Process for producing a piezo- and pyro-electric film
Assignee: Unitika Ltd
•
Filing: 1984-07-03
•
Granted: 1986-06-03
•
Expires: 2004-07-03
Abstract
Abstract A process for producing a piezo- and pyro-electric film, which comprises biaxially stretching a single- or multi-layered thermoplastic film containing from 3 to 80% by volume, as an average based on the entire film, of a ferroelectric substance, then subjecting the stretched film to polarization treatment by applying a high voltage at a temperature within a range of from 10° C. to a temperature lower than the melting point of said thermoplastic resin, and cooling the film while continuously applying the high voltage.
Inventors
- 👤 Kunio Murakami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:08
CPC Classifications
H; H10; H10N; H10N30/00; H10N30/01; H10N30/08; H10N30/084; H10N15/00; H10N15/10; H10N15/15; H10N30/04; H10N30/045; H10N30/80; H10N30/85; H10N30/852; Y; Y10; Y10T; Y10T29/00; Y10T29/42
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
144 words
A process for producing a piezo- and pyro-electric film having high strength and without great anisotrophy in the Piezo-electric characteristics, which comprises biaxially stretching a single- or multi-layered thermoplastic film containing from 3 to 80% by volume, as an average based on the entire film, of a ferroelectric substance such that during the biaxial stretching, particles of the ferroelectric substance are subjected to the shearing stress resulting from molecular chain orientation of the thermoplastic resin of the film and undergo a change in their state from a randomly dispersed state in the non-stretched film to an oriented state as stretched, then subjecting the stretched film to polarization by applying a high voltage at a temperature within a range of from 10° C. to a temperature lower than the melting point of said thermoplastic resin, and cooling the film while continuously applying the high voltage.
Claim 2
Dependent Claim
144 words
A process for producing a piezo- and pyro-electric film having high strength and without great anisotrophy in the Piezo-electric characteristics, which comprises biaxially stretching a single- or multi-layered thermoplastic film containing from 3 to 80% by volume, as an average based on the entire film, of a ferroelectric substance such that during the biaxial stretching, particles of the ferroelectric substance are subjected to the shearing stress resulting from molecular chain orientation of the thermoplastic resin of the film and undergo a change in their state from a randomly dispersed state in the non-stretched film to an oriented state as stretched, then subjecting the stretched film to polarization by applying a high voltage at a temperature within a range of from 10° C. to a temperature lower than the melting point of said thermoplastic resin, and cooling the film while continuously applying the high voltage.
Claim 3
Dependent Claim
30 words
The process according to claim 1, wherein the ferroelectric substance is at least one of a metal titanate, a metal stannate and a metal zirconate, or a solid solution thereof.
Claim 4
Dependent Claim
35 words
The process according to claim 1, wherein the ferroelectric substance is a solid solution comprising from 35 to 65 mol % of PbTiO 3 and from 65 to 35 mol % of PbZrO 3 .
Claim 5
Dependent Claim
38 words
The process according to claim 1, wherein the ferroelectric substance is a solid solution represented by the following formula: Pb.sub.1-x La.sub.x (Zr.sub.y Ti.sub.z).sub.1-x/4 O.sub.3 where x is from 1 to 0.05, and y/z is from 50/50 to 80/20.
Claim 6
Dependent Claim
25 words
The process according to claim 1, wherein the film contains from 0.01 to 10% by weight, relative to the ferroelectric substance, of a coupling agent.
Claim 7
Dependent Claim
27 words
The process according to claim 1, wherein the thermoplastic resin is a homopolymer of polyethylene terephthalate, poly-ε-capramide, polyvinylidene fluoride or polypropylene, or a copolymer composed mainly thereof.
Claim 8
Dependent Claim
18 words
The process according to claim 1, wherein the biaxial stretching is conducted by a simultaneous biaxial stretching method.
Claim 9
Dependent Claim
63 words
The process according to claim 1, wherein the thermoplastic film is simultaneously biaxially stretched at a temperature from (Tg-10)° to (Tm-20+V)° C., where Tg is the glass transition temperarure (°C.) of the thermoplastic resin, Tm is the melting point (°C.) of the thermoplastic resin, and V is the content (% by volume), as an average of the entire film, of the ferroelectric substance.
Claim 10
Dependent Claim
19 words
The process according to claim 1, wherein the biaxial stretching is conducted by a two-way successive biaxial stretching method.
Claim 11
Dependent Claim
76 words
The process according to claim 1, wherein the thermoplastic film is longitudinally stretched at a temperature of from (Tg-10)° to (Tm-30+V)° C., and then transversely stretched at a temperature of from Tg° to (Tm-20+V)° C., where Tg is the glass transition temperature (°C.) of the thermoplastic resin, Tm is the melting point (°C.) of the thermoplastic resin, and V is the content (% by volume), as an average of the entire film, of the ferroelectric substance.
Claim 12
Dependent Claim
56 words
The process according to claim 1, wherein a voltage of from 2 V/μ to 300 V/μ is applied over a period of from 10 minutes to 4 hours at a temperature within a range of from 20° C. to a temperature lower by 10° C. than the melting point or pour point of the thermoplastic resin.
References Cited (Backward Citations)
JPS5147298A
Cited
US4265841A
Cited
US4268653A
Cited
US4227111A
Cited
US4308370A
Cited
JPS5723286A
Cited
US4407054A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-02 | 1989-12-02 | 1990-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-02 | 1993-12-02 | 1994-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-02 | 1997-12-02 | 1998-06-03 | $7700.00 | Window Closed / Lapsed |