Heat-resistant, wear-resistant, and high-strength aluminum alloy powder and body shaped therefrom
Assignee: Riken Corp
•
Filing: 1988-10-18
•
Granted: 1990-07-03
•
Expires: 2008-10-18
Abstract
Abstract The present invention relates to an aluminum alloy powder. Aluminum alloy powder having a high Si content is known but its heat resistance, wear resistance, and strength are poor. The aluminum alloy powder according to the present invention is characterized in that it contains from approximately 10.0% to approximately 30.0% of silicon and at least one element selected from the group consisting of from approximately 5.0% to approximately 15.0% of nickel, from approximately 3.0% to approximately 15.0% of iron, and from approximately 5.0% to approximately 15.0% of manganese, the silicon crystals in the aluminum alloy powder being 15 mu m or less in size. Due to the high content of nickel, iron, and manganese, the matrix is hardened and strengthed by the presence of finely dispersed intermetallic compounds and the silicon crystals, and thereby the high-temperature characteristics are improved. The shaped body, e.g., a hot-extruded shaped body, according to the present invention comprises an aluminum alloy having the above composition powder of the present invention and preferably a solid lubricant, the silicon crystals in the shaped body being 15 mu m or less in size, and the intermetallic compounds 20 mu m or less in size being finely distributed in the shaped body. The high-temperature characteristics of the shaped body are very excellent, thereby enabling it to be used as a cylinder liner which is inserted into an aluminum cylinder block body by casting the body.
Inventors
- 👤 Fumio Kiyota
- 👤 Tatsuo Fujita
- 👤 Tadao Hirano
- 👤 Shin'ichi Horie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:50
CPC Classifications
F; F02; F02F; F02F7/00; F02F7/0085; B; B22; B22F; B22F3/00; B22F3/20; C; C22; C22C; C22C1/00; C22C1/04; C22C1/0408; C22C1/0416; F02F1/00; F02F1/004; F05; F05C; F05C2251/00; F05C2251/04; F05C2251/042
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
117 words
A heat-resistant, wear resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 5.9% by weight to 15.0% by weight iron, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of iron, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 2
Dependent Claim
117 words
A heat-resistant, wear resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 5.9% by weight to 15.0% by weight iron, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of iron, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 3
Dependent Claim
115 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 7.1% by weight to 15.0% by weight manganese, and at least one of 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of manganese, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 4
Dependent Claim
115 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 7.1% by weight to 15.0% by weight manganese, and at least one of 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of manganese, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 5
Dependent Claim
116 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 7.7% by weight to 15.0% by weight nickel, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of nickel, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 6
Dependent Claim
116 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt and which consists essentially of from 15.0% by weight to 25% by weight silicon, from 7.7% by weight to 15.0% by weight nickel, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of nickel, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 7
Dependent Claim
144 words
A heat-resistant, wear-resistant, and high strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, manganese and one of 4.1% or more of nickel or 4.5% or more of iron, wherein the total amount of the manganese and nickel or iron is less than 15.0% by weight, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of manganese and nickel or iron, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 8
Dependent Claim
144 words
A heat-resistant, wear-resistant, and high strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, manganese and one of 4.1% or more of nickel or 4.5% or more of iron, wherein the total amount of the manganese and nickel or iron is less than 15.0% by weight, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of manganese and nickel or iron, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 9
Dependent Claim
128 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, iron and 5.1% by weight or more of nickel, wherein the total amount of nickel and iron is 15.0% by weight or less, and at least one of from 0.5% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of iron and nickel, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 10
Dependent Claim
128 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder which is formed by pulverizing and solidifying a melt, and which consists essentially of from 15.0% by weight to 25% by weight silicon, iron and 5.1% by weight or more of nickel, wherein the total amount of nickel and iron is 15.0% by weight or less, and at least one of from 0.5% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of iron and nickel, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 11
Dependent Claim
122 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder is formed by pulverizing and solidifying a melt and which consists essentially of from 15% by weight to 25% by weight silicon, and 6 to 15% total of all three of nickel, iron, and manganese, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of nickel, iron, and manganese, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 12
Dependent Claim
122 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder is formed by pulverizing and solidifying a melt and which consists essentially of from 15% by weight to 25% by weight silicon, and 6 to 15% total of all three of nickel, iron, and manganese, and at least one of from 0.5% by weight to 5.0% by weight of copper and from 0.2% by weight to 3.0% by weight of magnesium, and comprising silicon crystals and intermetallic compounds of nickel, iron, and manganese, wherein the silicon crystals in said aluminum alloy powder are 15 μm or less in size and said intermetallic compounds are finely dividable acicular crystals that are 20 μm or less in size, in a plastic deforming process of said powder.
Claim 13
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 1, wherein the particles are 0.5 mm or less in diameter.
Claim 14
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 2, wherein the particles are 0.5 mm or less in diameter.
Claim 15
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 3, wherein the particles are 0.5 mm or less in diameter.
Claim 16
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 4, wherein the particles are 0.5 mm or less in diameter.
Claim 17
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 5, wherein the particles are 0.5 mm or less in diameter.
Claim 18
Dependent Claim
22 words
A heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 6, wherein the particles are 0.5 mm or less in diameter.
Claim 19
Dependent Claim
63 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 1, wherein the iron forms intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 20
Dependent Claim
63 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 2, wherein the manganese forms intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 21
Dependent Claim
63 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 3, wherein the nickel forms intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 22
Dependent Claim
68 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 4, wherein the manganese and the nickel or iron form intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 23
Dependent Claim
66 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 5, wherein the iron and the nickel form intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 24
Dependent Claim
66 words
A shaped body of the heat-resistant, wear-resistant, and high-strength aluminum alloy powder according to claim 6, wherein the nickel, iron, and manganese form intermetallic compounds that are 20 μm or less in size and are finely distributed in said shaped body, and said shaped body has a scuff resistance higher than A 390 and a tensile strength of 24 kg/mm 2 or more at 200° C.
Claim 25
Dependent Claim
35 words
A shaped body according to claim 13, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 26
Dependent Claim
35 words
A shaped body according to claim 14, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 27
Dependent Claim
35 words
A shaped body according to claim 15, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 28
Dependent Claim
35 words
A shaped body according to claim 16, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 29
Dependent Claim
35 words
A shaped body according to claim 17, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 30
Dependent Claim
35 words
A shaped body according to claim 18, which contains from 0.2% by weight to 5.0% by weight of at least one solid lubricant selected from the group consisting of graphite, molybdenum disulphide, and boron nitride.
Claim 31
Dependent Claim
39 words
A shaped body according to claim 13, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
Claim 32
Dependent Claim
39 words
A shaped body according to claim 14, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
Claim 33
Dependent Claim
39 words
A shaped body according to claim 15, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
Claim 34
Dependent Claim
39 words
A shaped body according to claim 16, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
Claim 35
Dependent Claim
39 words
A shaped body according to claim 17, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
Claim 36
Dependent Claim
39 words
A shaped body according to claim 18, wherein the majority of the intermetallic compound acicular crystals are 5 μm or less in size and the remainder of the intermetallic compound acicular crystals are 20 μm or less in size.
References Cited (Backward Citations)
US3325279A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-02 | 1994-01-01 | 1994-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-02 | 1998-01-01 | 1998-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-02 | 2002-01-01 | 2002-07-03 | $7700.00 | Window Closed / Lapsed |