Assignee: Fried Krupp AG Hoesch Krupp
•
Filing: 1989-12-11
•
Granted: 1992-03-03
•
Expires: 2009-12-11
Abstract
Abstract A plasma-activated CVD process provides improved adhesion of the coated surface layers and employs, as the plasma exciting source, a pulsed direct voltage and a residual direct voltage which remains during the pulse intervals. The residual direct voltage is equal to or greater than the lowest ionization potential of the gases participating in the CVD process, but is no more than 50% of the maximum value of the pulsed direct voltage. The total thickness of the layer(s) does not exceed 30 μm and the temperature of the basic tool body during the coating process is reduced, compared to prior art plasma CVD processes, and ranges from between 400° to 800° C., and is preferably kept below 600° C.
Inventors
- 👤 Hendrikus van den Berg
- 👤 Udo Konig
- 👤 Ralf Tabersky
- 👤 Josef Blum
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:23
CPC Classifications
G; G11; G11B; G11B23/00; G11B23/20; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; B; B26; B26D; B26D1/00; B26D1/0006; C23C16/32; C23C16/34; C23C16/36; C23C16/44; C23C16/50; C23C16/515; C23C16/52; C23C30/00; C23C30/005; B26D2001/002; B26D2001/0046; B26D2001/0053; B26D2001/0066
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
198 words
A plasma-activated CVD process for coating a basic tool body with at least one surface layer comprised of at least one hard substance selected from the group consisting of carbides, nitrides, and carbonitrides of titanium and zirconium, the plasma-activated CVD process comprising: a. positioning a basic tool body in a CVD chamber having means for supplying direct voltage thereto, the basic tool body being connected to the direct voltage supplying means as a cathode thereof; b. introducing into the CVD chamber a reactive gas mixture comprised of a nitrogen-containing substance, a carbon-containing substance, and at least one compound containing at least one of titanium and zirconium; and c. exciting plasma formation at the basic tool body and coating same by chemical vapor deposition by applying a pulsed direct voltage having a residual direct voltage thereto, the residual direct voltage having a magnitude which is at least equal to the lowest ionization potential of any gas in the reactive gas mixture but not exceeding 50% of the maximum value of the pulsed direct voltage, wherein the CVD chamber has a temperature ranging from 400° to 800° C. and a pressure ranging from 10 to 1,000 Pascal during step (c).
Claim 2
Dependent Claim
198 words
A plasma-activated CVD process for coating a basic tool body with at least one surface layer comprised of at least one hard substance selected from the group consisting of carbides, nitrides, and carbonitrides of titanium and zirconium, the plasma-activated CVD process comprising: a. positioning a basic tool body in a CVD chamber having means for supplying direct voltage thereto, the basic tool body being connected to the direct voltage supplying means as a cathode thereof; b. introducing into the CVD chamber a reactive gas mixture comprised of a nitrogen-containing substance, a carbon-containing substance, and at least one compound containing at least one of titanium and zirconium; and c. exciting plasma formation at the basic tool body and coating same by chemical vapor deposition by applying a pulsed direct voltage having a residual direct voltage thereto, the residual direct voltage having a magnitude which is at least equal to the lowest ionization potential of any gas in the reactive gas mixture but not exceeding 50% of the maximum value of the pulsed direct voltage, wherein the CVD chamber has a temperature ranging from 400° to 800° C. and a pressure ranging from 10 to 1,000 Pascal during step (c).
Claim 3
Dependent Claim
22 words
The plasma-activated process according to claim 1, wherein the pulsed direct voltage has a maximum voltage ranging from 200 to 900 volts.
Claim 4
Dependent Claim
30 words
The plasma-activated CVD process according to claim 1, wherein a ratio of the residual direct voltage to the maximum voltage of the pulsed direct voltage ranges from 0.02 to 0.5.
Claim 5
Dependent Claim
25 words
The plasma-activated CVD process according to claim 1, wherein the pulsed direct voltage has a duration period which ranges from 20 μs to 20 ms.
Claim 6
Dependent Claim
38 words
The plasma-activated CVD process according to claim 1, wherein the pulsed direct voltage has a pulse length and a pulse interval, and wherein a ratio of the pulse length to the pulse interval ranges from 0.1 to 0.6.
Claim 7
Dependent Claim
26 words
The plasma-activated CVD process according to claim 1, wherein the at least one surface layer has a growth rate which ranges from 0.5 to 10 μm/h.
Claim 8
Dependent Claim
21 words
The plasma-activated CVD process according to claim 1, wherein the CVD chamber has a temperature that does not exceed 600° C.
Claim 9
Dependent Claim
22 words
The plasma-activated CVD process according to claim 1, wherein the basic tool body is comprised of one of hard metal and steel.
References Cited (Backward Citations)
US4500563A
Cited
US4675200A
Cited
EP0193201A1
Cited
US4720437A
Cited
US4758451A
Cited
GB2194556A
Cited
US4915977A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-03 | 1995-09-02 | 1996-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-03 | 1999-09-02 | 2000-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-03 | 2003-09-02 | 2004-03-03 | $7700.00 | Window Closed / Lapsed |