Impervious absorbent barrier fabric embodying films and fibrous webs

Claim 2

An absorbent impervious barrier fabric comprising a fibrous section including a mat of polymeric melt blown microfibers with an average diameter of up to about 10 microns and a basis weight between about 0.3 oz/yd 2 and 4.0 oz/yd 2 , and an impervious polymeric film between about 0.0006 and 0.0016 inches thick adjacent said mat, said fibrous section and film being united in a pattern of compacted bond regions occupying less than about 15 percent of the total area and formed by the application of heat and pressure, said bond regions comprising pillars of bonds extending completely through the fabric from the outer surface where the fibrous elements are fused, to the interface between the mat and the film where the microfibers are fused to the film and the film has increased crystallinity in the bond regions without disruptions in the imperviousness of the film, the bond intensity tapering from said fused regions toward a low bonding level in the central plane of said mat to provide a double gradient in bond intensity in said pillars of bonds, the surface of the fibrous section of the fabric having a shape formed by depressions in the bond regions, providing a three dimensional configuration.

Claim 3

The nonwoven fabric of claim 1 wherein said fibrous section which includes said microfiber mat further includes a surface layer web of continuous and randomly deposited molecularly oriented filaments of a thermoplastic polymer with an average filament diameter in excess of about 12 microns, said web having intermittently discrete prebonded regions formed by the application of heat and pressure, the combination of said prebonded regions and said fused regions providing a stabilized abrasion resistant, textured surface.

Claim 4

The nonwoven fabric of claim 2 wherein said microfibers are entangled and bonded with the filaments of said continuous filament web as the mat is formed.

Claim 5

The fabric according to claims 1, 2 or 3 wherein the surface of said fibrous section has a slip resistance of at least about 20 degrees.

Claim 6

The fabric according to claim 1 wherein said fibrous section consists essentially of said microfiber mat and the microfibers are fused in the bond regions in the surface of said mat to stabilize the surface of the fabric.

Claim 7

The fabric according to claims 1, 2, 3, or 5 including surfactant on the surface of microfibers of said mat to increase absorbent capacity of said mat for aqueous solutions.

Claim 8

The fabric according to claims 2 or 3 including a salt on the continuous filaments to increase conductivity of said fabric.

Claim 9

The fabric according to claims 1, 2, 3, or 5 wherein said polymeric microfibers, said polymeric filaments and said polymeric film are of compatible polymers, copolymers or mixtures thereof from the group consisting of polyolefins, polyurethanes, polyvinyls, polyamides, and polyesters.

Claim 10

The fabric according to claim 8 wherein the microfibers, filaments and film are all made from the same polymers, copolymers or mixtures thereof.

Claim 11

The fabric according to claims 1, 2, 3, or 5 wherein the microfibers, filaments and film are polypropylene.

Claim 12

A process for the manufacture of an absorbent impervious barrier fabric comprising: forming a fibrous section including a mat of polymeric melt blown microfibers with an average diameter of up to about 10 microns and a basis weight between about 0.3 oz/yd 2 and 4.0 oz/yd 2 ; bringing an impervious polymeric film between about 0.0006 and 0.0016 inches thick adjacent said mat; passing said fibrous section and said film through the nip between heated rolls, with one of said rolls in contact with said fibrous section having a pattern of raised areas occupying less than about 15 percent of the surface of the roll and the other roll in contact with said film having a smooth surface, and applying pressure to said fibrous section and film by means of said rolls so as to form bond regions in said fabric; controlling the temperature of the rolls and the nip pressure to form pillars of bonds extending completely through the fabric from the outer surface where the fibrous elements are fused, to the interface between the mat and the film where the microfibers are fused to the film and the film has increased crystallinity in the bond regions without disrupting the imperviousness of the film, and to shape the surface of the fibrous section of the fabric to provide depressions in the bond regions and a three dimensional surface configuration.

Claim 13

A process for the manufacture of an absorbent impervious barrier fabric comprising: forming a fibrous section including a mat of polymeric melt blown microfibers with an average diameter of up to about 10 microns and a basis weight between about 0.3 oz/yd 2 and 4.0 oz/yd 2 ; bringing an impervious polymeric film between about 0.0006 and 0.0016 inches thick adjacent said mat; passing said fibrous section and said film through the nip between heated rolls, with one of said rolls in contact with said fibrous section having a pattern of raised areas occupying less than about 15 percent of the surface of the roll and the other roll in contact with said film having a smooth surface, and applying pressure to said fibrous section and film by means of said rolls so as to form bond regions in said fabric; controlling the temperature of the rolls and the nip pressure to form pillars of bonds extending completely through the fabric from the outer surface where the fibrous elements are fused, to the interface between the mat and the film where the microfibers are fused to the film and the film has increased crystallinity in the bond regions without disrupting the imperviousness of the film, and to shape the surface of the fibrous section of the fabric to provide depressions in the bond regions and a three dimensional surface configuration.

Claim 14

The process of claim 11 wherein said step of forming a fibrous section includes providing a web of continuous and randomly deposited molecularly oriented filaments of a thermoplastic polymer with an average filament diameter in excess of 12 microns, said web having intermittent discrete prebonded regions formed by the application of heat and pressure, and forming said mat of microfibers on said prebonded continuous filament web so as to entangle and provide primary bonds between the microfibers and the filaments of said fibrous section.

Claim 15

A process for the manufacture of an absorbent impervious barrier fabric comprising: providing a web of continuous and randomly deposited molecularly oriented filaments of a thermoplastic polymer with an average filament diameter in excess of 12 microns, said web having intermittent discrete prebonded regions formed by the application of heat and pressure; forming a mat of polymeric melt blown microfibers with an average diameter of up to about 10 microns and a basis wieght between about 0.3 oz/yd 2 and 4.0 oz/yd 2 on said web so as to entangle and provide primary bonds between the microfibers and the filaments and provide a fibrous section; bringing an impervious polymeric film between about 0.0006 and 0.0016 inches thick adjacent the surface of said mat of said fibrous section; passing said fibrous section and said film through the nip between heated rolls, with one of said rolls in contact with said fibrous section having a pattern of raised areas occupying less than about 15 percent of the surface of the roll and the other roll in contact with said film having a smooth surface, and applying pressure to said fibrous section and film by means of said rolls so as to form bond regions in said fabric; and controlling the temperature of the rolls and the nip pressure to form pillars of bonds extending completely through the fabric from the outer surface where the fibrous elements are fused, to the interface between the mat and the film where the microfibers are fused to the film and the film has increased crystallinity in the bond regions without disrupting the imperviousness of the film, and to shape the surface of the fibrous section of the fabric to provide depressions in the bond regions and a three dimensional surface configuration.

Claim 16

A process for the manufacture of an absorbent impervious barrier fabric comprising: providing a web of continuous and randomly deposited molecularly oriented filaments of a thermoplastic polymer with an average filament diameter in excess of 12 microns, said web having intermittent discrete prebonded regions formed by the application of heat and pressure; forming a mat of polymeric melt blown microfibers with an average diameter of up to about 10 microns and a basis wieght between about 0.3 oz/yd 2 and 4.0 oz/yd 2 on said web so as to entangle and provide primary bonds between the microfibers and the filaments and provide a fibrous section; bringing an impervious polymeric film between about 0.0006 and 0.0016 inches thick adjacent the surface of said mat of said fibrous section; passing said fibrous section and said film through the nip between heated rolls, with one of said rolls in contact with said fibrous section having a pattern of raised areas occupying less than about 15 percent of the surface of the roll and the other roll in contact with said film having a smooth surface, and applying pressure to said fibrous section and film by means of said rolls so as to form bond regions in said fabric; and controlling the temperature of the rolls and the nip pressure to form pillars of bonds extending completely through the fabric from the outer surface where the fibrous elements are fused, to the interface between the mat and the film where the microfibers are fused to the film and the film has increased crystallinity in the bond regions without disrupting the imperviousness of the film, and to shape the surface of the fibrous section of the fabric to provide depressions in the bond regions and a three dimensional surface configuration.

Claim 17

The process of claim 13 wherein said microfibers, filaments and film are polypropylene.

Claim 18

The process of claim 14 wherein said pattern roll is heated to a temperature between about 300-500 degrees F. and said smooth roll is heated to a temperature between about 200-260 degrees. F..

Claim 19

The process of claim 15 wherein a varying bond density is obtained in said mat which decreases from said fused regions towards a low bonding level in the central plane of said mat to provide a double gradient in bond intensity in said pillars of bonds.

Claim 20

The process of claims 11, 12 or 13 wherein said polymeric microfibers are polypropylene, further including applying surfactant in a spray to the microfibers after extrusion and before formation into a mat to make the polypropylene microfibers wettable and to enhance utilization of the absorbent capacity of the mat for aqueous solutions.

Claim 21

The process of claim 11 wherein said polymeric microfibers and said polymeric film are polypropylene.

Claim 22

The process of claims 12 or 13 wherein said polymeric microfibers, said polymeric filaments and said polymeric film are of the same polymer, copolymer or mixtures thereof from the group consisting of polyolefins, polyurethanes, polyvinyls, polyamides and polyesters.

Claim 23

The process of claims 12, 13, 14, 15, 16, or 18 further including applying surfactant to the mat to make the polypropylene microfibers wettable and improve utilization of the absorbent capacity of the mat for aqueous solutions.