Pre-swelling and etching of plastics for plating
Assignee: JP Laboratories Inc
•
Filing: 1988-11-07
•
Granted: 1990-07-17
•
Expires: 2008-11-07
Abstract
Abstract Formulations are provided for pre-swelling and etching of functionalized polymers, such as polycarbonate in one, two and three steps. The etched surface can then be plated with electroless nickel or copper with satisfactory adhesion of the plated metals. Swelling agents make polymer molecules on and near the surface of the polymer easily accessible to a degradation agent. A degradation agent degradates the polymer molecules. If required, a solubilizing agent increases the miscibility of the degradation agent and the swelling agent. A wetting agent increases the effectiveness of the etching agent. In the one-step process, polymer parts are dipped in a solution containing at least one swelling agent and at least one degradation agent. In the two-step process, polymer parts are first treated with a solution of a swelling agent followed by etching with a solution of degradation agent. In the three-step process, polymer parts are first micro-roughened with a solution of a swelling agent, then etched with a solution of mineral acids followed by dipping in a caustic bath to make the surface wettable.
Inventors
- 👤 Gordhanbhai N. Patel
- 👤 Durgadas Bolikal
- 👤 Richard A. Bellemare
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:08
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
216 words
A process of two step surface etching of polymeric materials made of polymers having at least one hydrolyzable functionallty selected from the group consisting of polycarbonates, anhydrides, carboxyl esters, sulphonic esters, amides and urethanes, which comprises the first step of exposing the surface to be etched to a liquid phase capable of microroughening said surface, comprising a good solvent for said polymer and a non-solvent for said polymer provided that where at least one member of the group of said good and said non solvents etchant is immiscible with the other, said liquid phase further comprises a sufficient amount of solubilizing agent miscible with said immiscible components to provide a single liquid phase and a second step of hydrolyzing the said functionalities on said surface to the extent needed to provide a water wettable surface capable of being plated with electroless nickel or electroless copper to provide a plated layer having a strong level of adhesion to said surface by treating said surface with an etchant selected from the group consisting of acidic etchants selected from the group consisting of aqueous mineral acids free of metallic components, benzene sulphonic acid and mixtures thereof and basic etchants selected from the group consisting of alkali metal hydroxides, quaternary ammonium hydroxides and mixtures thereof in the presence of triethanolamine.
Claim 2
Dependent Claim
216 words
A process of two step surface etching of polymeric materials made of polymers having at least one hydrolyzable functionallty selected from the group consisting of polycarbonates, anhydrides, carboxyl esters, sulphonic esters, amides and urethanes, which comprises the first step of exposing the surface to be etched to a liquid phase capable of microroughening said surface, comprising a good solvent for said polymer and a non-solvent for said polymer provided that where at least one member of the group of said good and said non solvents etchant is immiscible with the other, said liquid phase further comprises a sufficient amount of solubilizing agent miscible with said immiscible components to provide a single liquid phase and a second step of hydrolyzing the said functionalities on said surface to the extent needed to provide a water wettable surface capable of being plated with electroless nickel or electroless copper to provide a plated layer having a strong level of adhesion to said surface by treating said surface with an etchant selected from the group consisting of acidic etchants selected from the group consisting of aqueous mineral acids free of metallic components, benzene sulphonic acid and mixtures thereof and basic etchants selected from the group consisting of alkali metal hydroxides, quaternary ammonium hydroxides and mixtures thereof in the presence of triethanolamine.
Claim 3
Dependent Claim
11 words
A process of claim 1, wherein the polymer is a polycarbonate.
Claim 4
Dependent Claim
13 words
A process of claim 1, wherein the liquid phase comprises benzene sulphonic acid.
Claim 5
Dependent Claim
28 words
A process of claim 1, wherein the good solvent is selected from the group consisting of mono- or di-lower alkyl ethers of mono-, di- or tri-lower alkylene glycols.
Claim 6
Dependent Claim
28 words
A process of claim 4, wherein the good solvent is selected from the group consisting of mono- or di-methyl or ethyl ethers of mono-, di- or tri-ethylene glycol.
Claim 7
Dependent Claim
22 words
A process of claim 1, wherein the non-solvent is selected from the group consisting of water, lower alkylene glycols and lower alkanols.
Claim 8
Dependent Claim
28 words
A process of claim 1, wherein the solubilizing agent is selected from the group consisting of lower alkanoic acids, lower alkylene glycols, lower alkanols and benzene sulphonic acid.
Claim 9
Dependent Claim
20 words
A process of claim 1, wherein the etchant is a basic etchant consisting essentially of triethanolamine and aqueous sodium hydroxide.
Claim 10
Dependent Claim
28 words
A process of claim 8, wherein the concentration of the triethanolamine is between 30 and 80% w/w of the etchant and the sodium hydroxide is 0.5 to 1.5N.
Claim 11
Dependent Claim
15 words
A process of claim 9, wherein the reaction temperature is between 150° and 170° F.
Claim 12
Dependent Claim
11 words
A process of claim 10, wherein the polymer is a polycarbonate.
References Cited (Backward Citations)
US3660293A
Cited
US3671289A
Cited
US3649391A
Cited
US3758332A
Cited
US3795622A
Cited
US4125649A
Cited
US4042730A
Cited
US4131698A
Cited
US4335164A
Cited
US4281034A
Cited
EP0052968A2
Cited
US4592929A
Cited
WO1987000391A1
Cited
US4832799A
Cited
US4803097A
Cited
US4775557A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-16 | 1994-01-15 | 1994-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-16 | 1998-01-15 | 1998-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-16 | 2002-01-15 | 2002-07-17 | $7700.00 | Window Closed / Lapsed |