US4041203A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Nonwoven thermoplastic fabric
Assignee: Kimberly Clark Corp
•
Filing: 1976-10-04
•
Granted: 1977-08-09
•
Expires: 1996-10-04
Abstract
Abstract A non-woven fabric-like material comprising an integrated mat of generally discontinuous, thermoplastic polymeric microfibers and a web of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer. The polymeric microfibers have an average fiber diameter of up to about 10 microns while the average diameter of filaments in the continuous filament web is in excess of about 12 microns. Attachment between the microfiber mat and continuous filament web is achieved at intermittent discrete regions in a manner so as to integrate the continuous filament web into an effective load bearing constituent of the material. The material has desirable strength characteristics and possesses a textile-like appearance, drape and hand. By autogenously bonding the mat and web together in a manner so as to provide substantially uniform discrete bond regions, particularly outstanding strength characteristics with respect to energy absorption, tensile strength, and tear resistance can be achieved.
Inventors
- 👤 Robert J. Brock
- 👤 Gary H. Meitner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 16:32
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B5/02; B32B5/08; B32B37/00; B32B37/14; B32B37/15; B32B38/00; B32B38/06; B32B5/022; D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/559; D04H1/56; D04H3/00; D04H3/08; D04H3/14; A; A61; A61B; A61B42/00; A61B42/40; A61B46/00; A61B46/10; A61M; A61M5/00; A61M5/002; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2262/0261; B32B2262/14; B32B2307/00; B32B2307/70; B32B2307/718; B32B2309/00; B32B2309/02; B32B2309/12; B32B2309/14; B32B37/16; B32B37/20; B32B37/203; B32B37/206; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24488; Y10T428/24942; Y10T428/27; Y10T442/00; Y10T442/60; Y10T442/608; Y10T442/614; Y10T442/626; Y10T442/659; Y10T442/69
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
134 words
A nonwoven fabric-like material comprising a web of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer having an average filament diameter in excess of about 12 microns and an integrated mat of generally discontinuous, thermoplastic polymeric microfibers having an average fiber diameter of up to about 10 microns and a softening temperature of about 10°-40°C. less than the softening temperature of the continuous filaments; said web and mat being positioned in laminar surface-to-surface relationship and united together at intermittent discrete bond regions formed by the application of heat and pressure to thereby provide a unitary structure having desirable textile-like appearance and drape characteristics and to integrate the web of substantially continuous filaments so that said web can function as an effective load bearing constituent of the material during straining thereof.
Claim 2
Dependent Claim
134 words
A nonwoven fabric-like material comprising a web of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer having an average filament diameter in excess of about 12 microns and an integrated mat of generally discontinuous, thermoplastic polymeric microfibers having an average fiber diameter of up to about 10 microns and a softening temperature of about 10°-40°C. less than the softening temperature of the continuous filaments; said web and mat being positioned in laminar surface-to-surface relationship and united together at intermittent discrete bond regions formed by the application of heat and pressure to thereby provide a unitary structure having desirable textile-like appearance and drape characteristics and to integrate the web of substantially continuous filaments so that said web can function as an effective load bearing constituent of the material during straining thereof.
Claim 3
Dependent Claim
32 words
The nonwoven fabric-like material of claim 1 wherein the discrete bond regions are present in a density of about 50-1,000/in. 2 and occupy about 5-50% of the surface area of the material.
Claim 4
Dependent Claim
32 words
The nonwoven fabric-like material of claim 1 wherein the discrete bond regions are present in a density of about 100-500/in. 2 and occupy about 10-30% of the surface area of the material.
Claim 5
Dependent Claim
28 words
The nonwoven fabric-like material of claim 3 wherein the intermittent discrete bond regions are uniformly bonded without a substantial degree of fusion of the continuous filament occurring therein.
Claim 6
Dependent Claim
19 words
The nonwoven fabric-like material of claim 4 having a basis weight of up to about 4 oz./yd. 2 .
Claim 7
Dependent Claim
24 words
The nonwoven fabric-like material of claim 5 wherein the average filament diameter of the filaments of the continuous filament web is about 12-55 microns.
Claim 8
Dependent Claim
24 words
The nonwoven fabric-like material of claim 6 wherein the average filament diameter of the filaments of the continuous filament web is about 15-25 microns.
Claim 9
Dependent Claim
23 words
The nonwoven fabric-like material of claim 7 wherein the ratio of the mat to the web is about 0.2:1 to 4:1 by weight.
Claim 10
Dependent Claim
17 words
The nonwoven fabric-like material of claim 8 having a basis weight of about 0.75-2.5 oz./yd. 2 .
Claim 11
Dependent Claim
20 words
The nonwoven fabric-like material of claim 9 wherein the thermoplastic polymer filaments and the thermoplastic polymeric microfibers are of polypropylene.
Claim 12
Dependent Claim
36 words
The nonwoven fabric-like material of claim 1 wherein a second polymeric microfiber mat is united to the web on the other surface thereof to provide a material which is highly suitable for decorative or informative printing.
Claim 13
Dependent Claim
195 words
A sterile wrap for wrapping about items to be sterilized for subsequent use in surgical procedures, said sterile wrap having a surface resistivity of less than 1 × 10.sup. 12 ohms/square and comprising a web, having a basis weight of at least about 0.5 oz./yd. 2 of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer having an average filament diameter in excess of about 12 microns and, to provide bacterial barrier properities and yet allow sterilant penetration, an integrated mat, having a basis weight of at least about 0.3 oz./yd. 2 , of generally discontinuous, thermoplastic polymeric microfibers having an average fiber diameter of up to about 10 microns, said web and mat being positioned in laminar surface-to-surface relationship and united together at intermittent discrete bond regions formed by the application of heat and pressure to thereby provide a unitary structure having a desirable textile-like appearance and drape characteristics and to integrate the web of substantially continuous filaments and the microfiber mat so that said web can function as an effective load bearing constituent of the material while said mat retains said sterilant penetration and bacterial barrier properties in said material.
Claim 14
Dependent Claim
195 words
A sterile wrap for wrapping about items to be sterilized for subsequent use in surgical procedures, said sterile wrap having a surface resistivity of less than 1 × 10.sup. 12 ohms/square and comprising a web, having a basis weight of at least about 0.5 oz./yd. 2 of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer having an average filament diameter in excess of about 12 microns and, to provide bacterial barrier properities and yet allow sterilant penetration, an integrated mat, having a basis weight of at least about 0.3 oz./yd. 2 , of generally discontinuous, thermoplastic polymeric microfibers having an average fiber diameter of up to about 10 microns, said web and mat being positioned in laminar surface-to-surface relationship and united together at intermittent discrete bond regions formed by the application of heat and pressure to thereby provide a unitary structure having a desirable textile-like appearance and drape characteristics and to integrate the web of substantially continuous filaments and the microfiber mat so that said web can function as an effective load bearing constituent of the material while said mat retains said sterilant penetration and bacterial barrier properties in said material.
Claim 15
Dependent Claim
19 words
The sterile wrap of claim 12 wherein the thermoplastic polymer filaments and the thermoplastic polymeric microfibers are of polypropylene.
Claim 16
Dependent Claim
20 words
The sterile wrap of claim 13 having a basis weight of about 0.8 oz./yd. 2 - 2 oz./yd. 2 .
Claim 17
Dependent Claim
18 words
The sterile wrap of claim 14 having a surface resistivity of less than 1 × 10 11 ohms/square.
Claim 18
Dependent Claim
22 words
The sterile wrap of claim 15 wherein the ratio of the mat to the web is less than about 1:1 by weight.
Claim 19
Dependent Claim
20 words
The sterile wrap of claim 16 wherein the ratio of the mat to the web is about 0.7:1-0.9:1 by weight.
Claim 20
Dependent Claim
16 words
The sterile wrap of claim 17 having a basis weight of about 1.1-1.5 oz./yd. 2 .
Claim 21
Dependent Claim
44 words
The sterile wrap of claim 12 wherein a second web having a basis weight of at least about 0.5 oz./yd. 2 of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer is united to the mat on the other surface thereof.
Claim 22
Dependent Claim
31 words
The sterile wrap of claim 12 wherein the discrete bond regions are present in a density of about 50-1,000/in. 2 and occupy about 5-50% of the surface area of the material.
Claim 23
Dependent Claim
31 words
The sterile wrap of claim 12 wherein the discrete bond regions are present in a density of about 100-500/in. 2 and occupy about 10-30% of the surface area of the material.
Claim 24
Dependent Claim
27 words
The sterile wrap of claim 21 wherein the intermittent discrete bond regions are uniformly bonded without a substantial degree of fusion of the continuous filaments occurring therein.
Claim 25
Dependent Claim
23 words
The sterile wrap of claim 12 wherein the average filament diameter of the filaments of the continuous filament web is about 12-55 microns.
Claim 26
Dependent Claim
23 words
The sterile wrap of claim 24 wherein the average filament diameter of the filaments of the continuous filament web is about 15-25 microns.
Claim 27
Dependent Claim
35 words
The sterile wrap of claim 12 wherein a second polymeric microfiber mat is united to the web on the other surface thereof to provide a material which is highly suitable for decorative or informative printing.
Claim 28
Dependent Claim
34 words
The nonwoven fabric-like material of claim 1 wherein a second web of substantially continuous and randomly deposited, molecularly oriented filaments of a thermoplastic polymer is united to the mat on the other surface thereof.
References Cited (Backward Citations)
US3016599A
Cited
US3341394A
Cited
US3849241A
Cited
US3676242A
Cited
US3704198A
Cited
US3755527A
Cited
US3795571A
Cited
US3837995A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |