US4029631A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyester sheet containing antiblock agent added in degradable polycarbonate
Assignee: Honeywell International Inc
•
Filing: 1976-11-03
•
Granted: 1977-06-14
•
Expires: 1996-11-03
Abstract
Abstract A polyester sheet containing an antiblock agent is produced by uniformly blending a small amount of a degraded polycarbonate containing the antiblock agent. The antiblock agent must have an inherent or adjusted pH of less than six to degrade the polycarbonate to lower its molecular weight upon extrusion compounding. This in turn makes a uniform blend and resulting clear sheet with antiblocking properties. In another embodiment, larger amounts of polycarbonate containing the antiblock agent are used.
Inventors
- 👤 Philip Stuart Bollen
- 👤 Eugene Vincent Walacavage
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:26
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/36; C08L; C08L67/00; C08L67/02; C08L69/00
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
239 words
A method of adding an antiblock agent to polyethylene terephthalate, said polyethylene terephthalate having an intrinsic viscosity greater than 0.9, a melt viscosity at 525° F. of above about 10,000 poise, and used to form a sheet, consisting of a. compounding from about 0.25 to 0.01 percent by weight, based on the final total weight of all components, of said antiblock agent, said antiblock agent having a pH of less than 6, with from about 2.5 to 0.1 percent by weight, based on the final total weight of all components, of a degradable polycarbonate, said polycarbonate having an intrinsic viscosity of from about 0.55 to 0.7, before it is compounded, then b. uniformly blending said polyethylene terephthalate and said polycarbonate to make a composition of said polyethylene terephthalate and said polycarbonate containing said antiblock agent, then c. extruding said blended polyethylene terephthalate and polycarbonate containing antiblock agent at about 490° to 530° F. to form a sheet; and finally d. rapidly cooling the resulting extruded sheet with at least one cooling surface maintained at a surface temperature of from about 50° to about 160° F. for a period not exceeding about 15 seconds, said sheet being essentially amorphous and nonoriented, so that said antiblock agent degrades said polycarbonate due to heat and acid hydrolysis during compounding of said antiblock agent with said polycarbonate, whereby said blend of polyethylene terephthalate and polycarbonate is uniform and said extruded sheet is clear.
Claim 2
Independent Claim
239 words
A method of adding an antiblock agent to polyethylene terephthalate, said polyethylene terephthalate having an intrinsic viscosity greater than 0.9, a melt viscosity at 525° F. of above about 10,000 poise, and used to form a sheet, consisting of a. compounding from about 0.25 to 0.01 percent by weight, based on the final total weight of all components, of said antiblock agent, said antiblock agent having a pH of less than 6, with from about 2.5 to 0.1 percent by weight, based on the final total weight of all components, of a degradable polycarbonate, said polycarbonate having an intrinsic viscosity of from about 0.55 to 0.7, before it is compounded, then b. uniformly blending said polyethylene terephthalate and said polycarbonate to make a composition of said polyethylene terephthalate and said polycarbonate containing said antiblock agent, then c. extruding said blended polyethylene terephthalate and polycarbonate containing antiblock agent at about 490° to 530° F. to form a sheet; and finally d. rapidly cooling the resulting extruded sheet with at least one cooling surface maintained at a surface temperature of from about 50° to about 160° F. for a period not exceeding about 15 seconds, said sheet being essentially amorphous and nonoriented, so that said antiblock agent degrades said polycarbonate due to heat and acid hydrolysis during compounding of said antiblock agent with said polycarbonate, whereby said blend of polyethylene terephthalate and polycarbonate is uniform and said extruded sheet is clear.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein said polycarbonate is added in an amount of from about 40 to 0.1 percent by weight based on the final total weight of all components.
Claim 4
Dependent Claim
30 words
The method of claim 1 wherein the pH of said antiblock agent is adjusted to below 6 prior to being added to said polycarbonate, and said compounding is extrusion compounding.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said antiblock agent inherently has a pH lower than 6, and said compounding is extrusion compounding.
Claim 6
Dependent Claim
35 words
The method of claim 4 wherein said antiblock agent is an amorphous silica prepared by the hydrolysis of silicon tetrachloride, and said polycarbonate has an intrinsic viscosity of about 0.5 or less after said compounding.
Claim 7
Dependent Claim
20 words
The method of claim 5 wherein the particle size of said silica is between about 2 to about 6 microns.
Claim 8
Dependent Claim
17 words
The method of claim 6 wherein the average particle size of said silica is about 4 microns.
Claim 9
Dependent Claim
28 words
The method of claim 6 wherein said sheet has a haze value of less than about 5 percent and a block value of less than about 10 pounds.
Claim 10
Dependent Claim
15 words
The method of claim 1 wherein said contact time is less than about 10 seconds.
Claim 11
Dependent Claim
40 words
The method of claim 1 wherein said polyethylene terephthalate has an intrinsic viscosity of from about 0.9 to 1.2 and a melt viscosity at 525° F. of from about 10,000 to 50,000 poises, and said polycarbonate is poly(4,4'isopropylidene diphenylene carbonate).
Claim 12
Dependent Claim
26 words
The method of claim 1 wherein said blended composition is dried to a water content of less than about 0.02 percent by weight prior to extrusion.
Claim 13
Dependent Claim
35 words
The method of claim 1 wherein said composition is extruded onto at least two rotating cooling rolls maintained at a surface temperature of about 80° to 120° F. and rotating at substantially the same speed.
Claim 14
Dependent Claim
19 words
The method of claim 12 wherein a pair of internally cooled chill rolls are employed to cool said sheet.
Claim 15
Dependent Claim
18 words
The method of claim 12 wherein a stack of three chill rolls is employed to cool said sheet.
Claim 16
Dependent Claim
19 words
The method of claim 1 wherein said contact time is in the range of about 0.04 to 10 seconds.
Claim 17
Dependent Claim
34 words
The method of forming a container suitable for use in filling of heated foods which comprises thermoforming the sheet of claim 1 at a temperature of about 210° to 280° F. into said container.
Claim 18
Dependent Claim
148 words
A sheet containing an antiblock agent suitable to be formed and filled with meats, pharmaceuticals or heated foods and the like, said sheet being essentially amorphous and non-oriented, consisting of from about 97.25 percent to 99.89 percent by weight of polyethylene terephthalate having an intrinsic viscosity of above about 0.9 and a melt viscosity at 525° F. of above about 10,000 poises, 2.5 to 0.1 percent by weight of a polycarbonate resin having an intrinsic viscosity of about 0.55 to 0.7, before compounding with said antiblock agent, 0.25 to 0.01 percent by weight of an antiblock agent having a pH of below 6 before compounding, said sheet resulting from the extrusion of a uniform mixture of said polyethylene terephthalate and said polycarbonate, said antiblock agent being initially present in only said polycarbonate before addition to said polyethylene terephthalate, and said antiblock agent degrading said polycarbonate upon compounding therewith.
Claim 19
Dependent Claim
148 words
A sheet containing an antiblock agent suitable to be formed and filled with meats, pharmaceuticals or heated foods and the like, said sheet being essentially amorphous and non-oriented, consisting of from about 97.25 percent to 99.89 percent by weight of polyethylene terephthalate having an intrinsic viscosity of above about 0.9 and a melt viscosity at 525° F. of above about 10,000 poises, 2.5 to 0.1 percent by weight of a polycarbonate resin having an intrinsic viscosity of about 0.55 to 0.7, before compounding with said antiblock agent, 0.25 to 0.01 percent by weight of an antiblock agent having a pH of below 6 before compounding, said sheet resulting from the extrusion of a uniform mixture of said polyethylene terephthalate and said polycarbonate, said antiblock agent being initially present in only said polycarbonate before addition to said polyethylene terephthalate, and said antiblock agent degrading said polycarbonate upon compounding therewith.
Claim 20
Dependent Claim
39 words
The sheet of claim 17 wherein said polyethylene terephthalate is present in an amount from about 60 to 99.89 percent by weight, and said polycarbonate resin is present in an amount from about 39.75 to 0.1 percent by weight.
Claim 21
Dependent Claim
19 words
The sheet of claim 17 wherein said antiblock agent is amorphous silica prepared by the hydrolysis of silicon tetrachloride.
Claim 22
Dependent Claim
18 words
The sheet of claim 19 wherein the particle size of said silica is about 2 to 6 microns.
Claim 23
Dependent Claim
14 words
The sheet of claim 20 wherein the average particle size is about 4 microns.
Claim 24
Dependent Claim
13 words
The sheet of claim 17 wherein said polycarbonate is poly(4,4'- isopropylidene diphenylene carbonate).
Claim 25
Dependent Claim
32 words
The sheet of claim 17 wherein said polyethylene terephthalate has an intrinsic viscosity of about 0.9 to 1.2 and a melt viscosity at 525° F. of from about 10,000 to 50,000 poises.
Claim 26
Dependent Claim
30 words
The sheet of claim 17 wherein said polycarbonate has an intrinsic viscosity of from about 0.55 to about 0.7, before extrusion compounding, and less than about 0.5 after the compounding.
Claim 27
Dependent Claim
9 words
The container thermoformed from the sheet of claim 17.
Claim 28
Dependent Claim
22 words
The container of claim 25 having a haze value less than 5 percent and a block value of less than 10 pounds.
Claim 29
Dependent Claim
92 words
In a method for preparing a masterbatch of polycarbonate containing silica for subsequent addition to polyethylene terephthalate comprising mixing said silica with said polycarbonate, the improvement consisting of uniformly compounding from about 5 to 50 percent by weight of said silica having a pH of less than 6 and a particle size of from about 2 to 6 microns with from about 95 to 50 percent by weight of said polycarbonate having an intrinsic viscosity of from about 0.55 to 0.7, before compounding, so that said polycarbonate is degraded during said compounding.
Claim 30
Dependent Claim
92 words
In a method for preparing a masterbatch of polycarbonate containing silica for subsequent addition to polyethylene terephthalate comprising mixing said silica with said polycarbonate, the improvement consisting of uniformly compounding from about 5 to 50 percent by weight of said silica having a pH of less than 6 and a particle size of from about 2 to 6 microns with from about 95 to 50 percent by weight of said polycarbonate having an intrinsic viscosity of from about 0.55 to 0.7, before compounding, so that said polycarbonate is degraded during said compounding.
Claim 31
Dependent Claim
30 words
The method of claim 27 wherein from about 10 to about 20 percent by weight of silica is added to from about 90 to 80 percent by weight of polycarbonate.
Claim 32
Dependent Claim
25 words
The method of claim 28 wherein said silica is an amorphous silica prepared by the hydrolysis of silicon tetrachloride, and said compounding is extrusion compounding.
Claim 33
Dependent Claim
14 words
The method of claim 29 wherein said silica has a pH of about 5.
Claim 34
Dependent Claim
21 words
The method of claim 27 wherein the intrinsic viscosity of said polycarbonate after said compounding is from about 0.4 to 0.5.
References Cited (Backward Citations)
US3218372A
Cited
US3426100A
Cited
US3720732A
Cited
US3956229A
Cited
US3975485A
Cited
US3975355A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |