Multi-component stabilizer system for polyolefins pigmented with phthalocyanine pigments
Assignee: Noveon IP Holdings Corp
•
Filing: 1990-01-23
•
Granted: 1991-09-17
•
Expires: 2010-01-23
Abstract
Abstract Excellent color stabilization as well as fiber integrity is obtained in bright sunlight and at relatively high temperature, in polyolefin (PO) articles pigmented with phthalocyanine pigments, by combining the pigment with two `large molecule` primary stabilizers, the first a hindered amine light stabilizer (HALS) and the second a metal-organic phosphonate. The first contains at least one triazine ring, and each substitutable position on each triazine ring is substituted with an oxo-piperazinyl group; the second is a 2.1 complex of an alkylated phenol phosphonate with a Group VIII or Group IIA metal, e.g. a metal bis[O-alky(3,5-di-t-butyl-4-hytdroxybenzyl)] phosphonate ("35-DHBP"). Stabilization of the PO's color is obtained for as long as the PO articles themselves are stabilized by the combination of primary stabilizers. With the combination, phthalocyanine pigmented articles are not only thermooxidatively and light-stabilized, but there is exceptionally low color fade. Because fibers are extruded twice for better distribution of pigment, a small amount, no more than 0.1 phr of a secondary melt-stabilizer, may be used. Blue- and green-pigmented PO articles in particular, so stabilized, exhibit less than a ±2 change in color (color fading) due to degradation of the pigment, over exposure resulting in absorption of 1240 Kjoules. Such exposure, deemed equivalent to exposure to sunlight for about 2 years in Florida at a 45° South exposure, of PP fibers pigmented with the combination of primary stabilizers suffer essentially no loss of color due to degradation of the pigmented polymer.
Inventors
- 👤 George Kletecka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:22
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3467; C08K5/3477; C08K5/3492; C08K5/34926; C08K5/49; C08K5/51; C08K5/53; C08K5/5317; C08K5/5333
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
308 words
A method for imparting improved discoloration resistance to a shaped article of a polyolefin, comprising, incorporating into a melt from which said shaped article is formed, an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers substantially free of secondary stabilizers, including (a) a substituted oxo-piperazinyl triazine ("PIP-T") having a structure selected from the group consisting of ##STR9## wherein PSP is a substitutent having the following formula ##STR10## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 ,independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR11## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p1 represents an integer in the range from 2 to about 10; and, (b) a 2:1 complex of an alkylated phenol phosphonate with a metal ("3,5-DHBP") represented by the structure: ##STR12## wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 2
Independent Claim
308 words
A method for imparting improved discoloration resistance to a shaped article of a polyolefin, comprising, incorporating into a melt from which said shaped article is formed, an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers substantially free of secondary stabilizers, including (a) a substituted oxo-piperazinyl triazine ("PIP-T") having a structure selected from the group consisting of ##STR9## wherein PSP is a substitutent having the following formula ##STR10## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 ,independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR11## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p1 represents an integer in the range from 2 to about 10; and, (b) a 2:1 complex of an alkylated phenol phosphonate with a metal ("3,5-DHBP") represented by the structure: ##STR12## wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 3
Dependent Claim
105 words
The method of claim 1 wherein said polyolefin is selected from the group consisting of a homopolymer of ethylene, a copolymer of ethylene with a minor amount by weight of propylene, a copolymer of ethylene with a minor amount by weight of propylene, a random or block copolymer (E-co-X) wherein E represents ethylene and X represents a minor amount by weight of a monoolefinically unsaturated monomer, a homopolymer of propylene, a copolymer of propylene with a minor amount by weight of ethylene, a copolymer of propylene with a minor amount by weight of ethylene, and a random or block copolymer (P-co-X) wherein P represents propylene.
Claim 4
Dependent Claim
115 words
The method of claim 2 comprising exposing said phthalocyanine-pigmented in a Xenon Arc Weather-O-Meter SAE J1885 test for a period sufficient to absorb 1240 Kjoules, and resulting in less color change than ±2; and, said PIP-T is specified by, R hu 1 being C 3 -C 12 alkyl, and C 6 -C 7 cycloalkyl; R 2 and R 3 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; R 4 and R 5 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; and, R 6 is hydrogen, CH 3 , C 1 -C 3 alkoxy or C 2 -C 3 acyl.
Claim 5
Dependent Claim
30 words
The method of claim 3 wherein said PSP is represented by a structure selected from the group consisting of ##STR13## the bond on N indicates connection to the triazine ring.
Claim 6
Dependent Claim
18 words
The method of claim 4 wherein said metal is selected from the group consisting of nickel and calcium.
Claim 7
Dependent Claim
35 words
The method of claim 4 wherein said phthalocyanine pigment is selected from the group consisting of Blue 15, Blue 16, Blue 29, Blues 15:1 through 15:6, Green 7, Green 36-Y, Green 36-6Y and combinations thereof.
Claim 8
Dependent Claim
65 words
The method of claim 6 wherein said phthalocyanine pigment is present in an amount in the range from 0.1 phr to about 1 phr; said PIP-T is present in an amount in the range from 20 ppm to about 2 phr; said 3,5-DHBP is present in an amount in the range from 20 ppm to about 2 phr; based on the weight of said polyolefin.
Claim 9
Dependent Claim
33 words
The method of claim 3 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a meltstabilizing amount, less than 0.1 phr.
Claim 10
Dependent Claim
33 words
The method of claim 7 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a meltstabilizing amount, less than 0.1 phr.
Claim 11
Dependent Claim
37 words
The method of claim 9 wherein said polyolefin is selected from polypropylene homopolymer and a copolymer of propylene with a minor amount of ethylene; and, said secondary stabilizer is selected from a hindered phenol and a phosphite.
Claim 12
Dependent Claim
294 words
An article of manufacture of improved discoloration resistance, formed from a polyolefin containing an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers, the first a (a) a substituted oxo-piperazinyl triazine ("PIP-T") having a structure selected from the group consisting of ##STR14## wherein PSP is a substitutent having the following formula ##STR15## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 , independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR16## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p1 represents an integer in the range from 2 to about 10; and (b) a 2:1 complex of an alkylated phenol phosphonate with a metal ("3,5-DHBP") represented by the structure: ##STR17## t-Bu=t-butyl wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 13
Dependent Claim
294 words
An article of manufacture of improved discoloration resistance, formed from a polyolefin containing an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers, the first a (a) a substituted oxo-piperazinyl triazine ("PIP-T") having a structure selected from the group consisting of ##STR14## wherein PSP is a substitutent having the following formula ##STR15## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 , independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR16## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p1 represents an integer in the range from 2 to about 10; and (b) a 2:1 complex of an alkylated phenol phosphonate with a metal ("3,5-DHBP") represented by the structure: ##STR17## t-Bu=t-butyl wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 14
Dependent Claim
105 words
The article of claim 11 wherein said polyolefin is selected from the group consisting of a homopolymer of ethylene, a copolymer of ethylene with a minor amount by weight of propylene, a copolymer of ethylene with a minor amount by weight of propylene, a random or block copolymer (E-co-X) wherein E represents ethylene and X represents a minor amount by weight of a monoolefinically unsaturated monomer, a homopolymer of propylene, a copolymer of propylene with a minor amount by weight of ethylene, a copolymer of propylene with a minor amount by weight of ethylene, and a random or block copolymer (P-co-X) wherein P represents propylene.
Claim 15
Dependent Claim
114 words
The article of claim 12 wherein exposing said phthalocyanine-pigmented in a Xenon Arc Weather-O-Meter SAE J1885 test for a period sufficient to absorb 1240 Kjoules, and resulting in less color change than ±2; and, said PIP-T is specified by, R 1 being C 3 -C 12 alkyl, and C 6 -C 7 cycloalkyl; R 2 and R 3 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; R 4 and R 5 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; and, R 6 is hydrogen, CH 3 , C 1 -C 3 alkoxy or C 2 -C 3 acyl.
Claim 16
Dependent Claim
30 words
The article of claim 13 wherein said PSP is represented by a structure selected from the group consisting of ##STR18## the bond on N indicates connection to the triazine ring.
Claim 17
Dependent Claim
18 words
The article of claim 14 wherein said metal is selected from the group consisting of nickel and calcium.
Claim 18
Dependent Claim
35 words
The article of claim 14 wherein said phthalocyanine pigment is selected from the group consisting of Blue 15, Blue 16, Blue 29, Blues 15:1 through 15:6, Green 7, Green 36-Y, Green 36-6Y and combinations thereof.
Claim 19
Dependent Claim
65 words
The article of claim 6 wherein said phthalocyanine pigment is present in an amount in the range from 20 ppm to about 1 phr; said PIP-T is present in an amount in the range from 0.1 phr to about 2 phr; said 3,5-DHBP is present in an amount in the range from 20 ppm to about 2 phr; based on the weight of said polyolefin.
Claim 20
Dependent Claim
33 words
The article of claim 13 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a melt-stabilizing amount, less than 0.1 phr.
Claim 21
Dependent Claim
33 words
The article of claim 17 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a melt-stabilizing amount, less than 0.1 phr.
Claim 22
Dependent Claim
37 words
The article of claim 19 wherein said polyolefin is selected from polypropylene homopolymer and a copolymer of propylene with a minor amount of ethylene; and, said secondary stabilizer is selected from a hindered phenol and a phosphite.
Claim 23
Dependent Claim
318 words
A multi-component stabilizer system for stabilizing pigmented polyolefin against discoloration, thermooxidative degradation, and degradation due to ultraviolet light, consisting essentially of (a) no more than a melt-stabilizing quantity of a secondary stabilizer, and an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers identified as "PIP-T" and "3,5-DHBP" herebelow; said PIP-T being a substituted oxo-piperazinyl triazine having a structure selected from the group consisting of ##STR19## wherein PSP is a substitutent having the following formula ##STR20## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 , independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR21## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p represents an integer in the range from 2 to about 10; (b) said 3,5-DHBP being a 2:1 complex of an alkylated phenol phosphonate with a metal represented by the structure: ##STR22## wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 24
Dependent Claim
318 words
A multi-component stabilizer system for stabilizing pigmented polyolefin against discoloration, thermooxidative degradation, and degradation due to ultraviolet light, consisting essentially of (a) no more than a melt-stabilizing quantity of a secondary stabilizer, and an effective amount, sufficient to color the article from 0.1 phr but less than 2 phr, of a phthalocyanine pigment so as to produce a phthalocyanine-pigmented article, and an effective amount, sufficient to attenuate degradation of said phthalocyanine-pigmented article when exposed to sunlight, of a combination of two primary stabilizers identified as "PIP-T" and "3,5-DHBP" herebelow; said PIP-T being a substituted oxo-piperazinyl triazine having a structure selected from the group consisting of ##STR19## wherein PSP is a substitutent having the following formula ##STR20## wherein R 1 represents C 1 -C 24 alkyl, C 5 -C 7 cycloalkyl, C 7 -C 20 aralkyl, C 1 -C 24 hydroxyalkyl, C 1 -C 24 aminoalkyl, C 1 -C 24 alkylaminoalkyl, and C 6 -C 20 cycloaminoalkyl; R 2 , R 3 , R 4 , and R 5 , independently represent C 1 -C 18 alkyl, or when together cyclized, R 2 with R 3 , and R 4 with R 5 , represent C 4 -C 12 cycloalkyl, and C 1 -C 8 alkyl-substituted cycloalkyl; and, R 6 is selected from the group consisting of hydrogen, C 1 -C 8 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkanoyl, C 3 -C 8 alkenoyl and ##STR21## wherein R 7 represents hydrogen, C 1 -C 18 alkyl or alkenyl, phenyl or naphthyl; and, p represents an integer in the range from 2 to about 10; (b) said 3,5-DHBP being a 2:1 complex of an alkylated phenol phosphonate with a metal represented by the structure: ##STR22## wherein R 8 represents C 1 -C 12 alkyl, C 4 -C 12 cycloalkyl, and, C 1 -C 8 alkyl-substituted cycloalkyl; and, M represents a Group VIII or Group IIA metal.
Claim 25
Dependent Claim
106 words
The of stabilizer system claim 21 wherein said polyolefin is selected from the group consisting of a homopolymer of ethylene, a copolymer of ethylene with a minor amount by weight of propylene, a copolymer of ethylene with a minor amount by weight of propylene, a random or block copolymer (E-co-X) wherein E represents ethylene and X represents a minor amount by weight of a monoolefinically unsaturated monomer, a homopolymer of propylene, a copolymer of propylene with a minor amount by weight of ethylene, a copolymer of propylene with a minor amount by weight of ethylene, and a random or block copolymer (P-co-X) wherein P represents propylene.
Claim 26
Dependent Claim
115 words
The stabilizer system of claim 22 comprising exposing said phthalocyanine-pigmented in a Xenon Arc Weather-O-Meter SAE J1885 test for a period sufficient to absorb 1240 Kjoules, and resulting in less color change than ±2; and, said PIP-T is specified by, R 1 being C 3 -C 12 alkyl, and C 6 -C 7 cycloalkyl; R 2 and R 3 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; R 4 and R 5 are each C 1 -C 3 alkyl, and together, when cyclized represent cyclohexyl, methylcyclohexyl, or cycloheptyl; and, R 6 is hydrogen, CH 3 , C 1 -C 3 alkoxy or C 2 -C 3 acyl.
Claim 27
Dependent Claim
31 words
The stabilizer system of claim 23 wherein said PSP is represented by a structure selected from the group consisting of ##STR23## the bond on N indicates connection to the triazine ring.
Claim 28
Dependent Claim
19 words
The stabilizer system of claim 24 wherein said metal is selected from the group consisting of nickel and calcium.
Claim 29
Dependent Claim
36 words
The stabilizer system of claim 24 wherein said phthalocyanine pigment is selected from the group consisting of Blue 15, Blue 16, Blue 29, Blues 15:1 through 15:6, Green 7, Green 36-Y, Green 36-6Y and combinations thereof.
Claim 30
Dependent Claim
66 words
The stabilizer system of claim 26 wherein said phthalocyanine pigment is present in an amount in the range from 0.1 phr to about 1 phr; said PIP-T is present in an amount in the range from 20 ppm to about 2 phr; said 3,5-DHBP is present in an amount in the range from 20 ppm to about 2 phr; based on the weight of said polyolefin.
Claim 31
Dependent Claim
34 words
The stabilizer system of claim 23 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a melt-stabilizing amount, less than 0.1 phr.
Claim 32
Dependent Claim
34 words
The stabilizer system of claim 27 wherein said article is formed by melt-extruding said polyolefin, and said melt includes a secondary stabilizer present in no more than a melt-stabilizing amount, less than 0.1 phr.
Claim 33
Dependent Claim
38 words
The stabilizer system of claim 29 wherein said polyolefin is selected from polypropylene homopolymer and a copolymer of propylene with a minor amount of ethylene, and, said secondary stabilizer is selected from a hindered phenol and a phosphite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-16 | 1995-03-18 | 1995-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-16 | 1999-03-18 | 1999-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-16 | 2003-03-18 | 2003-09-17 | $7700.00 | Window Closed / Lapsed |