US4170662A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plasma plating
Assignee: Eastman Kodak Co
•
Filing: 1978-01-23
•
Granted: 1979-10-09
•
Expires: 1998-01-23
Abstract
Abstract A method for forming on a substrate a relatively thick, densified, essentially non-porous, fine-grained layer of a non-conductive material. The method comprises the steps of vapor depositing onto such substrate a starting material while simultaneously bombarding the substrate with ions of a preselected gas. During the process, the substrate is disposed in the atmosphere of a preselected gas, and an RF field is established between the substrate and an opposing electrode structure to produce a plasma of such gas in the vicinity of the substrate. The substrate is electrically biased to attract ions from the plasma, such ions serving to impact on the substrate and thereby densify the vapor deposit thereon. Preferably, the starting material is one which reacts with the gas ions to form the desired material on the substrate; alternatively, the starting material comprises the desired material, in which case the gas plasma preferably comprises an inert gas.
Inventors
- 👤 Armin K. Weiss
- 👤 John R. Clarke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:58
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/32
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
121 words
A method for forming on the surface of a substrate a dense, photoconductive layer of stoichiometrically balanced lead oxide, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a gas comprising a mixture of oxygen and an inert gas; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; and (d) depositing on the substrate surface a vapor of lead oxide while the surface undergoes bombardment by said gas ions.
Claim 2
Independent Claim
121 words
A method for forming on the surface of a substrate a dense, photoconductive layer of stoichiometrically balanced lead oxide, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a gas comprising a mixture of oxygen and an inert gas; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; and (d) depositing on the substrate surface a vapor of lead oxide while the surface undergoes bombardment by said gas ions.
Claim 3
Independent Claim
121 words
A method for forming on the surface of a substrate a photoconductive layer of stoichiometrically balanced lead oxide, said method comprising the steps of: (a) disposing the substrate in an atmosphere of an oxygen-containing gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the oxygen gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged oxygen gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged oxygen gas ions to bombard the substrate surface; and (d) depositing on the substrate surface a vapor of substantially pure lead while the surface undergoes bombardment by said oxygen gas ions.
Claim 4
Independent Claim
121 words
A method for forming on the surface of a substrate a photoconductive layer of stoichiometrically balanced lead oxide, said method comprising the steps of: (a) disposing the substrate in an atmosphere of an oxygen-containing gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the oxygen gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged oxygen gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged oxygen gas ions to bombard the substrate surface; and (d) depositing on the substrate surface a vapor of substantially pure lead while the surface undergoes bombardment by said oxygen gas ions.
Claim 5
Independent Claim
147 words
A method for forming on the surface of a substrate a dense layer of a photoconductive material, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a preselected gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; (d) depositing on the substrate surface a vapor of the photoconductive material while the surface undergoes bombardment by the gas ions, whereby a dense layer of photoconductive material is formed; and (e) post-firing the layer deposited on the substrate surface in an inert gas environment to a temperature of at least 400° C.
Claim 6
Independent Claim
147 words
A method for forming on the surface of a substrate a dense layer of a photoconductive material, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a preselected gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; (d) depositing on the substrate surface a vapor of the photoconductive material while the surface undergoes bombardment by the gas ions, whereby a dense layer of photoconductive material is formed; and (e) post-firing the layer deposited on the substrate surface in an inert gas environment to a temperature of at least 400° C.
Claim 7
Independent Claim
146 words
A method for forming on the surface of a substrate a dense layer of a photoconductive material, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a preselected gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; (d) depositing on the substrate surface a vapor of the photoconductive material while the surface undergoes bombardment by the gas ions, whereby a dense layer of photoconductive material is formed; and (e) post-firing the layer deposited on the substrate surface in an oxygen-containing environment to a temperature of at least 300° C.
Claim 8
Independent Claim
146 words
A method for forming on the surface of a substrate a dense layer of a photoconductive material, said method comprising the steps of: (a) disposing the substrate in an atmosphere of a preselected gas at a predetermined pressure; (b) establishing an RF electric field in the vicinity of the substrate surface to produce a plasma of the gas in the vicinity of the substrate surface, such plasma comprising a mixture of positively charged gas ions and electrons; (c) electrically biasing the substrate to cause the positively charged gas ions to bombard the substrate surface; (d) depositing on the substrate surface a vapor of the photoconductive material while the surface undergoes bombardment by the gas ions, whereby a dense layer of photoconductive material is formed; and (e) post-firing the layer deposited on the substrate surface in an oxygen-containing environment to a temperature of at least 300° C.
Claim 9
Independent Claim
158 words
A method for forming on the surface of a substrate a layer of a photoconductive metal oxide, said method comprising the steps of: (a) disposing the substrate in the atmosphere of oxygen-containing gas at a predetermined pressure; (b) establishing an RF field in the vicinity of said surface to produce a plasma of said gas in the vicinity of said surface, such plasma comprising a mixture of positively charged oxygen ions and electrons; (c) electrically biasing the substrate to a negative potential to cause such positively charged oxygen ions to bombard said surface; (d) depositing on said surface a vapor containing molecules of the metal component of said metal oxide while the substrate undergoes bombardment by oxygen ions, said oxygen ions reacting with said metal molecules to form said photoconductive material on the substrate surface; and (e) post-firing the layer deposited on the substrate surface in an inert gas environment to a temperature of at least 400° C.
Claim 10
Independent Claim
158 words
A method for forming on the surface of a substrate a layer of a photoconductive metal oxide, said method comprising the steps of: (a) disposing the substrate in the atmosphere of oxygen-containing gas at a predetermined pressure; (b) establishing an RF field in the vicinity of said surface to produce a plasma of said gas in the vicinity of said surface, such plasma comprising a mixture of positively charged oxygen ions and electrons; (c) electrically biasing the substrate to a negative potential to cause such positively charged oxygen ions to bombard said surface; (d) depositing on said surface a vapor containing molecules of the metal component of said metal oxide while the substrate undergoes bombardment by oxygen ions, said oxygen ions reacting with said metal molecules to form said photoconductive material on the substrate surface; and (e) post-firing the layer deposited on the substrate surface in an inert gas environment to a temperature of at least 400° C.
Claim 11
Dependent Claim
36 words
The method according to claim 5 wherein the metal oxide is selected from the group consisting of the oxides of lead, antimony, bismuth, cadmium, tin and zinc, and the sulfides of antimony, bismuth, cadmium and zinc.
Claim 12
Independent Claim
157 words
A method for forming on the surface of a substrate a layer of a photoconductive metal oxide, said method comprising the steps of: (a) disposing the substrate in the atmosphere of oxygen-containing gas at a predetermined pressure; (b) establishing an RF field in the vicinity of said surface to produce a plasma of said gas in the vicinity of said surface, such plasma comprising a mixture of positively charged oxygen ions and electrons; (c) electrically biasing a substrate to a negative potential to cause such positively charged oxygen ions to bombard said surface; (d) depositing on said surface a vapor containing molecules of the metal component of said metal oxide while the substrate undergoes bombardment by oxygen ions, said oxygen ions reacting with said metal molecules to form said photoconductive material on the substrate surface; and (e) post-firing the layer deposited on the substrate surface in an oxygen-containing environment to a temperature of at least 300° C.
Claim 13
Independent Claim
157 words
A method for forming on the surface of a substrate a layer of a photoconductive metal oxide, said method comprising the steps of: (a) disposing the substrate in the atmosphere of oxygen-containing gas at a predetermined pressure; (b) establishing an RF field in the vicinity of said surface to produce a plasma of said gas in the vicinity of said surface, such plasma comprising a mixture of positively charged oxygen ions and electrons; (c) electrically biasing a substrate to a negative potential to cause such positively charged oxygen ions to bombard said surface; (d) depositing on said surface a vapor containing molecules of the metal component of said metal oxide while the substrate undergoes bombardment by oxygen ions, said oxygen ions reacting with said metal molecules to form said photoconductive material on the substrate surface; and (e) post-firing the layer deposited on the substrate surface in an oxygen-containing environment to a temperature of at least 300° C.
Claim 14
Dependent Claim
36 words
The method according to claim 7 wherein the metal oxide is selected from the group consisting of the oxides of lead, antimony, bismuth, cadmium, tin and zinc, and the sulfides of antimony, bismuth, cadmium and zinc.
References Cited (Backward Citations)
CA868514A
Cited
CA889981A
Cited
US3307983A
Cited
US3369991A
Cited
US3525680A
Cited
US3419487A
Cited
US3673071A
Cited
US3604970A
Cited
US3639151A
Cited
US4019902A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-08 | 1983-04-09 | 1983-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-08 | 1987-04-09 | 1987-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-08 | 1991-04-09 | 1991-10-09 | $7700.00 | Window Closed / Lapsed |