US4659754A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dispersions of fibres in rubber
Assignee: Polysar Ltd
•
Filing: 1985-11-18
•
Granted: 1987-04-21
•
Expires: 2005-11-18
Abstract
Abstract Polymer-fibre mixtures with improved homogeniety of dispersion of fibres throughout the polymer matrix are prepared from fibres prior mixed or coated with a plasticizer which is compatible with both the fibre and the polymer matrix. Then the plasticizer-fibre combination can be mixed into the polymer matrix, using standard polymer mixing equipment and for reasonable lengths of time, to produce a mixture in which agglomerations of fibres are very materially reduced. A preferred fibre is a fibrillated aramid fibre, dispersion of which in polymers has previously caused particular difficulties. Suitable polymers include hydrocarbon elastomers such as SBR, for use with which an aromatic mineral oil is a preferred plasticizer, and oil-resistant NBR elastomers, for use with which an ester plasticizer such as dioctyl phthalate is preferred.
Inventors
- 👤 Douglas C. Edwards
- 👤 James A. Crossman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:05
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/22; C08J3/18
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
97 words
A plasticized fibre composition useful for reinforcing polymers, said composition comprising 100 parts by weight of fibrillated fibres selected from the group consisting of cellulose, glass fibres, asbestos, mineral wool, rayon, nylon, polyester, polypropylene and polymeric paraphenylene terephthalamide, and mixtures of two or more of said types of said types of fibres, and from about 80 to about 125 parts by weight of a plasticiser that is liquid at processing temperatures, said plasticizer being compatible with the chosen fibre or fibres and substantially homogeneously dispersed thereon so as effectively to wet the fibre surfaces with the plasticizer.
Claim 2
Dependent Claim
97 words
A plasticized fibre composition useful for reinforcing polymers, said composition comprising 100 parts by weight of fibrillated fibres selected from the group consisting of cellulose, glass fibres, asbestos, mineral wool, rayon, nylon, polyester, polypropylene and polymeric paraphenylene terephthalamide, and mixtures of two or more of said types of said types of fibres, and from about 80 to about 125 parts by weight of a plasticiser that is liquid at processing temperatures, said plasticizer being compatible with the chosen fibre or fibres and substantially homogeneously dispersed thereon so as effectively to wet the fibre surfaces with the plasticizer.
Claim 3
Dependent Claim
26 words
The composition of claim 1 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area greater than 1 m 2 /g.
Claim 4
Dependent Claim
51 words
The composition of claim 1 wherein the plasticizer is selected from hydrocarbon and mineral oils, low molecular weight polymers, esters of carboxylic acids, phosphoric acid esters, low molecular weight synthetic resins having melting points below about 150° C., liquid polyethers, liquid polyether/polythioethers, chlorinated paraffins, natural oils and resins and their derivatives.
Claim 5
Dependent Claim
20 words
The composition of claim 3 wherein the plasticizer is a hydrocarbon oil selected from the paraffinic, naphthenic and aromatic oils.
Claim 6
Dependent Claim
31 words
The composition of claim 3 wherein the plasticizer is an ester of a carboxyalic acid selected from dibutoxyethyl adipate, dibutyl phthalate, dioctyl phthalate, dioctyl sebacate, butyl oleate and triethylene glycol dibenzoate.
Claim 7
Dependent Claim
16 words
The composition of claim 3 wherein the plasticizer is selected from a polyether and a polyether/polythioether.
Claim 8
Dependent Claim
16 words
The composition of claim 1 wherein the fibre is selected from rayon, nylon, polyester and polypropylene.
Claim 9
Dependent Claim
18 words
The composition of claim 1 wherein the fibre is selected from cellulose, glass fibres, asbestos and mineral wool.
Claim 10
Dependent Claim
124 words
A process for preparing mixtures of polymers and fibrous material, which comprises: forming a substantially plasticized fibrous material composition by treating 100 parts by weight of fibre selected from the group consisting of cellulose, glass fibres, asbestos, mineral wool, rayon, nylon, polyester, polypropylene and polymeric paraphenylene terephthalamide and mixtures of two or more of said types of fibre with from about 80 to about 125 parts by weight of a plasticizer that is liquid at processing temperatures, and mixing the plasticized fibrous material composition with a polymer selected from natural rubber and synthetic elastomeric or thermoplastic polymeric material, said plasticizer being compatible with the chosen fibrillated fibre or fibres and substantially homogeneously dispersed thereon so as effectively to wet the fibre surfaces with plasticizer.
Claim 11
Dependent Claim
124 words
A process for preparing mixtures of polymers and fibrous material, which comprises: forming a substantially plasticized fibrous material composition by treating 100 parts by weight of fibre selected from the group consisting of cellulose, glass fibres, asbestos, mineral wool, rayon, nylon, polyester, polypropylene and polymeric paraphenylene terephthalamide and mixtures of two or more of said types of fibre with from about 80 to about 125 parts by weight of a plasticizer that is liquid at processing temperatures, and mixing the plasticized fibrous material composition with a polymer selected from natural rubber and synthetic elastomeric or thermoplastic polymeric material, said plasticizer being compatible with the chosen fibrillated fibre or fibres and substantially homogeneously dispersed thereon so as effectively to wet the fibre surfaces with plasticizer.
Claim 12
Dependent Claim
19 words
The process according to claim 9 wherein the polymer is selected from natural rubber and synthetic elastomeric polymeric materials.
Claim 13
Dependent Claim
15 words
The process of claim 9 wherein the polymer is selected from synthetic thermoplastic polymeric materials.
Claim 14
Dependent Claim
34 words
The process of claim 9 wherein the fibrous material is a fibrillated fibre used in an amount of from about 0.25 to about 100 parts by weight per 100 parts by weight of polymer.
Claim 15
Dependent Claim
24 words
The process of claim 9 wherein the fibre is a fibrillated synthetic organic fibre selected from rayon, nylon, polyester, polypropylene and polymeric paraphenylene terephthalamide.
Claim 16
Dependent Claim
21 words
The process of claim 9 wherein the fibre is a fibrillated fibre selected from cellulose, glass fibres, asbestos and mineral wool.
Claim 17
Dependent Claim
54 words
The process of claim 10 wherein the polymer is selected from natural rubber, styrene-butadiene copolymers, polyisoprene, butadiene-acrylonitrile copolymers, carboxylated styrene-butadiene polymers, carboxylated butadiene-acrylonitrile polymers, polymers comprising chloroprene, polymers comprising acrylic monomers, ethylene-propylene copolymers, polybutadiene, styrene-butadiene block copolymers, butyl rubber and halogenated butyl rubbers, EPDM rubbers and halogenated EPDM rubbers, silicone rubbers and chlorosulphonated polyethylene.
Claim 18
Dependent Claim
26 words
The process of claim 15 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area greater than 1 m 2 /g.
Claim 19
Dependent Claim
56 words
The process of claim 11 wherein the polymer is selected from polyethylene and the thermoplastic copolymers of ethylene, polypropylene and the thermoplastic copolymers of propylene, polystyrene and impact polystyrene, polybutene, polyvinyl chloride and the thermoplastic copolymers of vinyl chloride, polyvinylidene chloride and the thermoplastic copolymers of vinylidene chloride, styrene-acrylonitrile polymers, butadiene-styrene-acrylonitrile polymers, polyesters, polyamides and polycarbonates.
Claim 20
Dependent Claim
26 words
The process of claim 17 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area greater than 1 m 2 /g.
Claim 21
Dependent Claim
51 words
The process of claim 9 wherein the plasticizer is selected from hydrocarbon and mineral oils, low molecular weight polymers, esters of carboxylic acids, phosphoric acid esters, low molecular weight synthetic resins having melting points below about 150° C., liquid polyethers, liquid polyether/polythioethers, chlorinated paraffins, natural oils and resins and their derivatives.
Claim 22
Dependent Claim
53 words
The process of claim 9 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area of greater than 1 m 2 /g, the plasticizer is a hydrocarbon oil and the polymer is selected from natural rubber, styrene-butadiene copolymers, polybutadiene, butyl rubber, halogenated butyl rubber, ethylene-propylene copolymer, and EPDM.
Claim 23
Dependent Claim
53 words
The process of claim 9 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area of greater than 1 m 2 /g, the plasticizer is selected from C 4 -C 12 esters of dibasic organic acids, phosphate esters, polyethers and polyether/polythioethers and the polymer is a butadiene-acrylonitrile copolymer.
Claim 24
Dependent Claim
45 words
The process of claim 9 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area of greater than 1 m 2 /g, the plasticizer is a hydrocarbon oil and the polymer is selected from chlorosulphonated polyethylene, chlorobutyl, bromobutyl and polychloroprene.
Claim 25
Dependent Claim
39 words
The process of claim 9 wherein the fibre is an aramid fibre of polymeric paraphenylene terephthalamide having a surface area of greater than 1 m 2 /g, the plasticizer is silicone oil and the polymer is a silicone rubber.
References Cited (Backward Citations)
US3652380A
Cited
US3976608A
Cited
US4101050A
Cited
US4131592A
Cited
US4263184A
Cited
US4368283A
Cited
US4560718A
Cited
US4521553A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |