Planarized multilevel interconnection for integrated circuits
Assignee: Leland Stanford Junior University
•
Filing: 1988-12-13
•
Granted: 1989-12-19
•
Expires: 2008-12-13
Abstract
Abstract A process sequence for forming a multilevel tungsten interconnect array begins from a device level already planarized; alternate layers of silicon nitride and oxide are deposited. Via holes are then defined by masking, and anisotropically etched entirely through the nitride and oxide layers down to the device level (by reactive ion etching). Then the trenches for metal lines are defined intermediate the via holes and selectively plasma etched through the topmost layer of nitride and the topmost layer of dielectric, stopping atop the second layer of nitride. The oxide sidewalls of the metal line trenches and via holes are then etched laterally, using a wet etching process that results in much slower etching of the nitride layer so that nitride overhangs are formed that will protect the oxide sidewalls during subsequent vertical etchings. A layer of polysilicon is then deposited conformally which also covers the interior surface of each metal line trench and via hole, and an anisotropic etch performed so that the excess polysilicon is etched off from the top of the dielectric layer and the bottom of the trench is again open to the nitride surface and the bottom of the via hole is open to the device layer. Now the tungsten is deposited selectively, which will grow laterally in the trenches and via holes, filling them by lateral deposition after which processing is completed by a final annealing process to consume the excess polysilicon by tungsten.
Inventors
- 👤 Mehrdad M. Moslehi
- 👤 Krishna C. Saraswat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:17
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/076; H10W20/031; H10W20/056; H10W20/057; H10W20/064; H10W20/066; H10W20/081
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
190 words
A method of forming a tungsten interconnection array for an integrated circuit comprising the steps of on a device level of said integrated circuit which is already planarized, forming a thin first layer of nitride covered by a thick first layer of oxide, forming a second layer of nitride over said first oxide, forming a thick second layer of oxide over said second layer of nitride, forming a thin third layer of nitride over said second layer of oxide, defining the location of via holes which are to extend through said first and second layers of oxide and said first, second and third layers of nitride by etching said third nitride layer to define the location of metal lines, anisotropically etching said second oxide layer, said second etching nitride layer and said first oxide layer to create oxide trenches with substantially vertical sidewalls defining said via holes, etching through said nitride layer to open said holes to the underlying planarized device, depositing tungsten in said via holes to fill said via holes to the level of the third nitride and form a planarized surface having a complete level of metallization.
Claim 2
Independent Claim
190 words
A method of forming a tungsten interconnection array for an integrated circuit comprising the steps of on a device level of said integrated circuit which is already planarized, forming a thin first layer of nitride covered by a thick first layer of oxide, forming a second layer of nitride over said first oxide, forming a thick second layer of oxide over said second layer of nitride, forming a thin third layer of nitride over said second layer of oxide, defining the location of via holes which are to extend through said first and second layers of oxide and said first, second and third layers of nitride by etching said third nitride layer to define the location of metal lines, anisotropically etching said second oxide layer, said second etching nitride layer and said first oxide layer to create oxide trenches with substantially vertical sidewalls defining said via holes, etching through said nitride layer to open said holes to the underlying planarized device, depositing tungsten in said via holes to fill said via holes to the level of the third nitride and form a planarized surface having a complete level of metallization.
Claim 3
Dependent Claim
62 words
A method as in claim 1 further including following said anisotropic etch of said oxide layers the steps of defining the positions of metal lines trenches over said device, and etching said third layer of nitride and said second layer of oxide stopping at said second layer of nitride to define said metal line trenches with substantially vertical sidewalls in said oxide.
Claim 4
Dependent Claim
51 words
A method as in claim 2 including the step following anisotropic etching of said oxide layer of etching the vertical sidewalls of said trenches and said via holes to recess said sidewalls and establish nitride overhangs which protect the sidewalls and cooperate with the tungsten to form a stable enclosed structure.
Claim 5
Dependent Claim
17 words
A method as in claim 3 wherein the planarized device level is a silicon integrated circuit substrate.
Claim 6
Dependent Claim
23 words
A method as in claim 4 wherein said anisotropic etching is carried out using reactive ion etching using RF or ECR microwave plasma.
Claim 7
Dependent Claim
55 words
A method as in claim 3 including the further steps following the steps of etching said sidewalls of depositing a layer of polysilicon over the exposed surface areas including said trench and said via holes, and anisotropically etching said polysilicon so that it covers only said vertical sidewalls of said trench and said via holes.
Claim 8
Dependent Claim
28 words
A method as in claim 6 wherein said oxide is in the range of 5000 Å to 10,000 Å, and said nitride layers are each about 800 Å.
Claim 9
Dependent Claim
16 words
A method as in claim 7 wherein said polysilicon has a thickness of about 400 Å.
Claim 10
Dependent Claim
26 words
A method as in claim 6 wherein said tungsten is deposited by selective chemical-vapor deposition, filling the trenches by lateral deposition of tungsten followed by annealing.
Claim 11
Dependent Claim
39 words
A method as in claim 9 including the step of etching said second nitride layer with a slight slope so that said via hole extending through said first oxide is narrower than the via hole through said second oxide.
Claim 12
Independent Claim
121 words
A method of forming a tungsten interconnection array for an integrated circuit comprising the steps of on a device level of said integrated circuit which is already planarized, forming a thin first layer of nitride covered by a thick first layer of oxide, forming a second layer of nitride over said oxide, etching said second nitride layer to defining the location of metal lines, anisotropically etching said oxide layer to create oxide trenches with substantially vertical sidewalls defining said metal lines, etching through said nitride layer to open said trenches to the underlying planarized device, depositing tungsten in said trenches to fill said trenches to the level of the nitride and form a planarized surface having a complete level of metallization.
Claim 13
Independent Claim
121 words
A method of forming a tungsten interconnection array for an integrated circuit comprising the steps of on a device level of said integrated circuit which is already planarized, forming a thin first layer of nitride covered by a thick first layer of oxide, forming a second layer of nitride over said oxide, etching said second nitride layer to defining the location of metal lines, anisotropically etching said oxide layer to create oxide trenches with substantially vertical sidewalls defining said metal lines, etching through said nitride layer to open said trenches to the underlying planarized device, depositing tungsten in said trenches to fill said trenches to the level of the nitride and form a planarized surface having a complete level of metallization.
Claim 14
Dependent Claim
46 words
A method as in claim 10 including the step following anisotropic etching of said oxide layer of etching the vertical sidewalls of said trenches to recess said sidewalls and establish nitride overhangs which protect the sidewalls and cooperate with the tungsten to form a stable structure.
Claim 15
Dependent Claim
17 words
A method as in claim 12 wherein the planarized device level is a silicon integrated circuit substrate.
Claim 16
Dependent Claim
23 words
A method as in claim 13 wherein said anisotropic etching is carried out using reactive ion etching in RF or ECR microwave plasma.
Claim 17
Dependent Claim
47 words
A method as in claim 14 including the further steps following the steps of etching said sidewalls of depositing a layer of polysilicon over the exposed surface area of said trench, and anisotropically etching said polysilicon so that it covers only said vertical sidewalls of said trench.
Claim 18
Dependent Claim
28 words
A method as in claim 15 wherein said oxide is in the range of 5000 Å to 10,000 Å, and said nitride layers are each about 800 Å.
Claim 19
Dependent Claim
16 words
A method as in claim 16 wherein said polysilicon has a thickness of about 400 Å.
Claim 20
Dependent Claim
39 words
A method as in claim 14 wherein said tungsten is deposited by selective chemical-vapor deposition, filling the trenches by lateral deposition of tungsten followed by annealing to consume the excess silicon left on the trench and via hole sidewalls.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-18 | 1993-06-19 | 1993-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-18 | 1997-06-19 | 1997-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-18 | 2001-06-19 | 2001-12-19 | $7700.00 | Window Closed / Lapsed |