Rubber containing aramid pulp reinforcement

Claim 2

A process for preparing a vulcanized elastomer composite which comprises: (a) forming a premix consisting essentially of fibrillated aramid fibers and one or more particulate reinforcing agents selected from the group consisting of carbon black, silica and clay, said premix containing the entire quantity of aramid fibers desired in said composite and sufficient quantity of said reinforcing agent to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomers, said aramid fibers being composed of (1) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.02 millimeters and an aspect ratio greater than about 100, and (2) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to about 20 square meters per gram, (b), mixing said premix with a vulcanizable elastomeric matric material, additional amounts of said one or more particulate reinforcing agents and additional tire compounding ingredients in the absence of a solvent to form an unvulcanized elastomer composition, the quantity of said aramid fibers in said composition not exceeding 5 parts by weight per 100 of elastomer, and (c) curing the resulting composition.

Claim 3

A tire having a tread comprised of an aramid fiber-reinforced elastomeric composite prepared according to the process of claim 1 where the amount of aramid fiber is from about 0.2 to about 5 parts per 100 parts of elastomer in said composite.

Claim 4

A process according to claim 1 in which said vulcanized elastomer composite or a portion thereof forms a tire tread.

Claim 5

A process according to claim 1 further including the additional step of forming the unvulcanized elastomer composite prepared in step (b) into a tire tread, and thereafter curing said composite.

Claim 6

A process for building a tire containing one or more aramid-reinforced components including a tread, said process comprising: (a) forming a premix consisting essentially of fibrillated aramid fibers and one or more particulate reinforcing agents selected from the group consisting of carbon black, silicon, clay and mixtures thereof, said premix containing the entire quantity of aramid fibers desired in said composite and sufficient quantity of reinforcing agent to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, said aramid fibers being composed of (1) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.02 millimeters and an aspect ratio greater than about 100, and (2) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to about 20 square meters per gram, (b) mixing said premix with a vulcanizable elastomeric matric material, additional amounts of said one or more particulate reinforcing agents, and additional tire compounding ingredients in the absence of a solvent to form an unvulcanized elastomer composite, the quantity of said aramid fibers no exceeding 5 parts by weight per 100 of elastomer, and (c) forming the resulting unvulcanized elastomer composite or one or more portions thereof into one or more tire components, including a tread, in which aramid reinforcement is desired, (d) assembling said components into an uncured tire, and (e) curing the tire.

Claim 7

A process for building a tire containing one or more aramid-reinforced components including a tread, said process comprising: (a) forming a premix consisting essentially of fibrillated aramid fibers and one or more particulate reinforcing agents selected from the group consisting of carbon black, silicon, clay and mixtures thereof, said premix containing the entire quantity of aramid fibers desired in said composite and sufficient quantity of reinforcing agent to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, said aramid fibers being composed of (1) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.02 millimeters and an aspect ratio greater than about 100, and (2) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to about 20 square meters per gram, (b) mixing said premix with a vulcanizable elastomeric matric material, additional amounts of said one or more particulate reinforcing agents, and additional tire compounding ingredients in the absence of a solvent to form an unvulcanized elastomer composite, the quantity of said aramid fibers no exceeding 5 parts by weight per 100 of elastomer, and (c) forming the resulting unvulcanized elastomer composite or one or more portions thereof into one or more tire components, including a tread, in which aramid reinforcement is desired, (d) assembling said components into an uncured tire, and (e) curing the tire.

Claim 8

A process according to claim 5 in which the vulcanizable elastomeric matrix material is rubber.

Claim 9

A process according to claim 5 in which one of said tire components is the tread.

Claim 10

In a pneumatic tire comprising a plurality of components including a tire tread, a pair of sidewalls, a cord reinforced carcass, a pair of beads and one or more additional elastomeric structural reinforcing components, the improvement wherein at least one of said components comprises aramid fiber-reinforced vulcanized elastomeric composite comprising a matrix of cured elastomer, a reinforcing amount of a particulate reinforcing agent selected from the group consisting of carbon black, silica, clay and mixtures thereof, and an effective reinforcing amount not exceeding 5 parts by weight per 100 of elastomer, of short, discontinuous, fibrillated aramid fibers dispersed therein, said fibers being composed of (a) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.02 millimeters and an aspect ratio greater than about 100, and (b) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to about 20 square meters per gram, said composite being prepared by a process which comprises (1) forming a premix consisting essentially of all of said aramid fibers with at least a portion and less than all of said particulate reinforcing agent or mixture thereof, the quantity of said reinforcing agent or mixture thereof being sufficient to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, (2) mixing said premix with a vulcanizable elastomer, the remaining portion of said reinforcing agent or mixture thereof, and additional tire compounding ingredients and (3) curing the tire.

Claim 11

In a pneumatic tire comprising a plurality of components including a tire tread, a pair of sidewalls, a cord reinforced carcass, a pair of beads and one or more additional elastomeric structural reinforcing components, the improvement wherein at least one of said components comprises aramid fiber-reinforced vulcanized elastomeric composite comprising a matrix of cured elastomer, a reinforcing amount of a particulate reinforcing agent selected from the group consisting of carbon black, silica, clay and mixtures thereof, and an effective reinforcing amount not exceeding 5 parts by weight per 100 of elastomer, of short, discontinuous, fibrillated aramid fibers dispersed therein, said fibers being composed of (a) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.02 millimeters and an aspect ratio greater than about 100, and (b) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to about 20 square meters per gram, said composite being prepared by a process which comprises (1) forming a premix consisting essentially of all of said aramid fibers with at least a portion and less than all of said particulate reinforcing agent or mixture thereof, the quantity of said reinforcing agent or mixture thereof being sufficient to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, (2) mixing said premix with a vulcanizable elastomer, the remaining portion of said reinforcing agent or mixture thereof, and additional tire compounding ingredients and (3) curing the tire.

Claim 12

A tire according to claim 8 in which said tire includes a reinforcing belt between said carcass and said tread, said belt comprising at least one ply of said elastomeric composite.

Claim 13

A tire according to claim 9 in which said elastomeric composite further includes reinforcing cords extending therethrough.

Claim 14

A tire according to claim 8 in which said tire includes a belt overlay of said elastomeric composite.

Claim 15

A tire according to claim 8 in which said tire includes members of generally triangular cross section of said elastomeric composite extending radially outwardly from said beads.

Claim 16

A tire according to claim 8 in which said tire includes at least one toroidal member of generally triangular cross section of said elastomeric composite extending radially outwardly from said beads and diminishing in thickness as it extends outwardly.

Claim 17

A tire according to claim 8 in which the amount of said reinforcing agent or mixture thereof is from about 30 to about 100 parts by weight per 100 parts of said cured elastomer.

Claim 18

A tire according to claim 8 in which said reinforcing agent is carbon black.

Claim 19

A tire according to claim 8 in which said reinforcing agent is silica.

Claim 20

A tire according to claim 8 wherein said tread is a component thereof which comprises said aramid fiber-reinforced elastomeric composite and the amount of aramid fibers is in the range of 0.2 to 5 parts per 100 parts of elastomer in said composite.

Claim 21

A tire according to claim 15 wherein said aramid fiber-reinforced elastomeric composite is a tread thereof and the amount of aramid fiber is in the range of 0.2 to 5 parts per 100 parts of elastomer.

Claim 22

A tire according to claim 8 in which said cured elastomer is rubber.

Claim 23

A tire according to claim 8 in which reinforcing agent or mixture thereof and said additional tire compounding ingredients are conventional tire compounding ingredients and in which said mixing of said premix with said vulcanizable elastomer, said remaining portion of reinforcing agent or mixture thereof and said additional tire compounding ingredients is carried at in the substantial absence of additional materials.

Claim 24

A tire according to claim 8 in which said premix is mixed with said vulcanizable elastomer in the absence of a solvent.

Claim 25

A tire according to claim 8 in which the amount of aramid fibers is from 0.2 to 2 parts by weight, per 100 of elastomer.

Claim 26

A tire having a tread which comprises an aramid fiber-reinforced vulcanized elastomeric composite comprising a matrix of cured elastomer, a particulate reinforcing agent selected from the group consisting of carbon black, silica, clay and mixtures thereof, additional tire compounding ingredients and about 0.2 to about 5 parts by weight, per 100 parts of said elastomer, of short, discontinuous fibrillated aramid fibers being composed of (i) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.2 millimeters and an aspect ratio greater than about 100, and (ii) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to 20 square meters per gram, said composite being prepared by a process which comprises (1) forming a premix consisting essentially of all of said particulate reinforcing agent or mixture thereof being sufficient to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, (2) mixing said premix with a vulcanizable elastomer, the remaining portion of said reinforcing agent or mixture thereof, and said additional tire compounding ingredients and (3) curing the tire.

Claim 27

A tire having a tread which comprises an aramid fiber-reinforced vulcanized elastomeric composite comprising a matrix of cured elastomer, a particulate reinforcing agent selected from the group consisting of carbon black, silica, clay and mixtures thereof, additional tire compounding ingredients and about 0.2 to about 5 parts by weight, per 100 parts of said elastomer, of short, discontinuous fibrillated aramid fibers being composed of (i) a trunk portion having a length in the range of about 0.2 to about 5 millimeters, a diameter in the range of about 0.005 to about 0.2 millimeters and an aspect ratio greater than about 100, and (ii) a plurality of fibrils extending outwardly from said trunk and having diameters substantially smaller than the diameter of the trunk from which they extend, said fibers having a surface area in the range of about 4 to 20 square meters per gram, said composite being prepared by a process which comprises (1) forming a premix consisting essentially of all of said particulate reinforcing agent or mixture thereof being sufficient to cause partitioning of said aramid fibers and thereby promote subsequent compounding of said aramid fibers with elastomer, (2) mixing said premix with a vulcanizable elastomer, the remaining portion of said reinforcing agent or mixture thereof, and said additional tire compounding ingredients and (3) curing the tire.

Claim 28

The tire of claim 23 wherein said reinforcing agent is comprised of carbon black and where said aramid fibers are mixed with at least a portion of said reinforcing agent prior to mixing with said elastomer and the vulcanization thereof.

Claim 29

The tire of claim 23 in which the amount of said aramid fibers is from 0.2 to 2 parts by weight, per 100 parts of rubber.