Porous heat-shrinkable tetrafluoroethylene polymer tube and process for producing the same
Assignee: Daikin Industries Ltd
•
Filing: 1987-05-28
•
Granted: 1989-05-16
•
Expires: 2007-05-28
Abstract
Abstract A tetrafluoroethylene polymer tube which is in a porous form composed of continuous pores and has heat-shrinkability in a radial direction or both radial direction and longitudinal direction of the tube, and a process for producing the same comprising applying pressure into inside of a tetrafluoroethylene polymer tube formed by paste extrusion molding a powder of the tetrafluoroethylene polymer and then sintered while heating the same to a temperature of not higher than the melting initiation temperature of the tetrafluoroethylene polymer to expand the tube to a radial direction only or both radial direction and longitudinal direction of the tube, and then cooling the tube in a pressurized state.
Inventors
- 👤 Katsutoshi Yamamoto
- 👤 Norimasa Honda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 07:02
CPC Classifications
F; F16; F16L; F16L9/00; F16L9/14; F16L9/147; B; B01; B01D; B01D39/00; B01D39/14; B01D39/16; B01D39/1692; B29; B29C; B29C49/00; B29C49/0005; B29C49/0006; B29C55/00; B29C55/22; B29C61/00; B29C61/06; B29C61/08; B29C67/00; B29C67/20; B29C67/205; F16L9/12; B29K; B29K2027/00; B29K2027/12; B29K2027/18; B29L; B29L2023/00
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
74 words
A porous heat shrinkable tube produced by the process comprising: paste-extrusion molding a powder of a tetrafluoroethylene polymer to form a tetrafluoroethylene polymer tube; sintering said tetrafluoroethylene polymer tube; applying pressure to the inside of said tetrafluoroethylene polymer tube and heating to a temperature not higher than the melting point of said tetrafluoroethylene polymer thereby expanding said tetrafluoroethylene polymer tube in the radial and longitudinal direction of said polymer tube, and cooling said tube.
Claim 2
Dependent Claim
74 words
A porous heat shrinkable tube produced by the process comprising: paste-extrusion molding a powder of a tetrafluoroethylene polymer to form a tetrafluoroethylene polymer tube; sintering said tetrafluoroethylene polymer tube; applying pressure to the inside of said tetrafluoroethylene polymer tube and heating to a temperature not higher than the melting point of said tetrafluoroethylene polymer thereby expanding said tetrafluoroethylene polymer tube in the radial and longitudinal direction of said polymer tube, and cooling said tube.
Claim 3
Dependent Claim
40 words
A porous, heat shrinkable tube produced by the process according to claim 1 comprising a tetrafluoroethylene polymer, said heat shrinkable tube having a porosity of from 10 to 80%, and a gas permeability of from 100 to 100,000 sec./100 c.c.
Claim 4
Dependent Claim
43 words
The porous, heat shrinkable tube produced by the process according to claim 1 wherein the said polymer tube is expanded at an expansion rate of from 1.5 to 5 times in said radial direction and up to 3 times in said longitudinal direction.
Claim 5
Dependent Claim
42 words
A porous heat shrinkable tube produced by the process as in claim 1, wherein said tetrafluoroethylene polymer contains at least one of perfluoroalkyl vinyl ether, chlorotrifluoroethylene, and hexafluoropropylene as a copolymerizable monomer in an amount of not more than 2% by weight.
Claim 6
Dependent Claim
20 words
The product produced by the process according to claim 1 wherein said sintering occurs at a temperature of 360° C.
References Cited (Backward Citations)
US4110392A
Cited
US4332035A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-15 | 1992-11-14 | 1993-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-15 | 1996-11-14 | 1997-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-15 | 2000-11-14 | 2001-05-16 | $7700.00 | Window Closed / Lapsed |