Porous sheets and method of manufacture
Assignee: Porex Technologies Corp
•
Filing: 1979-02-15
•
Granted: 1981-03-17
•
Expires: 1999-02-15
Abstract
Abstract A porous thermoplastic sheet is formed by adding a material to a polymer latex to passivate the aqueous phase of the latex. An additional material of a preselected particle size, corresponding to the desired pore size of the final product is then added. The latex composition is gelled and is then formed into a sheet. The sheet is dried and cured or sintered and the solubles are extracted therefrom with a solvent. A preferred polymer latex is PTFE.
Inventors
- 👤 Harold B. Morris
- 👤 Donald G. Bright
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:45
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/26; B; B29; B29C; B29C67/00; B29C67/20; B29C67/202; Y; Y10; Y10S; Y10S264/00; Y10S264/02; Y10S521/00; Y10S521/919
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
163 words
A process for producing a porous polymer sheet comprising: (a) adding a first water soluble salt to a polymer latex in an amount sufficient to passivate the aqueous phase of the latex; (b) heating and agitating the polymer latex to passivate the aqueous phase; (c) adding to the polymer latex passivated with said first salt, a second water soluble salt of a preselected particle size corresponding to the desired pore size for the end-product polymer sheet and in an amount preselected to provide the desired porosity; (d) heating and agitating the latex containing said first salt and said second salt until a continuous, coherent dough-like material forms; (e) mechanically working the polymer material obtained in step (d); (f) forming the material into a sheet of the desired thickness; (g) drying and then curing or sintering the sheet; (h) extracting said first and second salts from the cured or sintered sheet with solvent; and (i) drying the extracted sheet to obtain the porous product.
Claim 2
Dependent Claim
163 words
A process for producing a porous polymer sheet comprising: (a) adding a first water soluble salt to a polymer latex in an amount sufficient to passivate the aqueous phase of the latex; (b) heating and agitating the polymer latex to passivate the aqueous phase; (c) adding to the polymer latex passivated with said first salt, a second water soluble salt of a preselected particle size corresponding to the desired pore size for the end-product polymer sheet and in an amount preselected to provide the desired porosity; (d) heating and agitating the latex containing said first salt and said second salt until a continuous, coherent dough-like material forms; (e) mechanically working the polymer material obtained in step (d); (f) forming the material into a sheet of the desired thickness; (g) drying and then curing or sintering the sheet; (h) extracting said first and second salts from the cured or sintered sheet with solvent; and (i) drying the extracted sheet to obtain the porous product.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein said sheet is shaped into a preform prior to drying and sintering.
Claim 4
Dependent Claim
13 words
The process of claim 1 wherein said first and second salts are identical.
Claim 5
Dependent Claim
34 words
The process of claim 1 wherein said first salt is a salt of relatively high solubility in the aqueous phase, and said second salt is a salt of lesser solubility in the aqueous phase.
Claim 6
Dependent Claim
27 words
The process of claim 1 wherein the temperature of the latex is maintained within a range of about 90° to 110° F. throughout steps (b) through (d).
Claim 7
Dependent Claim
16 words
The process of claim 1 wherein said mechanical working is accomplished by kneading the dough-like composition.
Claim 8
Dependent Claim
19 words
The process of claim 6 wherein said kneading is by passing the sheet through the nip of shaping rolls.
Claim 9
Dependent Claim
18 words
The process of claim 7 wherein the sheet is turned 90° on successive passes through the shaping rolls.
Claim 10
Dependent Claim
14 words
The process of claim 7 wherein the shaping rolls are maintained below 110° F.
Claim 11
Dependent Claim
24 words
The process of claim 1 wherein the mechanical working in step (e) is continued to reduce the moisture content of the mass to 10-12%.
Claim 12
Dependent Claim
59 words
The process of claim 1 wherein said mechanical working in step (e) is continued until the moisture content of the material has been reduced sufficiently to prevent the cohesion of two or more layers of said material when said layers are simultaneously passed between rollers thus enabling the ready separation of laminae of the rolled material into thinner sheets.
Claim 13
Dependent Claim
13 words
The process of claim 1 wherein said polymer latex is a PTFE latex.
Claim 14
Dependent Claim
55 words
The porous PTFE sheet produced by the process of claim 12 having an average pore size and pore volume to provide a Gurley air flow of 20-50 ml/min/sq. in. with a 20 oz. cylinder and a 1.0 inch square orifice, a tensile strength of 100-600 psi, an elongation of 50-250% and an open pore surface.
References Cited (Backward Citations)
US1142619A
Cited
US1710617A
Cited
US2175798A
Cited
US2542527A
Cited
US2504208A
Cited
US2707201A
Cited
US2983960A
Cited
US2846727A
Cited
US2997448A
Cited
US3062760A
Cited
US3556161A
Cited
US3376238A
Cited
US3281511A
Cited
US3253542A
Cited
US3496000A
Cited
GB1081046A
Cited
US3407249A
Cited
US3773878A
Cited
US3518332A
Cited
US3576686A
Cited
US3770537A
Cited
US3702267A
Cited
GB1364683A
Cited
US3763055A
Cited
US3930886A
Cited
US3890417A
Cited
GB1410313A
Cited
US4049589A
Cited
US3980613A
Cited
US3930979A
Cited
US3859402A
Cited
US3943006A
Cited
US4003818A
Cited
US3968292A
Cited
US4150076A
Cited
US4196070A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-16 | 1984-09-15 | 1985-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-16 | 1988-09-15 | 1989-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-16 | 1992-09-15 | 1993-03-17 | $7700.00 | Window Closed / Lapsed |