Dispersion-polymerization process using block copolymers
Assignee: Bpifrance Financement SA
•
Filing: 1975-05-02
•
Granted: 1977-05-31
•
Expires: 1995-05-02
Abstract
Abstract There is disclosed a process of dispersion-polymerizing vinyl monomers promoted by free-radical catalysts. This process comprises dispersing under stirring in water a block copolymer of the A-B type wherein A represents a lipophilic block and B a hydrophilic block, adding one or more vinyl monomers containing the promoter and heating the mixture with stirring to the desired temperature. This process enables beads or balls of the desired polymer to be obtained having very regular size distribution.
Inventors
- 👤 Morand Lambla
- 👤 Jean Terrisse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 07:36
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/22; C08F2/24; C08F287/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
180 words
A process for the free-radical polymerization of vinyl monomers, suspended in water, comprising the steps of: dispersing a block copolymer of the A-B type selected from the group consisting of: polystyrene-quaternized poly(vinyl-2-pyridine), polystyrene-quaternized poly(vinyl-3-pyridine), polystyrene-quaternized poly(methyl-2 vinyl-5 pyridine), polystyrene-anhydrated and hydrolyzed or salified polyisoprene, polystyrene-quaternized amidated polyisoprene, polystyrene-poly(dimethylaminoethyl methacrylate) polystyrene-quaternized poly(dimethylaminoethylmethacrylate), polystyrene-hydrolyzed and/or salified poly(trimethylsilyl methacrylate), polyisoprene-quaternized poly(vinyl-2-pyridine), polyisoprene-quaternized poly(vinyl-4-pyridine), poly(hexyl methacrylate)-poly(dimethylaminoethyl)methacrylate, poly(heptyl methacrylate)-poly(dimethylaminoethyl methacrylate), polydimethylsiloxane-quaternized poly(vinyl-2-pyridine), polydimethylsiloxane-quaternized poly(vinyl-4-pyridine), polydimethylsiloxane-poly(dimethylaminoethyl methacrylate), polydimethylsiloxane anhydrated, and hydrolyzed or hydrolysed and salified anhydrated polyisoprene, poly(vinyl chloride), hydrolyzed or hydrolysed and salified poly(vinyl acetate), polystyrene-polyacrylamide, polystyrene-polymethacrylamide, polystyrene-poly(acrylic acid) salified or not, polystyrene-polyvinylpyrrolidone, polystyrene-poly(styrene sulfonic acid), wherein A represents a lipophilic polymer block and B represents blocks A and B of said block copolymer are present in a respective molecular weight ratio of about 0.1 to 10; adding at least one vinyl monomer to be polymerized and containing a polymerization promoter to said dispersion, wherein the amount of block copolymer ranges from 0.05-5.0 parts by weight per thousand parts by weight of vinyl monomer; and heating the mixture with stirring to the desired polymerization temperature.
Claim 2
Dependent Claim
180 words
A process for the free-radical polymerization of vinyl monomers, suspended in water, comprising the steps of: dispersing a block copolymer of the A-B type selected from the group consisting of: polystyrene-quaternized poly(vinyl-2-pyridine), polystyrene-quaternized poly(vinyl-3-pyridine), polystyrene-quaternized poly(methyl-2 vinyl-5 pyridine), polystyrene-anhydrated and hydrolyzed or salified polyisoprene, polystyrene-quaternized amidated polyisoprene, polystyrene-poly(dimethylaminoethyl methacrylate) polystyrene-quaternized poly(dimethylaminoethylmethacrylate), polystyrene-hydrolyzed and/or salified poly(trimethylsilyl methacrylate), polyisoprene-quaternized poly(vinyl-2-pyridine), polyisoprene-quaternized poly(vinyl-4-pyridine), poly(hexyl methacrylate)-poly(dimethylaminoethyl)methacrylate, poly(heptyl methacrylate)-poly(dimethylaminoethyl methacrylate), polydimethylsiloxane-quaternized poly(vinyl-2-pyridine), polydimethylsiloxane-quaternized poly(vinyl-4-pyridine), polydimethylsiloxane-poly(dimethylaminoethyl methacrylate), polydimethylsiloxane anhydrated, and hydrolyzed or hydrolysed and salified anhydrated polyisoprene, poly(vinyl chloride), hydrolyzed or hydrolysed and salified poly(vinyl acetate), polystyrene-polyacrylamide, polystyrene-polymethacrylamide, polystyrene-poly(acrylic acid) salified or not, polystyrene-polyvinylpyrrolidone, polystyrene-poly(styrene sulfonic acid), wherein A represents a lipophilic polymer block and B represents blocks A and B of said block copolymer are present in a respective molecular weight ratio of about 0.1 to 10; adding at least one vinyl monomer to be polymerized and containing a polymerization promoter to said dispersion, wherein the amount of block copolymer ranges from 0.05-5.0 parts by weight per thousand parts by weight of vinyl monomer; and heating the mixture with stirring to the desired polymerization temperature.
Claim 3
Dependent Claim
53 words
The process of claim 1, wherein said block copolymer is: polystyrene-quaternized poly(vinyl-2-pyridine), polystyrene-quaternized poly(vinyl-4-pyridine), polystyrene-quaternized poly(methyl-2 vinyl-5 pyridine), polystyrene-anhydrated and hydrolyzed or salified polyisoprene, polystyrene-quaternized amidated polyisoprene, polystyrene-poly(dimethylaminoethyl methacrylate), polystyrene-quaternized poly(dimethylaminoethylmethacrylate), polystyrene-hydrolyzed and/or salified poly(trimethylsilyl methacrylate), poly(hexyl methacrylate)-poly(dimethylaminoethyl)methacrylate, poly(heptyl methacrylate)-poly(dimethylaminoethyl methacrylate), polystyrene-polyacrylamide, polystyrene-polymethylacrylamide, polystyrene-poly(acrylic acid) salified or not, polystyrene-polyvinylpyrrolidone, or polystyrene-poly(styrene sulfonic acid).
Claim 4
Dependent Claim
15 words
The process of claim 1, wherein said block copolymer is polyisoprene-quaternized poly(vinyl-2-pyridine) or polyisoprene-quaternized poly(vinyl-4-pyridine).
Claim 5
Dependent Claim
35 words
The process of claim 1, wherein said block copolymer is: polydimethylsiloxane-quaternized poly(vinyl-2-pyridine), polydimethylsiloxane-quaternized poly(vinyl-4-pyridine), polydimethylsiloxane-poly(dimethylaminoethyl methacrylate), polydimethylsiloxane anhydrated, and hydrolyzed or hydrolysed and salified anhydrated polyisoprene, poly(vinyl chloride), hydrolyzed or hydrolysed and salified poly(vinyl acetate).
Claim 6
Dependent Claim
35 words
The process according to claim 1, wherein the vinyl monomers are selected from the group consisting of substituted or non-substituted styrene, alkyl acrylates and methacrylates, vinyl acetate, acrylonitrile, vinyl chloride and other halogenated vinyl compounds.
Claim 7
Dependent Claim
37 words
The process according to claim 1, wherein the polymer forming the block B of the copolymer A-B is quaternized by means of an amount of a quaternizing agent corresponding to 1 to 10 times the stoichiometrical proportion.
Claim 8
Dependent Claim
25 words
The process according to claim 1, wherein block A of copolymer A-B represents 10 to 50% by weight of the total weight of said copolymer.
Claim 9
Dependent Claim
25 words
The process according to claim 1, wherein blocks A and B of block copolymer A-B have each number molecular weights between about 1000 and 200,000.
Claim 10
Dependent Claim
27 words
The process according to claim 1, wherein the polymerization is effected at a temperature of 0° C. to 150° C. under pressure of 1 to 20 bars.
Claim 11
Dependent Claim
31 words
The product comprizing beads or balls of vinyl polymer when prepared by the process of claim 1, said product being transparent and substantially free of materials extraneous to the base monomers.
References Cited (Backward Citations)
US3317635A
Cited
US3264234A
Cited
US3189665A
Cited
US3189663A
Cited
US3189664A
Cited
US3382297A
Cited
US3514500A
Cited
US3691257A
Cited
US3673272A
Cited
US3875254A
Cited
US3686356A
Cited
US3888945A
Cited
US3917741A
Cited
US3903201A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |