US5571567A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dip molded polyurethane film methods
Assignee: Polyzen Inc
•
Filing: 1995-06-07
•
Granted: 1996-11-05
•
Expires: 2015-06-07
Abstract
Abstract Dip molding of thermoplastic polyurethane elastomers to form medical and surgical gloves, condoms, instrument and appliance covers, and other rubber goods is improved by a controlled viscosity, controlled rate of evaporation solvent system, including a strong polar solvent, a weak solvent or non-solvent to control viscosity, and a blush resistor to control the rate of evaporation and the effects of humidity. For particularly enhanced barrier film formation, a leveling agent is also included. One or more layers are dipped in sequential steps in thicknesses of 0.5 to 1.5 mils per layer, with complete integral film formation and substantially complete freedom from porosity and pin holes. Cross-linkable polyurethanes may be cured after fully molded.
Inventors
- 👤 Tilak M. Shah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:17
CPC Classifications
C; C08; C08L; C08L75/00; C08L75/04; A; A61; A61F; A61F6/00; A61F6/02; A61F6/04; A61B; A61B42/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
256 words
The method of dip molding polyurethane elastomers comprising: A. forming a dipping solution comprising: i. a polyurethane elastomer; ii. a first solvent component which is at least one strong solvent for said polyurethane elastomer; iii. a second solvent component which is at least one non-solvent or non-polar or low polarity weak solvent for said polyurethane elastomer, whereto said second solvent component is freely miscible with said first solvent component; iv. a third solvent component which is at least one blush resistor which limits the rate of evaporation of said first solvent component and said second solvent component and which limits the absorption of water vapor into said composition; v. wherein said polyurethane is homogeneously dissolved in said solvent to form a solution having a viscosity in the range of from about 400 to about 800 cP; B. dipping a shaped form into said solution to wet the surface of said form; C. withdrawing said form from said solution to deposit a coating of said solution on the surface thereof, said coating having a thickness of from about 0.5 to 1.5 mils; D. drying said coating to form a continuous, non-porous solid polyurethane elastomer film having a thickness of from about 0.5 to about 1.5 mils on the surface of said form; E. repeating steps B, C, and D at least one additional time the continuous, non-porous solid polyurethane elastomer film has at least two of said thicknesses; F. stripping from said form said continuous, non-porous solid polyurethane elastomer film conforming to the shape of said form.
Claim 2
Independent Claim
256 words
The method of dip molding polyurethane elastomers comprising: A. forming a dipping solution comprising: i. a polyurethane elastomer; ii. a first solvent component which is at least one strong solvent for said polyurethane elastomer; iii. a second solvent component which is at least one non-solvent or non-polar or low polarity weak solvent for said polyurethane elastomer, whereto said second solvent component is freely miscible with said first solvent component; iv. a third solvent component which is at least one blush resistor which limits the rate of evaporation of said first solvent component and said second solvent component and which limits the absorption of water vapor into said composition; v. wherein said polyurethane is homogeneously dissolved in said solvent to form a solution having a viscosity in the range of from about 400 to about 800 cP; B. dipping a shaped form into said solution to wet the surface of said form; C. withdrawing said form from said solution to deposit a coating of said solution on the surface thereof, said coating having a thickness of from about 0.5 to 1.5 mils; D. drying said coating to form a continuous, non-porous solid polyurethane elastomer film having a thickness of from about 0.5 to about 1.5 mils on the surface of said form; E. repeating steps B, C, and D at least one additional time the continuous, non-porous solid polyurethane elastomer film has at least two of said thicknesses; F. stripping from said form said continuous, non-porous solid polyurethane elastomer film conforming to the shape of said form.
Claim 3
Dependent Claim
37 words
The polyurethane elastomer dip molding method of claim 1 wherein said first solvent component is a member selected from the group consisting of tetrahydrofuran, N-methylpyrrolidone, dimethyl acetamide, dimethyl formamide, methyl ethyl ketone, methylene chloride and mixtures thereof.
Claim 4
Dependent Claim
40 words
The polyurethane elastomer dip molding method of claim 1 wherein said second solvent component is a member selected from the group consisting of non-polar aliphatic and aromatic hydrocarbons having solubility parameters less than about 4.3, or greater than about 5.3.
Claim 5
Dependent Claim
28 words
The polyurethane elastomer dip molding polyurethane elastomer composition of claim 3 wherein said second solvent component solubility parameter is less than about 4.0 or greater than about 5.5.
Claim 6
Dependent Claim
16 words
The polyurethane elastomer dip molding method of claim 1 wherein said second solvent component is n-butanol.
Claim 7
Dependent Claim
42 words
The polyurethane elastomer dip molding method of claim 1 wherein said third solvent component is a member selected from the group consisting of glycol ethers and esters and mixtures thereof having a boiling point of about 20° C. to about 225° C.
Claim 8
Dependent Claim
25 words
The polyurethane elastomer dip molding method of claim 6 wherein said third solvent component has a boiling point of about 100° C. to 200° C.
Claim 9
Dependent Claim
27 words
The polyurethane elastomer dip molding method of claim 1 further comprising a leveling agent of poly (dimethyl-siloxane) with a molecular weight of about 250 to about 1,000.
Claim 10
Dependent Claim
36 words
The polyurethane elastomer dip molding method of claim 1 wherein said polyurethane elastomer is dissolved in said solvent system in an amount of from about 6 to 12 percent by weight of the dip molding solution.
Claim 11
Dependent Claim
36 words
The polyurethane elastomer dip molding method of claim 1 wherein said polyurethane elastomer is dissolved in said solvent system in an amount of from about 8 to 10 percent by weight of the dip molding solution.
References Cited (Backward Citations)
US3896753A
Cited
US3668173A
Cited
US4301053A
Cited
US4431763A
Cited
US4558075A
Cited
US4543405A
Cited
US4853418A
Cited
US5254619A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-11-05 | 2000-05-06 | 2000-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-11-05 | 2004-05-06 | 2004-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-11-05 | 2008-05-06 | 2008-11-05 | $7700.00 | Window Closed / Lapsed |