Deposited films with improved microstructures
Assignee: Battelle Memorial Institute Inc
•
Filing: 1982-02-22
•
Granted: 1984-08-28
•
Expires: 2002-02-22
Abstract
Abstract Methods for improving microstructures of line-of-sight deposited films are described. Columnar growth defects ordinarily produced by geometrical shadowing during deposition of such films are eliminated without resorting to post-deposition thermal or mechanical treatments. The native, as-deposited coating qualities, including homogeneity, fine grain size, and high coating-to-substrate adherence, can thus be retained. The preferred method includes the steps of emitting material from a source toward a substrate to deposit a coating non-uniformly on the substrate surface, removing a portion of the coating uniformly over the surface, again depositing material onto the surface, but from a different direction, and repeating the foregoing steps. The quality of line-of-sight deposited films such as those produced by sputtering, progressively deteriorates as the angle of incidence between the flux and the surface becomes increasingly acute. Depositing non-uniformly, so that the coating becomes progressively thinner as quality deteriorates, followed by uniformly removing some of the coating, such as by resputtering, eliminates the poor quality portions, leaving only high quality portions of the coating. Subsequently sputtering from a different direction applies a high quality coating to other regions of the surface. Such steps can be performed either simultaneously or sequentially to apply coatings of a uniformly high quality, closed microstructure to three-dimensional or large planar surfaces.
Inventors
- 👤 James W. Patten
- 👤 Ronald W. Moss
- 👤 Edwin D. McClanahan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:46
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/50; C23C14/505; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/938; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
105 words
A coated substrate comprising: a substrate having a three-dimensional surface and a physical vapor deposited solid coating covering said surface; said surface including at least first and second surface portions mutually oriented so that parallel lines of sight intersect the first portion at about a right angle and the second portion at an acute angle sufficient to produce geometric shadowing thereon; said coating having a substantially uniform microstructure over said surface with any columnar growth defects therein due to geometric shadowing being limited in length to less than the thickness of the coating; said coating being substantially free of microstructural modifications caused by heat treatment.
Claim 2
Dependent Claim
105 words
A coated substrate comprising: a substrate having a three-dimensional surface and a physical vapor deposited solid coating covering said surface; said surface including at least first and second surface portions mutually oriented so that parallel lines of sight intersect the first portion at about a right angle and the second portion at an acute angle sufficient to produce geometric shadowing thereon; said coating having a substantially uniform microstructure over said surface with any columnar growth defects therein due to geometric shadowing being limited in length to less than the thickness of the coating; said coating being substantially free of microstructural modifications caused by heat treatment.
Claim 3
Dependent Claim
17 words
A coated substrate according to claim 1 in which the coating is free of columnar growth defects.
Claim 4
Dependent Claim
31 words
A coated substrate according to claim 1 is a concavo-convex surface, the coating having a microstructural through-porosity of less than the thickness of the coating over the entirety of the surface.
Claim 5
Dependent Claim
15 words
A coated substrate according to claim 1 in which the coating is free of through-porosity.
Claim 6
Dependent Claim
22 words
A coated substrate according to claim 1 in which the coating is structurally homogeneous down to a diameter of approximately one micron.
Claim 7
Dependent Claim
17 words
A coated substrate according to claim 1 in which the coating is characterized by a non-equilibrium microstructure.
Claim 8
Dependent Claim
107 words
A coated substrate comprising: a substrate having a three-dimensional external surface including a first surface portion in a first plane and a second surface in a second plane oriented at an angle of at least about 60° from the first plane; and a physical vapor deposited solid coating covering said surface including said first and second portions; substantially the entire coating having a microstructure in which any voids therein due to geometric shadowing are limited in length to less than the thickness of the coating; said coating having a substantially uniform microstructure over said surface and being structurally homogeneous down to a dimension of approximately one micron.
Claim 9
Dependent Claim
107 words
A coated substrate comprising: a substrate having a three-dimensional external surface including a first surface portion in a first plane and a second surface in a second plane oriented at an angle of at least about 60° from the first plane; and a physical vapor deposited solid coating covering said surface including said first and second portions; substantially the entire coating having a microstructure in which any voids therein due to geometric shadowing are limited in length to less than the thickness of the coating; said coating having a substantially uniform microstructure over said surface and being structurally homogeneous down to a dimension of approximately one micron.
Claim 10
Dependent Claim
16 words
A coated substrate according to claim 7 in which the coating has a substantially uniform thickness.
Claim 11
Dependent Claim
21 words
A coated substrate according to claim 7 in which the coating has a grain size of less than one micron diameter.
Claim 12
Dependent Claim
36 words
A coated substrate according to claim 7 having a coating-to-substrate adherence such that any separation of the coating from the substrate will occur within one of the substrate and the coating, but not at their interface.
Claim 13
Dependent Claim
13 words
A coated substrate according to claim 7 in which the coating is sputter-deposited.
Claim 14
Dependent Claim
41 words
A coated substrate according to claim 7 in which: the coating has a microstructure of approximately uniform density over the entirety of the surface; and and voids in said microstructure are limited so that said coating is substantially impervious to liquids.
Claim 15
Dependent Claim
40 words
A coated substrate comprising: a substrate having a three-dimensional surface extending entirely around at least a portion of the substrate; and a sputter-deposited coating entirely covering said surface; said coating being free of columnar growth defects due to geometrical shadowing.
Claim 16
Dependent Claim
40 words
A coated substrate comprising: a substrate having a three-dimensional surface extending entirely around at least a portion of the substrate; and a sputter-deposited coating entirely covering said surface; said coating being free of columnar growth defects due to geometrical shadowing.
Claim 17
Dependent Claim
43 words
A coated substrate according to claim 13 in which a first portion of coating material has been deposited free of any of said defects on a region of said surface following the resputtering from said region of a second portion containing said defects.
Claim 18
Dependent Claim
21 words
A coated substrate according to claim 13 in which the coating is substantially free of microstructural modifications caused by heat treatment.
Claim 19
Dependent Claim
123 words
A coated substrate comprising a substrate having a coating which includes: a first physical vapor deposited coating initially deposited nonuniformly over first and second surface portions of a substrate, more thickly on the first portion than on the second portion, and then removed in part approximately uniformly from both portions so as to leave a residual coating substantially free of columnar growth defects covering only the first surface portion; and a second physical vapor deposited coating initially deposited on the substrate, in a nonuniform thickness offset from the first surface portion so as to overlap the residual coating and more thickly cover the second surface portion, and then removed in part approximately uniformly so as to expose a portion of the residual coating.
Claim 20
Dependent Claim
123 words
A coated substrate comprising a substrate having a coating which includes: a first physical vapor deposited coating initially deposited nonuniformly over first and second surface portions of a substrate, more thickly on the first portion than on the second portion, and then removed in part approximately uniformly from both portions so as to leave a residual coating substantially free of columnar growth defects covering only the first surface portion; and a second physical vapor deposited coating initially deposited on the substrate, in a nonuniform thickness offset from the first surface portion so as to overlap the residual coating and more thickly cover the second surface portion, and then removed in part approximately uniformly so as to expose a portion of the residual coating.
Claim 21
Dependent Claim
109 words
A coated substrate comprising a substrate having a coating which includes: a first physical vapor deposited coating initially deposited over first and second surface portions of a substrate, at a high angle of incidence on the first portion and a low angle of incidence on the second portion, and partially removed so as to leave a first residual coating covering only the first surface portion; and a second physical vapor deposited coating deposited and partially removed in essentially the same manner as the first coating but offset therefrom along the substrate surface to provide a second residual coating covering the second surface portion and overlapping the first residual coating.
Claim 22
Dependent Claim
109 words
A coated substrate comprising a substrate having a coating which includes: a first physical vapor deposited coating initially deposited over first and second surface portions of a substrate, at a high angle of incidence on the first portion and a low angle of incidence on the second portion, and partially removed so as to leave a first residual coating covering only the first surface portion; and a second physical vapor deposited coating deposited and partially removed in essentially the same manner as the first coating but offset therefrom along the substrate surface to provide a second residual coating covering the second surface portion and overlapping the first residual coating.
References Cited (Backward Citations)
US3021271A
Cited
US3736242A
Cited
US4006070A
Cited
US4036723A
Cited
US4038171A
Cited
US4150905A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-28 | 1988-02-27 | 1988-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-28 | 1992-02-27 | 1992-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-28 | 1996-02-27 | 1996-08-28 | $7700.00 | Window Closed / Lapsed |