Assignee: RTX Corp
•
Filing: 1977-05-23
•
Granted: 1979-04-17
•
Expires: 1997-05-23
Abstract
Abstract A sheet material, principally comprised of a polymer such as polytetrafluoroethylene, having characteristics which permit its use in a fuel cell electrode is formed from co-agglomerates of the polymer and a pore former. In a fuel cell electrode application, the polymer-pore former agglomerates are themselves caused to co-agglomerate with a catalyst, the resulting co-agglomerates are formed into a layer and the pore former is leached from the layer so as to produce a structure having gas channels only in the polymer portions thereof. Agglomeration of the pore former and polymer particles is permitted through first imparting a positive charge to the pore former particles. The gas permeable catalyst layer will be bonded to a support plate to define a fuel cell electrode.
Inventors
- 👤 Johannes M. Baris
- 👤 Charles D. Iacovangelo
- 👤 Wolfgang M. Vogel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:48
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/8663; H01M4/8668; H01M4/88; H01M4/8803; H01M4/8807; H01M4/8875; H01M4/8878; H01M4/8882; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
196 words
A method for the manufacture of polymer sheet material characterized by gas porosity comprising the steps of: providing a dispersion comprising nonwettable thermoplastic halogenated hydrocarbon polymer particles having a predetermined average diameter; providing a pore former comprising a material which is capable of being attacked by an etchant which will not attack the polymer, the pore former being in the form of particles having an average diameter which is not greater than the average diameter of the polymer particles; suspending the pore former particles in a solution comprising metal salt; adjusting the pH of the solution to hydrolize the metal salt; forming a coating comprising said hydrolized metal salt on the pore former particles to provide coated pore former particles having an electrical charge which is opposite to the charge of the polymer particles; mixing said polymer dispersion and the pore former particles to provide agglomerated particles comprising the pore former particles and the polymer particles; forming a layer comprising the agglomerated particles, the pore former particles and the polymer particles uniformly distributed throughout the layer; and leaching the pore former particles from the layer to form gas channels therein, said layer being resistant to wetting.
Claim 2
Independent Claim
196 words
A method for the manufacture of polymer sheet material characterized by gas porosity comprising the steps of: providing a dispersion comprising nonwettable thermoplastic halogenated hydrocarbon polymer particles having a predetermined average diameter; providing a pore former comprising a material which is capable of being attacked by an etchant which will not attack the polymer, the pore former being in the form of particles having an average diameter which is not greater than the average diameter of the polymer particles; suspending the pore former particles in a solution comprising metal salt; adjusting the pH of the solution to hydrolize the metal salt; forming a coating comprising said hydrolized metal salt on the pore former particles to provide coated pore former particles having an electrical charge which is opposite to the charge of the polymer particles; mixing said polymer dispersion and the pore former particles to provide agglomerated particles comprising the pore former particles and the polymer particles; forming a layer comprising the agglomerated particles, the pore former particles and the polymer particles uniformly distributed throughout the layer; and leaching the pore former particles from the layer to form gas channels therein, said layer being resistant to wetting.
Claim 3
Dependent Claim
46 words
A method according to claim 1 wherein the step of forming said coating on the pore former particles comprises suspending the coated pore former particles in an acidic solution which attacks the hydrolized metal salt coating to provide coated pore former particles having a positive charge.
Claim 4
Dependent Claim
16 words
A method according to claim 2 wherein the polymer dispersion comprises an aqueous dispersion of polytetrafluoroethylene.
Claim 5
Dependent Claim
25 words
A method according to claim 3 wherein the solution of metal salt comprises Th(NO 3 ) 4 and the pore former particles comprise zinc oxide.
Claim 6
Dependent Claim
20 words
A method according to claim 4 wherein the pH is adjusted by adding sodium hydroxide to hydrolize the metal salt.
Claim 7
Dependent Claim
71 words
A method according to claim 5 wherein the coated pore former particles are removed from the solution and are washed to remove the sodium hydroxide and further including resuspending the coated pore former particles in solution and adjusting the pH of the solution with nitric acid to thereby attack the coating on the pore former particles and remove hydroxide so as to leave the pore former particles with a positive charge.
Claim 8
Dependent Claim
16 words
A method according to claim 6 wherein subsequent to forming the layer, the layer is sintered.
References Cited (Backward Citations)
US3556161A
Cited
US3282737A
Cited
US3281511A
Cited
US3627859A
Cited
US3778313A
Cited
US3773878A
Cited
US3518332A
Cited
US3632704A
Cited
US3661645A
Cited
US3702267A
Cited
US4044193A
Cited
US3930886A
Cited
US3890417A
Cited
US3980613A
Cited
US3930979A
Cited
US3943006A
Cited
US4031041A
Cited
US3979227A
Cited
US4043933A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-16 | 1982-10-16 | 1983-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-16 | 1986-10-16 | 1987-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-16 | 1990-10-16 | 1991-04-17 | $7700.00 | Window Closed / Lapsed |