Method of forming a carbide layer
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1986-09-30
•
Granted: 1987-08-11
•
Expires: 2006-09-30
Abstract
Abstract A method of forming a layer of the carbide of titanium, vanadium, etc. on the surface of an article containing carbon by employing a fluidized bed furnace. The formation of the layer is effected by disposing in the furnace a coating agent prepared from a refractory powder, a carbide forming powder composed of at least one carbide forming metal or alloy and a halide powder, and the article, and introducing a fluidizing gas into the furnace under heat to fluidize the agent. This method enables the safe and rapid formation of a carbide layer having a uniform thickness and smooth surface.
Inventors
- 👤 Tohru Arai
- 👤 Junji Endo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:14
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5053; C04B41/5057; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C23; C23C; C23C10/00; C23C10/28; C23C10/34; C23C30/00; C23C30/005
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
126 words
A method of using a fluidized bed to form a carbide layer on the surface of a carbon-containing article, which comprises the steps of: (a) disposing the article and a coating agent in a fluidized bed furnace, (b) introducing a fluidizing gas into the furnace under heat to fluidize the coating agent, and (c) heating the coating agent to a treating temperature in the range of from 700° to 1200° C. said coating agent comprising: a fluidizable refractory powder, a carbide-forming powder composed of at least one carbide-forming metal or alloy and a halide powder composed of at least one of a halogenated ammonium salt and a metal halide which is sublimable or vaporizable at a temperature which is not in excess of the treating temperature.
Claim 2
Independent Claim
126 words
A method of using a fluidized bed to form a carbide layer on the surface of a carbon-containing article, which comprises the steps of: (a) disposing the article and a coating agent in a fluidized bed furnace, (b) introducing a fluidizing gas into the furnace under heat to fluidize the coating agent, and (c) heating the coating agent to a treating temperature in the range of from 700° to 1200° C. said coating agent comprising: a fluidizable refractory powder, a carbide-forming powder composed of at least one carbide-forming metal or alloy and a halide powder composed of at least one of a halogenated ammonium salt and a metal halide which is sublimable or vaporizable at a temperature which is not in excess of the treating temperature.
Claim 3
Dependent Claim
37 words
A method according to claim 1, wherein said coating agent contains 5 to 50% by weight of said carbide forming powder and 0.2 to 3% by weight of said halide powder, the balance being said refractory powder.
Claim 4
Dependent Claim
22 words
A method according to claim 1, wherein said refractory powder comprises at least one of alumina, silicon oxide, titanium oxide and zirconia.
Claim 5
Dependent Claim
31 words
A method according to claim 1, wherein said carbide forming metal is at least one member selected from the group consisting of titanium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten and manganese.
Claim 6
Dependent Claim
31 words
A method according to claim 1, wherein said halogenated ammonium salt is at least one member selected from the group consisting of ammonium chloride, ammonium bromide, ammonium iodide and ammonium fluoride.
Claim 7
Dependent Claim
12 words
A method according to claim 1 wherein step (c) precedes step (b).
Claim 8
Dependent Claim
19 words
A method according to claim 1, wherein said coating agent has a grain size of 60 to 350 mesh.
Claim 9
Dependent Claim
21 words
A method according to claim 1, wherein said fluidizing gas is an inert gas which is nonreactive with said coating agent.
Claim 10
Dependent Claim
12 words
A method according to claim 8, wherein said fluidizing gas is argon.
Claim 11
Dependent Claim
24 words
A method according to claim 1, wherein said fluidizing gas has a flow rate of at least 50 cm per minute in said furnace.
Claim 12
Dependent Claim
21 words
A method according to claim 10, wherein said flow rate is in the range of 50 to 700 cm per minute.
Claim 13
Dependent Claim
20 words
A method according to claim 11, wherein said flow rate is in the range of 60 to 600 per minute.
Claim 14
Dependent Claim
25 words
A method according to claim 1, wherein said fluidizing gas has a pressure of 0.5 to 2 kg/cm 2 at an inlet of said furnace.
Claim 15
Dependent Claim
35 words
A method according to claim 1, wherein said article is formed of a material selected from the group consisting of iron, nickel, cobalt, or an alloy thereof, each containing carbon, a cemented carbide and graphite.
Claim 16
Dependent Claim
17 words
A method according to claim 1, wherein said article contains at least 0.1% by weight of carbon.
Claim 17
Dependent Claim
21 words
A method according to claim 1, wherein the treating temperature is in the range of from 700° C. to 1200° C.
Claim 18
Dependent Claim
32 words
A method according to claim 16, wherein said metal halide is at least one member selected from the group consisting of titanium fluoride, vanadium fluoride, vanadaium chloride, titanium bromide and ferric chloride.
Claim 19
Dependent Claim
16 words
A method according to claim 1, wherein said article is heated for 0.5 to 16 hours.
Claim 20
Dependent Claim
49 words
A method according to claim 1, wherein coarse particles of refractory powder having a grain size of 5 to 20 mesh are further disposed in said furnace between a gas inlet thereof and said coating agent, thereby preventing said gas inlet from being closed due to said coating agent.
Claim 21
Dependent Claim
46 words
A method according to claim 2, wherein said coating agent has a grain size of 60 to 350 mesh, said flow rate is in the range of 50 to 700 cm per minute, and said temperature is in the range of 700° C. to 1200° C.
Claim 22
Dependent Claim
12 words
A method according to claim 20, wherein said fluidizing gas is argon.
Claim 23
Dependent Claim
19 words
A method according to claim 21, wherein said coating agent comprises chromium powder, ammonium bromide powder and alumina powder.
Claim 24
Dependent Claim
19 words
A method according to claim 21, wherein said coating agent comprises ferrotitanium powder, titanium fluoride powder and alumina powder.
Claim 25
Dependent Claim
19 words
A method according to claim 21, wherein said coating agent comprises ferrovanadium powder, vanadium chloride powder and alumina powder.
Claim 26
Dependent Claim
19 words
A method according to claim 21, wherein said coating agent comprises ferrovanadium powder, ammonium chloride powder and alumina powder.
Claim 27
Dependent Claim
36 words
A method according to claim 1 wherein the metal halide is at least one member selected from the group consisting of titanium fluoride, vanadium fluoride, vanadium chloride, titanium bromide, ferric chloride and an equivalent metal halide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |