Plasma chemical vapor deposition process for producing a hard multilayer coated product
Assignee: YKK Corp
•
Filing: 1992-03-31
•
Granted: 1993-11-09
•
Expires: 2012-03-31
Abstract
Abstract This present invention provides a hard multilayer coated product comprising a hard wear-resistant titanium compound coating layer, a titanium compound layer having a compositional gradient and a self-lubricating coating layer comprising hard amorphous carbon as the principal component successively formed on the surface of a substrate, the first layer being formed at about 500° C. by the plasma CVD method in a vacuum followed by the formation of the second and third layers at 250° to 400° C. in a vacuum maintained at the same level as above. The hard multilayer coated product is improved in wear-resistance and self-lubricity.
Inventors
- 👤 Shingo Kawamura
- 👤 Minoru Yamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 07:50
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/32; C23C16/34; C23C28/00; C23C28/04; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/30
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
142 words
A process for forming a multilayered coated product, said process comprising the steps of placing a substrate in a vacuum furnace; creating a vacuum in said vacuum furnace; contacting said substrate with a source gas containing a titanium compound at a temperature of about 500° C.; forming a titanium-containing coating layer on said substrate by plasma chemical vapor deposition; forming a second coating layer on said substrate by plasma chemical vapor deposition, said second coating layer having a titanium compositional gradient; and forming a third coating layer on said substrate by plasma chemical vapor deposition, said third coating layer being a self-lubricating layer and comprising amorphous carbon and said second and third coating layers being formed on said substrate while maintaining said vacuum in said furnace and maintaining said substrate at a temperature in a range of from 250° to 400° C.
Claim 2
Dependent Claim
142 words
A process for forming a multilayered coated product, said process comprising the steps of placing a substrate in a vacuum furnace; creating a vacuum in said vacuum furnace; contacting said substrate with a source gas containing a titanium compound at a temperature of about 500° C.; forming a titanium-containing coating layer on said substrate by plasma chemical vapor deposition; forming a second coating layer on said substrate by plasma chemical vapor deposition, said second coating layer having a titanium compositional gradient; and forming a third coating layer on said substrate by plasma chemical vapor deposition, said third coating layer being a self-lubricating layer and comprising amorphous carbon and said second and third coating layers being formed on said substrate while maintaining said vacuum in said furnace and maintaining said substrate at a temperature in a range of from 250° to 400° C.
Claim 3
Dependent Claim
57 words
The process of claim 1, wherein the second and third coating layers are formed by contacting said substrate with a feed gas comprising a hydrocarbon and a mixture of a hydrogen gas and gaseous titanium tetrachloride, said feed gas having a mole ratio of carbon in the hydrocarbon to hydrogen in the mixture of at least 0.2.
Claim 4
Dependent Claim
16 words
The process of claim 1, wherein said second and third coating layers comprise TiC or TiN.
Claim 5
Dependent Claim
29 words
The process of claim 2, wherein said third coating layer is formed by increasing the mole ratio of the carbon in the hydrocarbon to the hydrogen in the mixture.
Claim 6
Dependent Claim
30 words
The process of claim 1, wherein said third coating layer comprises amorphous carbon and 5 to 40 mol % of a titanium compound having up to 3 at. % chlorine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-08 | 1997-05-10 | 1997-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-08 | 2001-05-10 | 2001-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-08 | 2005-05-10 | 2005-11-09 | $7700.00 | Window Closed / Lapsed |