Process for the production of a tempered or bent glass plate with a rear coating, glass plate produced according to the same and the use thereof
Assignee: Pilkington Deutschland AG
•
Filing: 1990-01-26
•
Granted: 1991-02-12
•
Expires: 2010-01-26
Abstract
Abstract Process for the production of a tempered or bent glass plate provided with a transmission-reducing coating, in which to one side of the glass plate is applied at least one metal coating with a preponderant content of at least one metal or a metal alloy from elements of numbers 22 to 28 of the Periodic System of elements and to the latter is applied a metal-containing protective coating and subsequently a thermal tempering or bending process is performed in air at a temperature between approximately 580 DEG C. and 680 DEG C. and in which the thickness and material of the protective coating are selected in such a way that during the tempering or bending process there is no significant oxygen diffusion to the metal coating, characterized in that in the case of a rear arrangement of the reflecting metal coating made opaque through an adequate thickness, the protective coating is formed by an alloy of Al with Ti and/or Zr, the glass plate produced according the same and the use thereof.
Inventors
- 👤 Heinz W. Holscher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:29
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3618; B; B60; B60R; B60R1/00; B60R1/02; B60R1/08; B60R1/083; C03C17/3642; C03C17/3652; C03C17/3657; C03C17/366; C03C17/3663; C03C17/3681; C03C17/40; E; E04; E04F; E04F13/00; E04F13/07; E04F13/08; E04F13/14; E04F13/145; C03C2217/00; C03C2217/70; C03C2217/78; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
151 words
A process for the production of a tempered or bent glass plate provided with a reflective coating, comprising the steps of: applying to the rear side of the glass plate at least one opaque metal layer with a preponderant content of at least one metal or a metal alloy from elements of numbers 22 to 28 of the Periodic System of elements; applying to said at least one metal layer a protective layer; thermal tempering or bending said coated glass plate in air at a temperature between approximately 580° C. and 680° C., wherein the thickness and material content of said protective layer are selected such that during the tempering or bending step there is no significant oxygen diffusion to said at least one metal layer, and wherein said protective layer is formed by an alloy of Al with Ti and/or Zr with the content thereof at least 10 atomic %.
Claim 2
Dependent Claim
151 words
A process for the production of a tempered or bent glass plate provided with a reflective coating, comprising the steps of: applying to the rear side of the glass plate at least one opaque metal layer with a preponderant content of at least one metal or a metal alloy from elements of numbers 22 to 28 of the Periodic System of elements; applying to said at least one metal layer a protective layer; thermal tempering or bending said coated glass plate in air at a temperature between approximately 580° C. and 680° C., wherein the thickness and material content of said protective layer are selected such that during the tempering or bending step there is no significant oxygen diffusion to said at least one metal layer, and wherein said protective layer is formed by an alloy of Al with Ti and/or Zr with the content thereof at least 10 atomic %.
Claim 3
Dependent Claim
21 words
Process according to claim 1, wherein the protective layer has a Ti and/or Zr content of at least 20 atomic %.
Claim 4
Dependent Claim
28 words
Process according to claim 1, wherein the protective layer comprises an AltI alloy without a Zr content, and has a Ti content of 30 to 50 atomic %.
Claim 5
Dependent Claim
18 words
Process according to claim 3, wherein the protective layer has a Ti content of approximately 40 atomic %.
Claim 6
Dependent Claim
28 words
Process according to claim 1, wherein the protective layer comprises an AlZr alloy without a Ti content, and has a Zr content of 25 to 45 atomic %.
Claim 7
Dependent Claim
18 words
Process according to claim 5, wherein the protective layer has a Zr content of approximately 35 atomic %.
Claim 8
Dependent Claim
19 words
Process according to claim 1, wherein the protective layer is applied in a thickness of 10 to 50 nm.
Claim 9
Dependent Claim
19 words
Process according to claim 7, wherein the protective layer is applied in a thickness of 20 to 30 nm.
Claim 10
Dependent Claim
53 words
Process according to claim 1, further comprising the step of, prior to the application of the metal layer, applying to the glass carrier an adhesive layer of at least one of the metal oxides from the group consisting of TiO 2 , Ta 2 O 5 , ZrO 2 and SiO 2 .
Claim 11
Dependent Claim
23 words
Process according to claim 9, wherein the adhesive layer is applied in sufficient thickness that said adhesive layer acts as colour-modifying interference layer.
Claim 12
Dependent Claim
27 words
Process according to claim 1, wherein said step of applying at least one of the layers comprises a magnetron cathodic sputtering of said at leas one layer.
Claim 13
Dependent Claim
29 words
Process according to claim 11, wherein the protective layer is applied by simultaneous or alternating sputtering of two cathodes with an Al target and a Ti and/or Zr target.
Claim 14
Dependent Claim
24 words
Process according to claim 11, wherein the protective layer is applied by sputtering a melt or powder-metallurgically produced alloying target with a corresponding composition.
Claim 15
Dependent Claim
17 words
Glass plate with a rear, opaque and reflecting coating produced according to the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-11 | 1994-08-13 | 1995-02-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-11 | 1998-08-13 | 1999-02-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-11 | 2002-08-13 | 2003-02-12 | $7700.00 | Window Closed / Lapsed |