Process for producing platelet α-Al2 O3 based ceramic composite

Claim 2

A process for producing platelet α-Al 2 O 3 based ceramic composite, which comprises: blending Al 2 O 3 powder with from 0.02 to 4 weight percent of a first additive for promoting platelet formation in α-Al 2 O 3 grains, wherein said first additive is at least one oxide of a member selected from the group, consisting of Li, K, Na, Ca, Sr, Si, and Ba; adding from 5 to 40 weight percent of a second additive for controlling grain growth of said α-Al 2 O 3 platelets, wherein said second additive is at least one member selected from the group consisting of ZrO 2 HfO 2 , SiC whiskers, SiC particles and carbides, nitrides or carbonitrides of IVa, Va or VIa metals; said Al 2 O 3 , said first additive and said second additive forming a mixture; and sintering said mixture to produce said platelet α-Al 2 O 3 based ceramic composite.

Claim 3

A process as in claim 1, wherein said sintering is carried out at a temperature ranging from about 1300° C. to about 1900° C.

Claim 4

The process according to claim 1, wherein: said first additive ranges from about 0.02 to about 2 weight percent of said α-Al 2 O 3 mixture.

Claim 5

The process according to claim 1, wherein said second additive is at least one member selected from the group consisting of partially stabilized ZrO 2 , and partially stabilized HfO 2 ; and said partially stabilized HfO 2 and ZrO 2 further include a solid solution containing at least one member selected from the group consisting of Y 2 O 3 , MgO, CaO, and CeO 2 .

Claim 6

A process for producing platelet α-Al 2 O 3 based ceramic composite, comprising: blending Al 2 O 3 powder with from 0.02 to 4 weight percent of a first additive for promoting platelet formation in α-Al 2 O 3 grains and from 5 to 40 weight percent of a second additive for controlling grain growth of said α-Al 2 O 3 selected from the group consisting of ZrO 2 , HfO 2 , SiC whickers, SiC particles and carbides, nitrides or carbonitrides of IVa, Va and VIa metals, to form a raw powder composition; said first additive is selected from the group consisting of salts of alkali metals, salts of alkaline earth metals which upon heating decompose into oxides, SiO 2 and a compound which produces SiO 2 ; heat treating a portion said raw powder composition at a temperature 1000° C. to about 1500° C., to produce a liquid phase component; grinding said liquid phase component to produce a liquid phase powder; mixing the remainder of said raw powder composition and said liquid phase powder forming a powder shape; and sintering said powder shape to produce platelet α-Al 2 O 3 based ceramic composite.

Claim 7

A process for producing platelet α-Al 2 O 3 based ceramic composite, comprising: blending Al 2 O 3 powder with from 0.02 to 4 weight percent of a first additive for promoting platelet formation in α-Al 2 O 3 grains and from 5 to 40 weight percent of a second additive for controlling grain growth of said α-Al 2 O 3 selected from the group consisting of ZrO 2 , HfO 2 , SiC whickers, SiC particles and carbides, nitrides or carbonitrides of IVa, Va and VIa metals, to form a raw powder composition; said first additive is selected from the group consisting of salts of alkali metals, salts of alkaline earth metals which upon heating decompose into oxides, SiO 2 and a compound which produces SiO 2 ; heat treating a portion said raw powder composition at a temperature 1000° C. to about 1500° C., to produce a liquid phase component; grinding said liquid phase component to produce a liquid phase powder; mixing the remainder of said raw powder composition and said liquid phase powder forming a powder shape; and sintering said powder shape to produce platelet α-Al 2 O 3 based ceramic composite.

Claim 8

The process according to claim 5, wherein the step of heat treating is carried out at a temperature ranging from about 1000° C. to about 1,050° C.

Claim 9

The process according to claim 5, wherein said sintering is carried out at a temperature ranging from about 1300° C. to about 1900° C.

Claim 10

The process according to claim 5, wherein said salts of alkali metals are chlorides, carbonates, nitrates, sulfates or oxylates of at least one selected from the group consisting of Li, K and Na.

Claim 11

The process according to claim 5, wherein said salts of alkaline earth metals are chlorides, carbonates, nitrates, sulfates or oxylates of at least one selected from the group consisting of Ca, Sr and Ba.

Claim 12

The process according to claim 5, wherein said first additive is Si alkoxide, which upon heating decomposes to produce SiO 2 .

Claim 13

The process according to claim 5, wherein said Al 2 O 3 powder has an average particles size of about 0.3 μm.

Claim 14

The process according to claim 5, wherein said first additive has an average particles size of from 0.1 to 5 μm.

Claim 15

A platelet α-Al 2 O 3 based ceramic composite according to claim 1, wherein said α-Al 2 O 3 based ceramic composite comprises grains having a longer diameter of up to 15 μm.

Claim 16

A platelet α-Al 2 O 3 based ceramic composite according to claim 5, wherein said α-Al 2 O 3 based ceramic composite comprises grains having a longer diameter of up to 15 μm.