US5522898A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dehydration of hydrogels
Assignee: Howmedica Osteonics Corp
•
Filing: 1993-09-16
•
Granted: 1996-06-04
•
Expires: 2013-09-16
Abstract
Abstract Novel prosthetic nuclear implants for insertion into vertebral discs are prepared by dehydrating hydrated bulky hydrogel discs under specific conditions so as to reduce the water content as low as possible (down to about 10% by weight) but without distortion of the implants, without the formation of concavities and sharp edges, and without changing the shape of the hydrated implant.
Inventors
- 👤 Qi-Bin Bao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 08:02
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/44; A61F2/441; A61F2/442; A61F2002/30001; A61F2002/30108; A61F2002/3011; A61F2002/30112; A61F2002/30133; A61F2002/30316; A61F2002/30535; A61F2002/30581; A61F2002/444; A61F2230/00; A61F2230/0002; A61F2230/0004; A61F2230/0015; C08J2329/00; C08J2329/02; C08J2329/04; Y; Y10; Y10S; Y10S264/00; Y10S264/90; Y10S264/901
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
89 words
A method of dehydrating a bulky hydrogel nuclear vertebral implant having a weight before dehydration between about 3 and about 10 grams and having a shape substantially similar to a human vertebral disc nucleus and having a water content before dehydration between about 30 and about 60% by weight, said method comprising: dehydrating said implant at (a) a relative humidity of at least about 80%, (b) at a drying temperature between about 10° and about 40° C., and (c) for a time of drying of more than two days.
Claim 2
Independent Claim
89 words
A method of dehydrating a bulky hydrogel nuclear vertebral implant having a weight before dehydration between about 3 and about 10 grams and having a shape substantially similar to a human vertebral disc nucleus and having a water content before dehydration between about 30 and about 60% by weight, said method comprising: dehydrating said implant at (a) a relative humidity of at least about 80%, (b) at a drying temperature between about 10° and about 40° C., and (c) for a time of drying of more than two days.
Claim 3
Dependent Claim
70 words
A method according to claim 1, wherein said implant weighs about 5 grams before dehydration, is made of bulky hydrogel material comprising highly hydrolyzed polyvinyl alcohol and said hydrogel exhibiting a compressive strength of at least 4 MNm -2 , wherein said relative humidity is within a range from about 90 to about 99% and wherein said drying temperature is within a range from about 20° to about 35° C.
Claim 4
Dependent Claim
25 words
A method according to claim 2, wherein said relative humidity is at least about 95% and wherein said dehydration takes place within a humidity chamber.
Claim 5
Independent Claim
144 words
A method of dehydration of a hydrated bulky hydrogel implant having an original shape, said hydrogel being highly hydrolyzed polyvinyl alcohol, so as to maintain said original shape of said hydrated implant, said method comprising: dehydrating said implant when the water content of said implant is within a range from about 30 to about 60 percent by weight under controlled conditions of relative humidity and temperature and time, wherein said relative humidity is at least about 80%, said drying temperature is within a range from about 10° to about 40° C., and said time of drying is at least two days and sufficient to enable said implant to be dried without distortion to a water content below about 30%, and said implant weighing between about 3 and about 10 grams and having a shape which is substantially similar to a human vertebral disc nucleus.
Claim 6
Independent Claim
144 words
A method of dehydration of a hydrated bulky hydrogel implant having an original shape, said hydrogel being highly hydrolyzed polyvinyl alcohol, so as to maintain said original shape of said hydrated implant, said method comprising: dehydrating said implant when the water content of said implant is within a range from about 30 to about 60 percent by weight under controlled conditions of relative humidity and temperature and time, wherein said relative humidity is at least about 80%, said drying temperature is within a range from about 10° to about 40° C., and said time of drying is at least two days and sufficient to enable said implant to be dried without distortion to a water content below about 30%, and said implant weighing between about 3 and about 10 grams and having a shape which is substantially similar to a human vertebral disc nucleus.
Claim 7
Dependent Claim
36 words
A method according to claim 4, wherein said drying temperature is within a range from about 20° to about 35° C. and wherein said relative humidity is within a range from about 90 to about 99%.
Claim 8
Dependent Claim
25 words
A method according to claim 5, wherein said relative humidity is at least 95% and wherein said time of drying is at least several days.
Claim 9
Independent Claim
104 words
A method of producing a synthetic vertebral disc implant comprising highly hydrolyzed polyvinyl alcohol having a water content below about 30 weight percent and exhibiting (when viewed with no additional magnification beyond a naked eye) no visible distortion and no sharp edges, and having a minimum dehydrated volume, said method comprising: when said implant has a water content between about 30 to about 60 percent by weight, dehydrating said implant at a relative humidity of at least about 80%, at a drying temperature within a range from about 10° to about 40° C., and for a drying time which is at least two days.
Claim 10
Independent Claim
104 words
A method of producing a synthetic vertebral disc implant comprising highly hydrolyzed polyvinyl alcohol having a water content below about 30 weight percent and exhibiting (when viewed with no additional magnification beyond a naked eye) no visible distortion and no sharp edges, and having a minimum dehydrated volume, said method comprising: when said implant has a water content between about 30 to about 60 percent by weight, dehydrating said implant at a relative humidity of at least about 80%, at a drying temperature within a range from about 10° to about 40° C., and for a drying time which is at least two days.
Claim 11
Dependent Claim
84 words
A method according to claim 7, wherein said implant comprises highly hydrolyzed polyvinyl alcohol having a compressive strength of at least 4 MNm -2 , wherein said implant has a size within a range from about 3 to about 10 grams, and a shape which is substantially similar to a human vertebral disc nucleus wherein said relative humidity is within a range from about 90 to about 99%, and wherein said drying temperature is within a range from about 20° to about 35° C.
Claim 12
Dependent Claim
31 words
A method according to claim 8, wherein said implant weighs about 5 grams before dehydration, wherein said relative humidity is at least about 95%, and wherein said bulky hydrogel is PVA.
References Cited (Backward Citations)
US3234659A
Cited
US3760045A
Cited
US4808353A
Cited
US4663358A
Cited
US5012503A
Cited
US5047055A
Cited
US5314478A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-06-04 | 1999-12-04 | 2000-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-06-04 | 2003-12-04 | 2004-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-06-04 | 2007-12-04 | 2008-06-04 | $7700.00 | Window Closed / Lapsed |