Prosthetic anterior cruciate ligament design

Claim 2

An artificial ligament device having a generally multilayered or tubular woven ligament and being adapted for joining the ends of two bones, at least one of the bones having a tunnel extending therethrough, said device comprising: (a) a ligament having (1) an intra-articular region adapted for disposition between the respective ends of the two bones; (2) at least one bend region juxtaposed to the intra-articular region and adapted for encasement within a bone block and being located generally where the ligament exits and runs within the bone block; and (3) at least one end region juxtaposed to the bend region and adapted for fixed encasement within the bone block; a plurality of warp yarns extending at least through the bend region; and a fill yarn woven through the warp yarns in a density dependent upon the number of picks per inch in the weave; and a pick density in the bend region being not greater than one-third the pick density in the intra-articular region; and (b) at least one bone block adapted for insertion into the bone tunnel and having fixedly encased therein the end region and a portion of the bend region, said bone block providing a permanent bend radius for the bend region at the point of exit from the bone block.

Claim 3

The artificial ligament recited in claim 1 wherein the pick density in the bend region is less than one-fifth the pick density in the end region and wherein the exposed portion of the ligament is encased within a thin polymer sleeve.

Claim 4

The artificial ligament recited in claim 1 wherein the number of picks per inch in the bend region is not more than eight and wherein the bone block comprises a thermoset resin and the resin runs within the interstices in the woven ligament.

Claim 5

The artificial ligament recited in claim 1 wherein the number of picks per inch in the bend region is not more than three and wherein the bone block is thermomolded to the ligament.

Claim 6

The artificial ligament recited in claim 1 wherein the number of picks per inch in the bend region is not more than one.

Claim 7

The artificial ligament recited in claim 1 further comprising: marker means disposed relative to the bend region for providing a visual indication of the location of the bend region.

Claim 8

The artificial ligament recited in claim 6 wherein the marker means includes a thread disposed transverse to the warp yarns at each end of the bend region.

Claim 9

An artificial ligament device adapted for joining the ends of two bones, at least one of the bones having a tunnel extending therethrough, said device comprising: (a) a ligament of a generally multilayered or tubular woven structure having warp and filler yarns wherein the warp yarns are composite, having a higher melting polymer core within a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising: (1) an intra-articular region adapted for disposition between the respective ends of the two bones; (2) at least one bend region Juxtaposed to the intra-articular region and being located generally where the ligament exits and runs within the bone block; (3) at least one end region juxtaposed to the bend region and adapted for thermomold encasement within a bone block; a plurality of warp yarns extending continuously through the intra-articular region, and the bend region; a fill yarn woven through the warp yarns with a pick density in the bend region of not more than eight picks per inch; and each of the warp and fill yarns consisting of filaments numbering in a range between about 20 and 200 filaments and having a density in the range of about 50 to 1100 denier; and (b) at least one bone block adapted for insertion into the bone tunnel and being thermomolded to the ligament so as to provide a permanent bend radius for the bend region at the point of exit of the bend region from the bone block.

Claim 10

An artificial ligament device adapted for joining the ends of two bones, at least one of the bones having a tunnel extending therethrough, said device comprising: (a) a ligament of a generally multilayered or tubular woven structure having warp and filler yarns wherein the warp yarns are composite, having a higher melting polymer core within a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising: (1) an intra-articular region adapted for disposition between the respective ends of the two bones; (2) at least one bend region Juxtaposed to the intra-articular region and being located generally where the ligament exits and runs within the bone block; (3) at least one end region juxtaposed to the bend region and adapted for thermomold encasement within a bone block; a plurality of warp yarns extending continuously through the intra-articular region, and the bend region; a fill yarn woven through the warp yarns with a pick density in the bend region of not more than eight picks per inch; and each of the warp and fill yarns consisting of filaments numbering in a range between about 20 and 200 filaments and having a density in the range of about 50 to 1100 denier; and (b) at least one bone block adapted for insertion into the bone tunnel and being thermomolded to the ligament so as to provide a permanent bend radius for the bend region at the point of exit of the bend region from the bone block.

Claim 11

The artificial ligament recited in claim 8 wherein each of the warp and fill yarns consists of filaments numbering in a range of about 50 to 150 filaments and a diameter in a range of about 50 to 150 denier and wherein the bone block comprises the lower melting polymer.

Claim 12

The artificial ligament recited in claim 9 wherein each of the warp and fill yarns consists of about 100 filaments and has a diameter of about 350 denier.

Claim 13

The artificial ligament device of claim 8 further comprising a thin polymer sleeve encasing the portion of the ligament extending from the bone block.

Claim 14

The artificial ligament device of claim 11 wherein the number of bone blocks, bend regions and end regions is two and said bone block, bend regions and end regions are symmetrically arranged about a central intra-articular region and wherein the sleeve is thermomolded to encase the portion of the ligament exposed between the bone blocks.

Claim 15

A replacement ligament device, which device comprises: (a) an artificial ligament of a generally multilayered or tubular woven structure having warp and filling yarns wherein the warp yarns are composite, having a higher melting polymer core with a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising (1) an intra-articular region adapted for disposition between the respective ends of the two bones and having woven, highly crimped warp yarns wherein the degree of crimping of the warp yarns is such that, within the range of normal physiological loads, the intra-articular region has an elongation at failure and an elasticity substantially the same as those of a normal natural ligament of the type that the artificial ligament is intended to replace; (2) at least one bend region juxtaposed to the intra-articular region wherein the degree of crimping of the warp yarns is substantially less than in the intra-articular region and wherein the pick density is from zero to eight picks per inch; and (3) at least one end region juxtaposed to the bend region at the end of the ligament wherein the end region is woven under a relatively high warp tension and wherein the degree of crimping is substantially less than in the intra-articular region for providing a strong, stiff matrix for thermomold attachment of the end region to a bone block; and (b) at least one bone block of a thermoplastic, low melting polymer wherein the bone block is sized for emplacement into a bone tunnel drilled into a bone to which a normal natural ligament of the type that the artificial ligament is intended to replace would attach, and wherein the bone block is thermomolded to said ligament so that about one half of the bend region and the contiguous portion of the end region of the ligament are fixedly encased within the bone block and wherein the bone block provides a permanent bend radius for the ligament at the point of attachment to the ligament, said bend radius being sized for enhancing the bending fatigue life of the ligament.

Claim 16

A replacement ligament device, which device comprises: (a) an artificial ligament of a generally multilayered or tubular woven structure having warp and filling yarns wherein the warp yarns are composite, having a higher melting polymer core with a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising (1) an intra-articular region adapted for disposition between the respective ends of the two bones and having woven, highly crimped warp yarns wherein the degree of crimping of the warp yarns is such that, within the range of normal physiological loads, the intra-articular region has an elongation at failure and an elasticity substantially the same as those of a normal natural ligament of the type that the artificial ligament is intended to replace; (2) at least one bend region juxtaposed to the intra-articular region wherein the degree of crimping of the warp yarns is substantially less than in the intra-articular region and wherein the pick density is from zero to eight picks per inch; and (3) at least one end region juxtaposed to the bend region at the end of the ligament wherein the end region is woven under a relatively high warp tension and wherein the degree of crimping is substantially less than in the intra-articular region for providing a strong, stiff matrix for thermomold attachment of the end region to a bone block; and (b) at least one bone block of a thermoplastic, low melting polymer wherein the bone block is sized for emplacement into a bone tunnel drilled into a bone to which a normal natural ligament of the type that the artificial ligament is intended to replace would attach, and wherein the bone block is thermomolded to said ligament so that about one half of the bend region and the contiguous portion of the end region of the ligament are fixedly encased within the bone block and wherein the bone block provides a permanent bend radius for the ligament at the point of attachment to the ligament, said bend radius being sized for enhancing the bending fatigue life of the ligament.

Claim 17

The device of claim 13 comprising two bone blocks, one thermomolded to each end of the ligament so as to encase therein respectively about one-half of a bend region and the contiguous portion of the end region of the ligament and wherein the thermomold interface between the bone block and the ligament has an ultimate shear load in excess of about 1800 Newtons.

Claim 18

The device of claim 13 wherein the lower melting fiber and the bone block consist essentially of the same biocompatible, thermoplastic polymer.

Claim 19

The device of claim 13 wherein the bone block and the lower melting fiber comprise a silicone-modified thermoplastic elastomer.

Claim 20

The device of claim 13 wherein the intra-articular region has a percent elongation at failure of from about 10% to about 50% and an elasticity which enables it to recover to substantially its original dimensions after being subjected to repeated cycles of 25% of the tensile failure load and wherein the mechanical stiffness of the bone block is at least about 1500 Newtons per millimeter and the ultimate shear load of the thermomold interface between the ligament and the bond block is at least about 1000 Newtons.

Claim 21

The device of claim 13 wherein the warp and filling yarns are prepared from polymer fibers which exhibit low elongations under load and wherein the bone block is elongate and has the shape in the cross-section selected from the group consisting of a circle, square or rectangle.

Claim 22

The device of claim 16, wherein the warp and filling yarns have diameters from about 50 to about 1100 denier, and contain from about 20 to about 200 filaments per yarn.

Claim 23

The device of claim 14 wherein the bone block has the shape of a solid right cylinder having a right cross-sectional diameter of from about 6 to 14 mm and the ultimate shear load of the interface is at least about 1800 Newtons.

Claim 24

The device of claim 20 wherein the diameter is from about 8 to 12 mm..

Claim 25

The device of claim 17 wherein the bone block has the shape of a solid right cylinder with a conical depression in the end at the point from which the ligament exits, wherein the side of the cone is convex to provide the permanent bend radius.

Claim 26

The device of claim 22 wherein the bend radius is from about 1.5 to 1.3 mm.

Claim 27

The device of claim 16 wherein the filling yarns are prepared solely from the higher melting polymer.

Claim 28

The device of claim 13 wherein the warp density of the intra-articular region ranges from about 800 to about 1200 yarns per inch and the pick density of the intra-articular region ranges from about 40 to about 70 picks per inch and the pick density of the bend region is not more than one.

Claim 29

The device of claim 13 wherein the weave pattern of the intra-articular region is a 5-1-1-5 broken twill.

Claim 30

The device of claim 25 wherein the warp density of the intra-articular region is about 1000 yarns per inch and the pick density of the intra-articular region ranges from about 50 to about 60 picks per inch.

Claim 31

The device of claim 13 wherein the warp tension employed during the weaving of the intra-articular region is from about 0.01 to about 0.05 lb. per yarn end, and the filling yarn tension is from about 0.05 to about 0.5 lb. per yarn end.

Claim 32

The device of claim 15 wherein the ligament is subjected to a post-weaving heat-setting step prior to being thermomolded into the bone block, wherein the heat-setting step is to increase the elongation under load of the intra-articular region and to increase the stiffness of the end region.

Claim 33

The device of claim 13 wherein the ligament is subjected to a post-weaving heat-setting step to increase the elongation under load of the intra-articular region and to increase the stiffness of the end region contiguous thereto.

Claim 34

The device of claim 29 or 30 wherein the intra-articular region is substantially unconstrained during the heat-setting step, thereby allowing the warp yarns to crimp and the weft yarns to remain uncrimped, producing a high elongation under load, and the bend and end regions are constrained against longitudinal movement, thereby inhibiting the warp yarns from crimping and producing a low elongation under load.

Claim 35

The device of claim 29 or 30 wherein the elongation under load of the bend region is less than about 15% at failure and the elongation under load of the intra-articular region is from about 10 to 50% at failure.

Claim 36

The device of claim 29 or 30 wherein the composite yarn is formed during the post-weaving heat-setting step from a substrate yarn comprising commingled lower melting point fibers and higher melting point fibers, the temperature at the heat-setting step being sufficiently above the melting temperature of the lower melting polymer, but sufficiently below the melting temperature of the higher melting polymer, to cause the lower melting fibers to melt to form a coating substantially surrounding the higher melting fibers without weakening the higher melting fibers.

Claim 37

The device of claim 15 wherein the higher melting fiber is polyethylene terephthalate and the lower melting fiber is styrene-ethylene/butylene, styrene block copolymer with polydimethylsiloxane modifiers.

Claim 38

The device of claim 13 wherein the intra-articular region has a relatively small cross-sectional area, a high aspect ratio approximating that of the natural ligament being replaced and a length of from about 30 to about 36 mm.

Claim 39

The device of claim 35 wherein the cross-sectional area is circular with a diameter of from about 4 to 8 mm and wherein the tensile strength of the intra-articular region is from 2000 to about 2250 Newtons.

Claim 40

The device of claim 36 wherein the cross-sectional area is circular with a diameter of from about 4 to 5 mm and the tensile strength is about 3500 Newtons.

Claim 41

The device of claim 33 wherein the warp tension during the weaving of the intra-articular region is from about 0.01 to about 0.05 lb. per yarn end, and the filling tension is from about 0.05 to about 0.5 lb. per yarn end.

Claim 42

The device of claim 15 wherein the higher melting fiber comprises a polyester having a melting point from 10 to 100 Centigrade degrees higher than the melting point of the lower melting fiber.

Claim 43

The device of claim 13 wherein the surface of the bone block is uneven to promote bony ingrowth therein.

Claim 44

The device of claim 40 wherein the uneven surface of the bone block comprises fibrous protuberances.

Claim 45

The device of claim 40 wherein the uneven surface of the bone block is porous.

Claim 46

The device of claim 42 wherein the pores in the porous surface are from about 100 to about 400 microns in diameter and in depth.

Claim 47

The device of claim 40 wherein the uneven surface of the bone block is beaded.

Claim 48

The device of claim 44 wherein the beaded surface comprises raised beads of about 200 to about 400 microns in diameter and in height.

Claim 49

The device of claim 13 wherein the ligament further comprises a thin sleeve of the lower melting polymer thermomolded thereon so as to completely encase the portion of the ligament extending from the bone block.

Claim 50

The device of claim 46 wherein the sleeve of lower melting polymer has a wall thickness of from about 0.05 to about 1.0 mm.

Claim 51

The device of claim 47 wherein the sleeve of lower melting polymer has a wall thickness of from about 0.25 to about 1.0 mm.

Claim 52

The device of claim 13 wherein the surface of the bone block further comprises a thin coating of osteo-conductive material.

Claim 53

A replacement ligament device being adapted for joining the ends of two bones, which device comprises: (a) a multibundled artificial ligament having a plurality of ligaments in the bundle wherein each ligament is of a generally multilayered or tubular woven structure having warp and filler yarns, said ligament comprising (1) an intra-articular region adapted for disposition between the respective ends of the two bones; (2) bend regions juxtaposed to the intra-articular region wherein the elongation under load is substantially less and the flexibility is substantially greater than that of the intra-articular region; (3) end regions juxtaposed to the bend regions at the two ends of the ligament for providing a strong, stiff matrix for fixed encasement within a bone block; and (b) two bone blocks sized for emplacement into a bone tunnel drilled into one of the bones, wherein each bone block encases and is fixedly attached to one end region and a portion of the contiguous bend region and provides a permanent bend radius for the bend region at the point of attachment to the ligament, said bend radius being sized for enhancing the bending fatigue life of the ligament. wherein the device is adapted so that the bend regions are situated at the point at which the bone block exits from a tunnel in the respective bones.

Claim 54

A replacement ligament device being adapted for joining the ends of two bones, which device comprises: (a) a multibundled artificial ligament having a plurality of ligaments in the bundle wherein each ligament is of a generally multilayered or tubular woven structure having warp and filler yarns, said ligament comprising (1) an intra-articular region adapted for disposition between the respective ends of the two bones; (2) bend regions juxtaposed to the intra-articular region wherein the elongation under load is substantially less and the flexibility is substantially greater than that of the intra-articular region; (3) end regions juxtaposed to the bend regions at the two ends of the ligament for providing a strong, stiff matrix for fixed encasement within a bone block; and (b) two bone blocks sized for emplacement into a bone tunnel drilled into one of the bones, wherein each bone block encases and is fixedly attached to one end region and a portion of the contiguous bend region and provides a permanent bend radius for the bend region at the point of attachment to the ligament, said bend radius being sized for enhancing the bending fatigue life of the ligament. wherein the device is adapted so that the bend regions are situated at the point at which the bone block exits from a tunnel in the respective bones.

Claim 55

The device of claim 49 wherein the number of ligaments is two.

Claim 56

The device of claim 49 wherein the number of ligaments is three.

Claim 57

The device of claim 50 wherein the warp yarn has a denier of from about 1000 to about 1500.

Claim 58

A replacement ligament device being adapted for Joining the ends of two bones, which device comprises: (a) a multibundled artificial ligament having a plurality of ligaments in the bundle wherein each ligament is of a generally multilayered or tubular woven structure having warp and filler yarns wherein the warp yarns are composite, having a higher melting polymer core with a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising: (1) an intra-articular region adapted for disposition between the respective ends of the two bones and having highly crimped warp yarns wherein the degree of crimping of the warp yarns is such that, within the range of normal physiological loads, the intra-articular region has an elongation at failure and an elasticity substantially the same as those of a normal natural ligament of the type that the artificial ligament is intended to replace; (2) bend regions juxtaposed to the intra-articular region wherein the degree of crimping of the warp yarns is substantially less than in the intra-articular region and the pick density is from zero to 8 picks per inch, such that the elongation under load is substantially less and the flexibility is substantially greater than that of the intra-articular region; (3) end regions juxtaposed to the bend regions at the two ends of the ligament wherein the end region is woven under a relatively high warp tension and wherein the degree of crimping is substantially less than in the intra-articular region for providing a strong, stiff matrix for thermomold attachment of the end regions to a bone block; and (b) two bone blocks of a thermoplastic, low melting polymer wherein the bone block is sized for emplacement into a bone tunnel drilled into one of the bones, and wherein each bone block has thermomolded thereinto one end of each ligament so that about one half of one bend region and the contiguous portion of one end region of the ligament are fixedly encased within the bone block and wherein the bone block provides a permanent bend radius at the point of attachment to bend region, said bend radius being sized for enhancing the bending fatigue life of the ligament. wherein the device is adapted so that the bend regions are situated at the point at which the bone block exits from the tunnel in the respective bone.

Claim 59

A replacement ligament device being adapted for Joining the ends of two bones, which device comprises: (a) a multibundled artificial ligament having a plurality of ligaments in the bundle wherein each ligament is of a generally multilayered or tubular woven structure having warp and filler yarns wherein the warp yarns are composite, having a higher melting polymer core with a substantially continuous covering of a thermoplastic lower melting polymer, said ligament comprising: (1) an intra-articular region adapted for disposition between the respective ends of the two bones and having highly crimped warp yarns wherein the degree of crimping of the warp yarns is such that, within the range of normal physiological loads, the intra-articular region has an elongation at failure and an elasticity substantially the same as those of a normal natural ligament of the type that the artificial ligament is intended to replace; (2) bend regions juxtaposed to the intra-articular region wherein the degree of crimping of the warp yarns is substantially less than in the intra-articular region and the pick density is from zero to 8 picks per inch, such that the elongation under load is substantially less and the flexibility is substantially greater than that of the intra-articular region; (3) end regions juxtaposed to the bend regions at the two ends of the ligament wherein the end region is woven under a relatively high warp tension and wherein the degree of crimping is substantially less than in the intra-articular region for providing a strong, stiff matrix for thermomold attachment of the end regions to a bone block; and (b) two bone blocks of a thermoplastic, low melting polymer wherein the bone block is sized for emplacement into a bone tunnel drilled into one of the bones, and wherein each bone block has thermomolded thereinto one end of each ligament so that about one half of one bend region and the contiguous portion of one end region of the ligament are fixedly encased within the bone block and wherein the bone block provides a permanent bend radius at the point of attachment to bend region, said bend radius being sized for enhancing the bending fatigue life of the ligament. wherein the device is adapted so that the bend regions are situated at the point at which the bone block exits from the tunnel in the respective bone.

Claim 60

The device of claim 54 wherein the lower melting fiber and the bone block consist essentially of the same biocompatible, thermoplastic polymer, wherein the number of ligaments is three, and wherein the diameter of the warp and filler yarns ranges from about 1000 to 1500 and the number of filaments ranges from about 100 to 230.

Claim 61

The device of claim 55 wherein the bone block and the lower melting fiber comprise a silicone-modified thermoplastic elastomer.

Claim 62

The device of claim 54 wherein the intra-articular region has a percent elongation at failure of from about 10% to about 50% and an elasticity which enables it to recover to substantially its original dimensions after being subjected to repeated cycles of 25% the tensile failure load and wherein the mechanical stiffness of the bone block is at least about 1500 Newtons per millimeter and the ultimate shear load of the thermomold interface between the ligament and the bond block is at least about 1000 Newtons.

Claim 63

The device of claim 54 wherein the warp and filling yarns are prepared from polymer fibers which exhibit low elongations under load and wherein the bone block is elongate and has the shape in the cross-section selected from the group consisting of a circle, square or rectangle.

Claim 64

The device of claim 56, wherein the warp and filling yarns have diameters from about 1250 to about 1350 denier, and contain from about 100 to about 230 filaments per yarn.

Claim 65

The device of claim 56 wherein the bone block has the shape of a solid right cylinder having a right cross-sectional diameter of from about 6 to 14 mm.

Claim 66

The device of claim 60 wherein the diameter of the bone block is from about 8 to 12 mm.

Claim 67

The device of claim 57 wherein the bone block has the shape of a solid right cylinder with a conical depression in the end at the point from which the ligament exits, wherein the side of the cone is convex to provide the permanent bend radius.

Claim 68

The device of claim 62 wherein the bend radius is from about 1.5 to 1.3 mm.

Claim 69

The device of claim 56 wherein the filling yarns are prepared solely from the higher melting polymer.

Claim 70

The device of claim 54 wherein the warp density of the intra-articular region ranges from about 800 to about 1200 yarns per inch and the pick density of the intra-articular region ranges from about 40 to about 70 picks per inch and the pick density of the bend region is not more than one.

Claim 71

The device of claim 54 wherein the weave pattern of the intra-articular region is a 5-1-1-5 broken twill.

Claim 72

The device of claim 54 wherein the warp density of the intra-articular region is about 1000 yarns per inch and the pick density of the intra-articular region ranges from about 50 to about 60 picks per inch.

Claim 73

The device of claim 54 wherein the warp tension employed during the weaving of the intra-articular region is from about 0.01 to about 0.05 lb. per yarn end, and the filling yarn tension is from about 0.05 to about 0.5 lb. per yarn end.

Claim 74

The device of claim 54 wherein the ligament is subjected to a post-weaving heat-setting step prior to being thermomolded into the bone block, wherein the heat-setting step is to increase the elongation under load of the intra-articular region and to increase the stiffness of the end region.

Claim 75

The device of claim 54 wherein the ligament is subjected to a post-weaving heat-setting step to increase the elongation under load of the intra-articular region and to increase the stiffness of the end region contiguous thereto.

Claim 76

The device of claim 69 or 70 wherein the intra-articular region is substantially unconstrained during the heat-setting step, thereby allowing the warp yarns to crimp and the weft yarns to remain uncrimped, producing a high elongation under load, and the bend and end regions are constrained against longitudinal movement, thereby inhibiting the warp yarns from crimping and producing a low elongation under load.

Claim 77

The device of claim 69 or 70 wherein the elongation under load of the bend region is less than about 15% at failure and the elongation under load of the intra-articular region is from about 10 to 50% at failure.

Claim 78

The device of claim 69 or 70 wherein the composite yarn is formed during the post-weaving heat-setting step from a substrate yarn comprising commingled lower melting point fibers and higher melting point fibers, the temperature at the heat-setting step being sufficiently above the melting temperature of the lower melting polymer, but sufficiently below the melting temperature of the higher melting polymer, to cause the lower melting fibers to melt to form a coating substantially surrounding the higher melting fibers without weakening the higher melting fibers.

Claim 79

The device of claim 54 wherein the higher melting fiber is polyethylene terephthalate and the lower melting fiber is styrene-ethylene/butylene, styrene block copolymer with polydimethylsiloxane modifiers.

Claim 80

The device of claim 54 wherein the higher melting fiber comprises a polyester having a melting point at least 10 Centigrade degrees higher than the melting point of the lower melting fiber.

Claim 81

The device of claim 54 wherein the surface of the bone block is uneven to promote bony ingrowth therein.

Claim 82

The device of claim 54 wherein the ligament further comprises a thin sleeve of the lower melting polymer thermomolded thereon so as to completely encase the portion of the ligament extending from the bone block.

Claim 83

The device of claim 71 wherein the sleeve of lower melting polymer has a wall thickness of from about 0.05 to about 1.0 mm.

Claim 84

The device of claim 11 wherein the surface of the bone blocks further comprises a thin coating of osteo-conductive material.

Claim 85

An improved method for making an artificial ligament device adapted to replace a natural ligament extending between the ends of two bones, including the steps of: providing a plurality of warp yarns extending longitudinally of the ligament in both an end region and a bend region of the ligament; weaving a fill yarn into the warp yarns in a density dependent upon the number of picks per inch; controlling the weave to provide a particular number of picks per inch in the intra-articular region; reducing the number of picks per inch to not more than one-third the particular number during the weaving of the bend region; and molding a polymer bone block around the end region and a portion of the bend region so as to fixedly encase said regions and provide a fixed bend radius for the bend region at the point of exit from the bone block.

Claim 86

An improved method for making an artificial ligament device adapted to replace a natural ligament extending between the ends of two bones, including the steps of: providing a plurality of warp yarns extending longitudinally of the ligament in both an end region and a bend region of the ligament; weaving a fill yarn into the warp yarns in a density dependent upon the number of picks per inch; controlling the weave to provide a particular number of picks per inch in the intra-articular region; reducing the number of picks per inch to not more than one-third the particular number during the weaving of the bend region; and molding a polymer bone block around the end region and a portion of the bend region so as to fixedly encase said regions and provide a fixed bend radius for the bend region at the point of exit from the bone block.

Claim 87

The method of claim 80 further comprising the steps of (1) heatsetting the ligament to provide a substantial crimp in the warp yarn in the intra-articular region while leaving the warp yarn in the remainder of the ligament substantially uncrimped and (2) thermomolding a thin polymer sleeve around the portion of the ligament extending from the bone block.

Claim 88

The method of claim 81 wherein the warp yarns used in the weaving steps are formed from commingled higher melting and thermoplastic, lower melting fibers and the bone block is formed from a thermoplastic, lower melting polymer wherein during the molding step the lower melting polymers are heated sufficiently to cause the warp yarns to reform into a composite, having a higher melting polymer core with a substantially continuous covering of a thermoplastic lower melting polymer and to cause the bone block to be thermomolded to the ligament.

Claim 89

The method of claim 81 wherein the bone block is formed from a thermoset resin and wherein during the molding step the resin flows into the interstices in the weave of the end and bend regions of the ligament and is thermoset therein.