Nonwoven fibrous substrate for battery separator
Assignee: Dexter Corp
•
Filing: 1978-11-09
•
Granted: 1981-07-21
•
Expires: 1998-11-09
Abstract
Abstract A substrate for an alkaline battery separator is made of a light weight, porous, heat bonded, synthetic organic sheet material having a basis weight of less than about 35 gsm and a thickness of less than about 200 microns. The major fibrous component is synthetic pulp comprising thermoplastic polyolefin fibers having a prefused microfibrillar structure similar to wood pulp. The minor fibrous component is a high tenacity polyamide fiber having a fiber length greater than about 6 mm. The heat bonding by partial fusion of the microfibrillar polyolefin is sufficient to impart to the sheet material a wet tensile strength of at least 400 g/in. width while permitting retention of air permeability of about 100 liters per minute and more. The substrate exhibits excellent receptivity to impregnation by pore-forming battery separator coatings and is particularly well suited for use in nickel-zinc batteries.
Inventors
- 👤 Arthur L. Benson
- 👤 David A. Jordan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:40
CPC Classifications
D; D21; D21H; D21H5/00; D21H5/12; D21H5/20; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/423; H01M50/44; H01M50/489; H01M50/494; H01M2300/00; H01M2300/0002; H01M2300/0014; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T442/00; Y10T442/60; Y10T442/69; Y10T442/692
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
156 words
A nonwoven fibrous web material suited for use as a substrate for an alkaline battery separator comprising a light weight, porous, heat bonded, synthetic organic sheet material resistant to degradation upon prolonged exposure at elevated temperatures to a highly concentrated alkaline environment, said fibrous web material having a basis weight of less than 50 gsm and a thickness of less than about 200 microns, a major fibrous component of the web being a synthetic thermoplastic polyolefin fiber having a microfibrillar structure comprised of microfibrils similar to wood pulp, a minor fibrous component of the web being a polyamide fiber having a fiber length greater than about 6 mm, the heat bonding by partial fusion of the microfibrillar polyolefin being sufficient to impart to the sheet material a wet tensile strength of at least 400 g/in. width while retaining an air permeability greater than about 50 liters/min., said substrate exhibiting excellent receptivity to pore-forming battery separator coatings.
Claim 2
Dependent Claim
156 words
A nonwoven fibrous web material suited for use as a substrate for an alkaline battery separator comprising a light weight, porous, heat bonded, synthetic organic sheet material resistant to degradation upon prolonged exposure at elevated temperatures to a highly concentrated alkaline environment, said fibrous web material having a basis weight of less than 50 gsm and a thickness of less than about 200 microns, a major fibrous component of the web being a synthetic thermoplastic polyolefin fiber having a microfibrillar structure comprised of microfibrils similar to wood pulp, a minor fibrous component of the web being a polyamide fiber having a fiber length greater than about 6 mm, the heat bonding by partial fusion of the microfibrillar polyolefin being sufficient to impart to the sheet material a wet tensile strength of at least 400 g/in. width while retaining an air permeability greater than about 50 liters/min., said substrate exhibiting excellent receptivity to pore-forming battery separator coatings.
Claim 3
Dependent Claim
49 words
The nonwoven web material of claim 1 wherein the synthetic fiber pulp is present in an amount within the range of 50% to 80% by weight and the polyamide fibers are of high tenacity and are present in an amount within the range of 10% to 50% by weight.
Claim 4
Dependent Claim
38 words
The nonwoven web material of claim 1 wherein the basis weight is less than about 35 gsm, the synthetic fiber pulp is a high density polyolefin of low melt index and a high molecular weight greater than 40,000.
Claim 5
Dependent Claim
47 words
The nonwoven web material of claim 1 having a thickness within the range of 50-150 microns, the synthetic fiber pulp having a melting point in the range of 135°-150° C., and the web being partially fused sufficiently to provide a wet tensile strength of 800 g/in. width.
Claim 6
Dependent Claim
69 words
The nonwoven web material of claim 1 wherein the synthetic fiber pulp is a water dispersible high density polyolefin selected from the group consisting of polyethylene, polypropylene and mixtures thereof having a melt index below 0.1, and a high molecular weight greater than 500,000, said high density polyolefin including less than 5% by weight of a wetting agent enhancing the wettability of said web by said battery separator coating.
Claim 7
Dependent Claim
55 words
The nonwoven web material of claim 1 wherein the synthetic fiber pulp consists essentially of high density polyethylene having a melting point in the range of 135°-150° C., said partial fusion being no more than that obtained upon exposure of the web to a temperature equal to said melting point for less than 3 minutes.
Claim 8
Dependent Claim
27 words
The nonwoven web of claim 6 wherein said partial fusion is no more than that obtained upon exposure of said web to 270° F. for 1.5-2.0 minutes.
Claim 9
Dependent Claim
44 words
The nonwoven web material of claim 1 wherein the basis weight is less than about 35 gsm, the wet tensile strength is greater than 800 g/in. width, the air permeability is at least 200 liters per minute and said web includes polyolefin staple fibers.
Claim 10
Dependent Claim
83 words
The nonwoven web material of claim 1 wherein the polyamide fibers are of 6 denier and less, a length of 10 mm. and more and constitute 10-50% by weight of the fiber content, the web including 10-30% by weight of polyolefin staple fibers, the partial fusion being no more than that obtained upon exposure of said web to 270° F. for less than 3 minutes, said web being resistant to degradation upon exposure to 31% KOH at 80° C. for over 300 hours.
Claim 11
Dependent Claim
91 words
The nonwoven web material of claim 1 wherein the basis weight is about 22-28 gsm, the thickness is 75-130 microns, the synthetic fiber similar to wood pulp consists essentially of water dispersible high density polyethylene having a melting point in the range of 135°-150° C. and a molecular weight greater than 800,000, said synthetic pulp being present in amounts of 55%-65% by weight, the polyamide fibers constituting 10-25% by weight, said web including 10-30% by weight of a snythetic organic staple fiber compatable with said synthetic pulp and said polyamide fibers.
References Cited (Backward Citations)
US3016599A
Cited
US2973398A
Cited
US3560318A
Cited
US3573994A
Cited
US3811957A
Cited
US4078124A
Cited
US3947537A
Cited
US3972759A
Cited
US4041203A
Cited
US3967978A
Cited
US4048364A
Cited
US4118531A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |