Assignee: Nissin Electric Co Ltd
•
Filing: 1990-06-27
•
Granted: 1991-04-23
•
Expires: 2010-06-27
Abstract
Abstract A method of forming a diamond film on a substrate comprises the steps of depositing carbon on said substrate in vacuum by vapor deposition, and irradiating accelerated ions onto said substrate, said ions being obtained by ionizing a gas composed of at least one of a hydrogen gas, inert gases, hydrocarbon gases, organic compound gases and silicon base gases.
Inventors
- 👤 Kiyoshi Ogata
- 👤 Yasunori Ando
- 👤 Eiji Kamijo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:28
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/06; C23C14/0605; C23C14/0611; C30; C30B; C30B23/00; C30B23/02; C30B29/00; C30B29/02; C30B29/04
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
74 words
A method of forming a diamond film on a substrate, comprising the steps of: depositing carbon from an evaporation source onto said substrate in vacuum by vapor deposition to provide a carbon film on the substrate; and irradiating accelerated ions having an energy of less than 40 KeV onto said substrate, said ions being obtained by ionizing a gas composed of at least one of a hydrogen gas, inert gases, and silicon base gases.
Claim 2
Independent Claim
74 words
A method of forming a diamond film on a substrate, comprising the steps of: depositing carbon from an evaporation source onto said substrate in vacuum by vapor deposition to provide a carbon film on the substrate; and irradiating accelerated ions having an energy of less than 40 KeV onto said substrate, said ions being obtained by ionizing a gas composed of at least one of a hydrogen gas, inert gases, and silicon base gases.
Claim 3
Dependent Claim
25 words
A method of forming a diamond film on a substrate as claimed in claim 1, wherein said silicon base gases are monosilane and dislane gases.
Claim 4
Dependent Claim
26 words
A method of forming a diamond film on a substrate as claimed in claim 1, wherein the degree of vacuum is 10 -5 -10 -7 Torr.
Claim 5
Dependent Claim
39 words
A method of forming a diamond film on a substrate as claimed in claim 1, wherein said depositing and irradiating steps are carried out at a temperature within the range of room temperature to that of several hundred degrees.
Claim 6
Independent Claim
96 words
A method of forming a diamond film comprising the steps of transporting carbon atoms from an evaporation source and neon ions having kinetic energy to provide a carbon film on a substrate in vacuum, wherein said energy (eV) of said neon ions and the ratio (%) of the quantity of said transported neon ions to that of said transported carbon atoms are selected within the region enclosed with four points (10, 10), (10, 73), (1,000, 1) and (1,000, 15) in rectangular coordinates made up of said energy as the abscissa and said ratio as the ordinate.
Claim 7
Independent Claim
96 words
A method of forming a diamond film comprising the steps of transporting carbon atoms from an evaporation source and neon ions having kinetic energy to provide a carbon film on a substrate in vacuum, wherein said energy (eV) of said neon ions and the ratio (%) of the quantity of said transported neon ions to that of said transported carbon atoms are selected within the region enclosed with four points (10, 10), (10, 73), (1,000, 1) and (1,000, 15) in rectangular coordinates made up of said energy as the abscissa and said ratio as the ordinate.
Claim 8
Dependent Claim
33 words
A method of forming a diamond film as claimed in claim 5, wherein an incident angle of said transported neon ions relative to a perpendicular of a surface of said substrate is 0°-60°.
Claim 9
Dependent Claim
23 words
A method of forming a diamond film as claimed in claim 5, wherein the degree of vacuum is 10 -5 -10 -7 Torr.
Claim 10
Dependent Claim
34 words
A method of forming a diamond film as claimed in claim 5, wherein said transporting steps are carried out at a temperature within the range of room temperature to that of several hundred degrees.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-22 | 1994-10-22 | 1995-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-22 | 1998-10-22 | 1999-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-22 | 2002-10-22 | 2003-04-23 | $7700.00 | Window Closed / Lapsed |