714A
Cited
GB1123574A
Cited
US3743491A
Cited
US3762902A
Cited
GB1336825A
Cited
US3793167A
Cited
US4329379A
Cited
EP0035906A2
Cited
GB2129831A
Cited
GB2135697A
Cited
US4497700A
Cited
US4547400A
Cited
EP0229921A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-07 | 1991-12-07 | 1992-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-07 | 1995-12-07 | 1996-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-07 | 1999-12-07 | 2000-06-07 | $7700.00 | Window Closed / Lapsed |