Metal oxide films
Assignee: Pilkington Automotive Ltd
•
Filing: 1972-01-26
•
Granted: 1977-02-01
•
Expires: 1992-01-26
Abstract
Abstract A substantially uniform, transparent, electrically conducting, metal oxide film (e.g. of indium/tin oxide) can be deposited on to a substrate such as glass of large lateral dimensions, e.g. a windscreen for an aircraft or a land vehicle, by low-pressure reactive sputtering from a cathode of the metal, using an atmosphere of oxygen and another gas or gases (preferably an inert gas) at reduced pressure, by providing access for the sputtering atmosphere to penetrate into the whole of the working space between the cathode and the substrate so as to maintain a substantial degree of uniformity in the oxygen concentration in the working space. Access for the atmosphere may be provided by means of passages extending through the cathode assembly, by dividing the cathode assembly into parallel strips separated by gaps, and the atmosphere may be supplied direct to the working space through such gaps. Relative movement is effected between the cathode assembly and the substrate, e.g. by reciprocating the parallel strips of the divided cathode in the direction perpendicular to their length.
Inventors
- 👤 Robert David King
- 👤 Robert Hiscutt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:35
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/228; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C23C14/0021; C23C14/0036; C23C14/0063; H; H01; H01B; H01B1/00; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C03C2217/231; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/154; C03C2218/155
Claims Analysis
Total Claims: 52
Claim 1
Independent Claim
298 words
A method of depositing a transparent, electrically conducting, metal oxide film onto the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, said strips being spaced apart to define passages therebetween: b. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxygen and at least one other gas which is inert to oxygen and to the other materials in the vacuum chamber, at a controlled reduced pressure; e. heating the substrate to a selected, elevated temperature prior to a reactive sputtering step to be recited; d. maintaining a substantial degree of uniformity in the oxygen concentration in said working space by allowing said atmosphere to penetrate through the spaces between said spaced strips and into said working space; e. applying a high negative potential to the cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips on to the substrate; and f. maintaining the substrate at the selected, elevated temperature during the sputtering step; g. causing relative translatory movement between the cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 2
Independent Claim
298 words
A method of depositing a transparent, electrically conducting, metal oxide film onto the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, said strips being spaced apart to define passages therebetween: b. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxygen and at least one other gas which is inert to oxygen and to the other materials in the vacuum chamber, at a controlled reduced pressure; e. heating the substrate to a selected, elevated temperature prior to a reactive sputtering step to be recited; d. maintaining a substantial degree of uniformity in the oxygen concentration in said working space by allowing said atmosphere to penetrate through the spaces between said spaced strips and into said working space; e. applying a high negative potential to the cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips on to the substrate; and f. maintaining the substrate at the selected, elevated temperature during the sputtering step; g. causing relative translatory movement between the cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 3
Dependent Claim
34 words
A method according to claim 1 wherein the cathode assembly is formed from a metal having an atomic number between 48 and 51, alloyed with a metal of higher valency and similar atomic size.
Claim 4
Dependent Claim
16 words
A method according to claim 2 wherein the cathode assembly is formed from an indium/tin alloy,
Claim 5
Dependent Claim
24 words
A method according to claim 3 wherein the indium/tin alloy comprises between 75% and 95% indium and between 5% and 25% tin by weight.
Claim 6
Dependent Claim
16 words
A method according to claim 4 wherein the indium/tin alloy comprises 80% indium and 20% tin.
Claim 7
Dependent Claim
16 words
A method according to claim 4 wherein the indium/tin alloy comprises 88% indium and 12% tin.
Claim 8
Dependent Claim
21 words
A method according to claim 1 wherein the relative movement between the cathode assembly and the substrate is a reciprocating movement.
Claim 9
Dependent Claim
26 words
A method according to claim 1 wherein the amplitude of the relative movement is substantially equal to the spacing between the centre lines of adjacent strips.
Claim 10
Dependent Claim
17 words
A method according to claim 1 wherein the strips move on guide rails relative to the substrate.
Claim 11
Dependent Claim
57 words
A method according to claim 1 wherein the atmosphere is fed into the vacuum chamber at one end thereof and is exhausted therefrom at the opposite end thereof so that the atmosphere flow from inlet to exhaust tends to pass through the working space and thereby assists in maintaining uniformity of oxygen concentration in the working space.
Claim 12
Dependent Claim
12 words
A method according to claim 1, wherein the inert gas is argon.
Claim 13
Dependent Claim
63 words
A method according to claim 1 wherein the value of the negative potential applied to the cathode assembly is selected within the range -1KV to -5KV, the value of the oxygen concentration in the atmosphere in the working space is selected in the range between 1.5% and 4.8% by volume, and the temperature is selected within the range 240° C to 400° C.
Claim 14
Dependent Claim
27 words
A method according to claim 1 wherein the oxygen concentration in the atmosphere in the working space is maintained in the range 1% to 10% by volume.
Claim 15
Dependent Claim
22 words
A method according to claim 1 wherein the negative potential applied to the cathode assembly is between 1.0 KV and 5.0 KV.
Claim 16
Dependent Claim
22 words
A method according to claim 1 wherein the controlled elevated temperature of the substrate surface is between 240° C and 400° C.
Claim 17
Dependent Claim
14 words
A method according to claim 1 wherein the substrate is a sheet of glass.
Claim 18
Dependent Claim
28 words
A method according to claim 1 wherein the pressure in the vacuum chamber is between 1 × 10.sup. -2 mm Hg and 10 × 10.sup. -2 mm Hg.
Claim 19
Independent Claim
347 words
A method of depositing a transparent, electrically conducting, metal oxide film onto the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, the strips being spaced apart to define passages therebetween; b. enclosing the cathode assembly and the substrate within a vacuum chamber; c. supplying a sputtering atmosphere of oxygen and another gas or gases to the vacuum chamber; d. heating the substrate to an elevated temperature selected in accordance with criteria to be recited prior to a reactive sputtering step to be recited; e. applying a high negative potential to the cathode assembly to effect deposition of the metal oxide film by reactive sputtering; f. controlling the oxygen concentration in the vacuum chamber, the substrate temperature, the vacuum chamber pressure, and the cathode potential during the sputtering step at values selected such that the deposition coating is haze-free and its specific electrical resistivity lies at or close to the minimum of the curve which is obtained by plotting specific electrical resistivity against oxygen concentration while maintaining the substrate temperature, vacuum chamber pressure, and cathode potential all constant at selected values; g. maintaining a substantial degree of uniformity in the oxygen concentration in the working space by: i. allowing the sputtering atmosphere to penetrate through the spaces between the spaced strips and into the working space and ii. causing relative translatory movement between the cathode assembly and the substrate in a direction transverse to the length of the strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of the strips during the deposition process.
Claim 20
Independent Claim
347 words
A method of depositing a transparent, electrically conducting, metal oxide film onto the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, the strips being spaced apart to define passages therebetween; b. enclosing the cathode assembly and the substrate within a vacuum chamber; c. supplying a sputtering atmosphere of oxygen and another gas or gases to the vacuum chamber; d. heating the substrate to an elevated temperature selected in accordance with criteria to be recited prior to a reactive sputtering step to be recited; e. applying a high negative potential to the cathode assembly to effect deposition of the metal oxide film by reactive sputtering; f. controlling the oxygen concentration in the vacuum chamber, the substrate temperature, the vacuum chamber pressure, and the cathode potential during the sputtering step at values selected such that the deposition coating is haze-free and its specific electrical resistivity lies at or close to the minimum of the curve which is obtained by plotting specific electrical resistivity against oxygen concentration while maintaining the substrate temperature, vacuum chamber pressure, and cathode potential all constant at selected values; g. maintaining a substantial degree of uniformity in the oxygen concentration in the working space by: i. allowing the sputtering atmosphere to penetrate through the spaces between the spaced strips and into the working space and ii. causing relative translatory movement between the cathode assembly and the substrate in a direction transverse to the length of the strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of the strips during the deposition process.
Claim 21
Dependent Claim
16 words
A method according to claim 18 wherein the cathode assembly is formed from an indium/tin alloy.
Claim 22
Dependent Claim
24 words
A method according to claim 19 wherein the indium/tin alloy comprises between 75% and 95% indium and between 5% and 25% tin by weight.
Claim 23
Dependent Claim
16 words
A method according to claim 20 wherein the indium/tin alloy comprises 80% indium and 20% tin.
Claim 24
Dependent Claim
16 words
A method according to claim 21 wherein the indium/tin alloy comprises 88% indium and 12% tin.
Claim 25
Dependent Claim
36 words
A method according to claim 18 wherein the atmosphere comprises a mixture of oxygen and a gas which is at least substantially inert to the remainder of the atmosphere and the materials in the vacuum chamber.
Claim 26
Dependent Claim
12 words
A method according to claim 23, wherein the inert gas is argon.
Claim 27
Dependent Claim
26 words
A method according to claim 18 wherein the amplitude of the relative movement is substantially equal to the spacing between the centre lines of adjacent strips.
Claim 28
Dependent Claim
17 words
A method according to claim 18 wherein the strips move on guide rails relative to the substrate.
Claim 29
Dependent Claim
57 words
A method according to claim 18 wherein the atmosphere is fed into the vacuum chamber at one end thereof and is exhausted therefrom at the opposite end thereof so that the atmosphere flow from inlet to exhaust tends to pass through the working space and thereby assists in maintaining uniformity of oxygen concentration in the working space.
Claim 30
Dependent Claim
63 words
A method according to claim 18 wherein the value of the negative potential applied to the cathode assembly is selected within the range -1KV to -5KV, the value of the oxygen concentration in the atmosphere in the working space is selected in the range between 1.5% and 4.8% by volume, and the temperature is selected within the range 240° C to 400° C.
Claim 31
Dependent Claim
27 words
A method according to claim 18 wherein the oxygen concentration in the atmosphere in the working space is maintained in the range 1% to 10% by volume.
Claim 32
Dependent Claim
34 words
A method according to claim 18, wherein the cathode assembly is formed from a metal having an atomic number between 48 and 51, alloyed with a metal of higher valency and similar atomic volume.
Claim 33
Dependent Claim
14 words
A method according to claim 18 wherein the substrate is a sheet of glass.
Claim 34
Dependent Claim
28 words
A method according to claim 18 wherein the pressure in the vacuum chamber is between 1 × 10.sup. -2 mm Hg and 10 × 10.sup. -2 mm Hg.
Claim 35
Independent Claim
327 words
A method of depositing a transparent, electrically conducting film of an oxide of metal of atomic number 48 to 51 on to the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising said metal, said strips being spaced apart to define passages therebetween; b. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxgyen and an inert gas with a controlled oxygen concentration of between 1% and 10% by volume, at a controlled reduced pressure of between 1 × 10.sup. -2 mm Hg and 10 × 10.sup. -2 mm Hg; c. heating the substrate to a selected, elevated temperature between 240° C and 400° C prior to a reactive sputtering step to be recited; d. maintaining a substantial degree of uniformity in the oxygen concentration in the working space by allowing said atmosphere to penetrate through the spaces between said spaced strips into the working space; c. applying a high negative potential of between -1 KV and -5 KV to the cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips on to the substrate surface; f. maintaining the substrate at the selected, elevated temperature during the sputtering step; and g. causing relative reciprocating movement between the cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 36
Independent Claim
327 words
A method of depositing a transparent, electrically conducting film of an oxide of metal of atomic number 48 to 51 on to the surface of a substrate of extended lateral dimensions, said method comprising the steps of: a. arranging a cathode assembly whose overall lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising said metal, said strips being spaced apart to define passages therebetween; b. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxgyen and an inert gas with a controlled oxygen concentration of between 1% and 10% by volume, at a controlled reduced pressure of between 1 × 10.sup. -2 mm Hg and 10 × 10.sup. -2 mm Hg; c. heating the substrate to a selected, elevated temperature between 240° C and 400° C prior to a reactive sputtering step to be recited; d. maintaining a substantial degree of uniformity in the oxygen concentration in the working space by allowing said atmosphere to penetrate through the spaces between said spaced strips into the working space; c. applying a high negative potential of between -1 KV and -5 KV to the cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips on to the substrate surface; f. maintaining the substrate at the selected, elevated temperature during the sputtering step; and g. causing relative reciprocating movement between the cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 37
Dependent Claim
22 words
A method according to claim 33 wherein said metal is alloyed with a metal of a higher valency and similar atomic volume.
Claim 38
Dependent Claim
16 words
A method according to claim 34 wherein the cathode assembly is formed from an indium/tin alloy.
Claim 39
Dependent Claim
24 words
A method according to claim 34 wherein the indium/tin alloy comprises between 75% and 95% indium and between 5% and 25% tin by weight.
Claim 40
Dependent Claim
16 words
A method according to claim 35 wherein the indium/tin alloy comprises 80% indium and 20% tin.
Claim 41
Dependent Claim
16 words
A method according to claim 35 wherein the indium/tin alloy comprises 88% indium and 12% tin.
Claim 42
Dependent Claim
26 words
A method according to claim 33 wherein the amplitude of the relative movement is substantially equal to the spacing between the centre lines of adjacent strips.
Claim 43
Dependent Claim
17 words
A method according to claim 33 wherein the strips move on guide rails relative to the substrate.
Claim 44
Dependent Claim
57 words
A method according to claim 33 wherein the atmosphere is fed into the vacuum chamber at one end thereof and is exhausted therefrom at the opposite end thereof so that the atmosphere flow from inlet to exhaust tends to pass through the working space and thereby assists in maintaining uniformity of oxygen concentration in the working space.
Claim 45
Dependent Claim
12 words
A method according to claim 33 wherein the inert gas is argon.
Claim 46
Dependent Claim
31 words
A method according to claim 33 wherein the value of the oxygen concentration in the atmosphere in the working space is selected in the range between 1.5% and 4.8% by volume.
Claim 47
Dependent Claim
14 words
A method according to claim 33 wherein the substrate is a sheet of glass.
Claim 48
Dependent Claim
417 words
An article having its smallest lateral dimension greater than 30 cm. and having a stable transparent electrically conductive film deposited on a surface thereof, said film: a. having a specific electrical resistivity of between 2 × 10.sup. -4 ohm cm. and 20 × 10.sup. -4 ohm cm., which resistivity is substantially uniform over the whole of said film; b. having a thickness which is everywhere less than 10,000A; c. having a light transmission figure of over 70%; and d. having been deposited by a reactive sputtering method comprising the steps of: i. arranging a cathode assembly whose overal lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, said strips being spaced apart to define passages therebetween; ii. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxygen and at least one other gas which is inert to oxygen and to the other materials in the vacuum chamber, at a controlled reduced pressure; iii. heating the substrate to a selected, elevated temperature prior to sputtering; iv. maintaining a substantial degree of uniformity in the oxygen concentration in said working space by allowing said atmosphere to penetrate through the spaces between said spaced strips into said working space; v. maintaining the substrate at the selected, elevated temperature during sputtering; vi. applying a high negative potential to said cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips onto the substrate; vii. selecting the value of the oxygen concentration, substrate temperature, vacuum chamber pressure, and cathode potential such that the deposited coating is haze-free and its specific electrical resistivity lies at or close to the minimum of the curve which is obtained by plotting specific electrical resistivity against oxygen concentration while maintaining the substrate temperature, vacuum chamber pressure, and cathode potential all constant at selected values and e. causing relative translatory movement between said cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 49
Dependent Claim
417 words
An article having its smallest lateral dimension greater than 30 cm. and having a stable transparent electrically conductive film deposited on a surface thereof, said film: a. having a specific electrical resistivity of between 2 × 10.sup. -4 ohm cm. and 20 × 10.sup. -4 ohm cm., which resistivity is substantially uniform over the whole of said film; b. having a thickness which is everywhere less than 10,000A; c. having a light transmission figure of over 70%; and d. having been deposited by a reactive sputtering method comprising the steps of: i. arranging a cathode assembly whose overal lateral dimensions are not substantially less than those of the substrate in the vicinity of the substrate but spaced apart therefrom to define a working space between the cathode assembly and the substrate surface, the cathode assembly being so constructed as to present a plurality of elongated, side-by-side strips comprising a metal capable of being reactively sputtered, said strips being spaced apart to define passages therebetween; ii. enclosing the cathode assembly and the substrate within a vacuum chamber containing an atmosphere of oxygen and at least one other gas which is inert to oxygen and to the other materials in the vacuum chamber, at a controlled reduced pressure; iii. heating the substrate to a selected, elevated temperature prior to sputtering; iv. maintaining a substantial degree of uniformity in the oxygen concentration in said working space by allowing said atmosphere to penetrate through the spaces between said spaced strips into said working space; v. maintaining the substrate at the selected, elevated temperature during sputtering; vi. applying a high negative potential to said cathode assembly to effect deposition of said metal oxide film by reactive sputtering substantially perpendicularly from said strips onto the substrate; vii. selecting the value of the oxygen concentration, substrate temperature, vacuum chamber pressure, and cathode potential such that the deposited coating is haze-free and its specific electrical resistivity lies at or close to the minimum of the curve which is obtained by plotting specific electrical resistivity against oxygen concentration while maintaining the substrate temperature, vacuum chamber pressure, and cathode potential all constant at selected values and e. causing relative translatory movement between said cathode assembly and the substrate in a direction transverse to the length of said strips, through an amplitude substantially smaller than the overall length of the cathode assembly, but sufficient to cause all parts of the substrate surface to be coated by sputtering from at least one of said strips during the deposition process.
Claim 50
Dependent Claim
22 words
An article as recited in claim 45 wherein the thickness of said film is substantially uniform over the whole of said film.
Claim 51
Dependent Claim
15 words
An article as recited in claim 45 wherein the substrate is a sheet of glass.
Claim 52
Dependent Claim
19 words
An article as recited in claim 45 wherein the thickness of said film is everywhere greater than 500° A.
References Cited (Backward Citations)
US3414503A
Cited
US3619402A
Cited
GB1201743A
Cited
GB1147318A
Cited
DE1938131A1
Cited
US3630873A
Cited
US3907660A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-01 | 1980-08-02 | 1981-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-01 | 1984-08-02 | 1985-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-01 | 1988-08-02 | 1989-02-01 | $7700.00 | Window Closed / Lapsed |