Ion implanation of titanium workpieces without surface discoloration
Assignee: Spire Corp
•
Filing: 1986-05-12
•
Granted: 1987-09-15
•
Expires: 2006-05-12
Abstract
Abstract A process for preventing surface discoloration in orthopedic implants made of titanium and its alloys is disclosed. Such surface discoloration is apt to occur when the orthopedic implants are ion implanted to improve their wear characteristics. The process essentially includes exposing all fixtures and shields, made of pure titanium, located in an implant chamber, to an ion beam, creating a vacuum within the chamber not exceeding about 5×10 -5 torr, introducing an orthopedic implant within the chamber to be directly exposed to the beam, and reducing the ion beam current power density so as not to exceed about 1.0 watt/cm 2 . Exposing the fixtures and shields to the ion beam first serves to remove surface contamination therefrom, followed by forming a surface layer thereon. This surface layer effectively lowers the sputtering coefficient of the fixtures and shields, and thus reduces the amount of material sputtered from areas exposed to the ion beam to unexposed areas. Preferably, the vacuum is created by using an oil-free vacuum pump.
Inventors
- 👤 Piran Sioshansi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 21:00
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/48; A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L; A61L27/00; A61L27/02; A61L27/04; A61L27/06; A61F2/3094; A61F2/38; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00389; A61F2310/00592; A61F2310/00856; A61F2310/0088; Y; Y10; Y10S; Y10S148/00; Y10S148/90
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
197 words
A process for preventing surface discoloration of workpieces formed of titanium and its alloys during their ion implantation wherein a plurality of workpieces are exposed to an ion beam in series so as to improve their wear performance comprising: (a) exposing all titanium fixtures and shields mounted within an implant chamber prior to each ion implantation to an ion beam so as to cleanse them of surface contamination and to form a surface layer thereon having a sputtering coefficient lower than that of titanium; (b) creating a vacuum within said implant chamber not exceeding about 5×10 -5 torr; and (c) introducing a workpiece formed of titanium and its alloys into said implant chamber to be secured therein by said cleansed and surface layer coated titanium fixtures and exposing said workpiece to a direct line of said ion beam while shielding areas thereof not being treated; (d) said ion beam having an ion beam power density on the surface of said workpiece not exceeding about 1.0 watt/cm 2 ; (e) said ion beam incorporating one of a group of elemental species consisting of nitrogen, carbon, chromium, zirconium, oxygen, boron, tin, iron, tantalum, molbdenum, neon, argon, krypton and xenon.
Claim 2
Dependent Claim
197 words
A process for preventing surface discoloration of workpieces formed of titanium and its alloys during their ion implantation wherein a plurality of workpieces are exposed to an ion beam in series so as to improve their wear performance comprising: (a) exposing all titanium fixtures and shields mounted within an implant chamber prior to each ion implantation to an ion beam so as to cleanse them of surface contamination and to form a surface layer thereon having a sputtering coefficient lower than that of titanium; (b) creating a vacuum within said implant chamber not exceeding about 5×10 -5 torr; and (c) introducing a workpiece formed of titanium and its alloys into said implant chamber to be secured therein by said cleansed and surface layer coated titanium fixtures and exposing said workpiece to a direct line of said ion beam while shielding areas thereof not being treated; (d) said ion beam having an ion beam power density on the surface of said workpiece not exceeding about 1.0 watt/cm 2 ; (e) said ion beam incorporating one of a group of elemental species consisting of nitrogen, carbon, chromium, zirconium, oxygen, boron, tin, iron, tantalum, molbdenum, neon, argon, krypton and xenon.
Claim 3
Dependent Claim
73 words
The process of claim 1 wherein said exposing said titanium fixtures and shields to said ion beam is for a period of about three and a half hours, with an ion beam particle energy from about 10 keV to about 200 keV so as to implant a dose of about 3×10 17 ions/cm 2 , and wherein the peak current density of said ion beam does not exceed about ten microamperes/cm 2 .
Claim 4
Dependent Claim
33 words
The process of claim 1 wherein said ion beam power current density is achieved by expanding the spot size of said ion beam by a magnetic lens system surrounding said incoming ion beam.
Claim 5
Dependent Claim
34 words
The process of claim 1 wherein said ion beam power current density is achieved by expanding the spot size of said ion beam by an electrostatic lens system acting on said incoming ion beam.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein said workpiece includes orthopaedic surgical implants for use as artificial knee and hip joints.
Claim 7
Dependent Claim
218 words
A process for preventing surface discoloration of workpieces formed of titanium and its alloys during their ion implantation wherein a plurality of workpieces are exposed to an ion beam in series so as to improve their wear performance comprising: (a) exposing all fixtures and shields mounted within an implant chamber and formed of pure titanium to an ion beam prior to each implantation so as to cleanse them of surface contamination; (b) creating a vacuum within said chamber not exceeding about 5×10 -5 torr; (c) introducing a workpiece formed of titanium alloy into said chamber; (d) said ion beam having an ion beam power current density on the surface of said workpiece not exceeding about 1.0 watt/cm 2 ; and (e) exposing said workpiece to a direct line of said ion beam to ion implant the same; (f) said exposing said pure titanium fixtures and shields to said ion beam first sputter-cleans the surfaces thereof, followed by forming a surface layer thereon possessing a sputtering coefficient lower than that of pure titanium; (g) said titanium alloy being Ti-6Al-4V and said vacuum being created by using an oil-free vacuum pump; (h) said ion beam incorporating one of a group of elemental species consisting of nitrogen, carbon, chromium, zirconium, oxygen, boron, tin, iron, tantalum, molybdenum, neon, argon, krypton and xenon.
Claim 8
Dependent Claim
218 words
A process for preventing surface discoloration of workpieces formed of titanium and its alloys during their ion implantation wherein a plurality of workpieces are exposed to an ion beam in series so as to improve their wear performance comprising: (a) exposing all fixtures and shields mounted within an implant chamber and formed of pure titanium to an ion beam prior to each implantation so as to cleanse them of surface contamination; (b) creating a vacuum within said chamber not exceeding about 5×10 -5 torr; (c) introducing a workpiece formed of titanium alloy into said chamber; (d) said ion beam having an ion beam power current density on the surface of said workpiece not exceeding about 1.0 watt/cm 2 ; and (e) exposing said workpiece to a direct line of said ion beam to ion implant the same; (f) said exposing said pure titanium fixtures and shields to said ion beam first sputter-cleans the surfaces thereof, followed by forming a surface layer thereon possessing a sputtering coefficient lower than that of pure titanium; (g) said titanium alloy being Ti-6Al-4V and said vacuum being created by using an oil-free vacuum pump; (h) said ion beam incorporating one of a group of elemental species consisting of nitrogen, carbon, chromium, zirconium, oxygen, boron, tin, iron, tantalum, molybdenum, neon, argon, krypton and xenon.
Claim 9
Dependent Claim
55 words
The process of claim 6 wherein said exposing said titanium fixtures and shields to said ion beam is for a period of about three and a half hours, with an ion beam particle energy from about 10 keV to about 200 keV so as to implant a dose of about 3×10 17 ions/cm 2 .
Claim 10
Dependent Claim
54 words
The process of claim 6 wherein said exposing said workpiece to said ion beam extends for a period of about three and a half hours, with an ion beam particle energy from about 10 keV to about 200 keV so as to implant a dose of at least about 3×10 17 ions/cm 2 .
Claim 11
Dependent Claim
21 words
The process of claim 6 wherein said sputtering coefficient of said surface layer is about 0.06, and does not exceed 0.09.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-14 | 1991-03-16 | 1991-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-14 | 1995-03-16 | 1995-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-14 | 1999-03-16 | 1999-09-15 | $7700.00 | Window Closed / Lapsed |