US4547400A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making infrared reflective glass sheet-I
Assignee: Ford Motor Co
•
Filing: 1985-02-25
•
Granted: 1985-10-15
•
Expires: 2005-02-25
Abstract
Abstract This disclosure is directed to a method of making an infrared reflective glass sheet. The method has the following steps. The glass sheet formed of soda/lime silica glass is selected. The glass sheet is heated to a temperature in a range from 900° to 1100° F. If desired, the sheet glass selected may be selected at the time it is being manufactured in a glass manufacturing operation and it would have upon leaving a process such as a float process a temperature in a range of 900° to 1100° F. An organic/metallic ion-containing, chlorine-free compound is applied to a surface of the glass sheet. Application of this compound forms a metallic oxide seal coating on the surface of the glass sheet. A coating of tin oxide is applied to the metal oxide seal coating. The coating of tin oxide is formed from the decomposition of butyltin trichloride. The glass sheet is cooled to room temperature after application of the metal oxide seal coating and the tin oxide coating thereon.
Inventors
- 👤 Daryl J. Middleton
- 👤 Jodyne I. Grenier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:59
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3417
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
112 words
A method of making an infrared reflective glass sheet which comprises the steps of: selecting a glass sheet formed of soda/lime silica glass; heating said glass sheet to a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet a metallic oxide seal coating which does not form sodium chloride crystals which cause the visual appearance of the film to be hazy; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 2
Independent Claim
112 words
A method of making an infrared reflective glass sheet which comprises the steps of: selecting a glass sheet formed of soda/lime silica glass; heating said glass sheet to a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet a metallic oxide seal coating which does not form sodium chloride crystals which cause the visual appearance of the film to be hazy; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 3
Independent Claim
73 words
A method of making an infrared reflective glass sheet which comprising the steps of: forming a glass sheet of soda/lime silica glass at a temperature in a range from 900° to 1100° F.; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 4
Independent Claim
73 words
A method of making an infrared reflective glass sheet which comprising the steps of: forming a glass sheet of soda/lime silica glass at a temperature in a range from 900° to 1100° F.; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 5
Independent Claim
108 words
A method of making an infrared reflective glass sheet which comprises the steps of: selecting a glass sheet formed of soda/lime silica glass; heating said glass sheet to a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet an organic/metallic ion-containing, chlorine-free compound to form a metallic oxide seal coating on said surface of said glass sheet; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 6
Independent Claim
108 words
A method of making an infrared reflective glass sheet which comprises the steps of: selecting a glass sheet formed of soda/lime silica glass; heating said glass sheet to a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet an organic/metallic ion-containing, chlorine-free compound to form a metallic oxide seal coating on said surface of said glass sheet; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 7
Independent Claim
103 words
A method of making an infrared reflective glass sheet which comprising the steps of: forming a glass sheet of soda/lime silica glass at a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet an organic/metallic ion-containing, chlorine-free compound to form a metallic oxide seal coating on said surface of said glass sheet; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 8
Independent Claim
103 words
A method of making an infrared reflective glass sheet which comprising the steps of: forming a glass sheet of soda/lime silica glass at a temperature in a range from 900° to 1100° F.; applying to a surface of said glass sheet an organic/metallic ion-containing, chlorine-free compound to form a metallic oxide seal coating on said surface of said glass sheet; applying to said metal oxide seal coating a coating of tin oxide formed from the decomposition of butyltin trichloride doped with fluoride; cooling said glass sheet to room temperature after application of said metal oxide seal coating and said tin oxide coating thereon.
Claim 9
Dependent Claim
20 words
The method of claim 3, wherein said metal oxide seal coating has a thickness in a range of 25-100 nanometers.
Claim 10
Dependent Claim
31 words
The method of claim 5, wherein the combined coating of said metal oxide seal coating and said tin oxide coating have a thickness in a range from 100 to 400 nanometers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |