Surgical cement containing α-tricalcium phosphate, poly(carboxylic acid) and water
Assignee: Meishintoryo Co Ltd
•
Filing: 1985-03-22
•
Granted: 1987-06-30
•
Expires: 2005-03-22
Abstract
Abstract Here disclosed are surgical cement useful for filling defect parts and vacant part of bones and teeth which comprises (a) a component (A) of self-hardening alpha -tricalcium phosphate powder, (b) a component (B) of a surgically acceptable water-soluble poly(carboxylic acid), and (c) water and which is prepared by mixing the component (A), (B) and water or mixing the component (A) and an aqueous solution of the component (B), then kneading the mixture.
Inventors
- 👤 Tatsumi Shiotsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:49
CPC Classifications
A; A61; A61L; A61L24/00; A61L24/0047; A61L24/0073; A61L24/0084; C; C08; C08K; C08K3/00; C08K3/32
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
29 words
A surgical cement consisting essentially of: (a) a component (A) composed of self-hardening α-tricalcium phosphate powder; (b) a component (B) of surgically acceptable water-soluble poly(carboxylic acid); and (c) water.
Claim 2
Dependent Claim
29 words
A surgical cement consisting essentially of: (a) a component (A) composed of self-hardening α-tricalcium phosphate powder; (b) a component (B) of surgically acceptable water-soluble poly(carboxylic acid); and (c) water.
Claim 3
Dependent Claim
43 words
A surgical cement according to claim 1 which consists essentially of: (a) from 23 to 75% by weight of the component (A); (b) from 2 to 46% by weight of the component (B); and (c) from 10 to 69% by weight of water.
Claim 4
Dependent Claim
31 words
A surgical cement according to claim 1, in which the component (B) is in the form of an aqueous solution containing from 10 to 60% by weight of the component (B).
Claim 5
Dependent Claim
48 words
A surgical cement according to claim 1, which consists essentially of: (a) the component (A) and (b) an aqueous solution containing from 10 to 60% by weight of the component (B), and the weight ratio of (a) to (b) being in the range of from 0.3:1 to 3.0:1.
Claim 6
Dependent Claim
53 words
A surgical cement according to claim 2, in which the self-hardening α-tricalcium phosphate powder is the powder obtained by compressing α-tricalcium phosphate under press, calcining the pressed tricalcium phosphate at a temperature of from 1,200° to 1,500° C. for at least one hour and then pulverizing the calcined tricalcium phosphate into fine powder.
Claim 7
Dependent Claim
47 words
A surgical cement according to claim 1, in which the self-hardening α-tricalcium phosphate is the powder obtained by compressing amorphous tricalcium phosphate under press, calcining the pressed tricalcium phosphate at a temperature of from 1,200° to 1,500° C. for at least one hour and then finely pulverizing.
Claim 8
Dependent Claim
67 words
A surgical cement according to claim 1, in which the poly(carboxylic acid) is a homopolymer of acrylic acid or a copolymer of (a) acrylic acid as principal monomer with (b) at least one unsaturated monomer selected from the group consisting of itaconic acid, maleic acid, fumaric acid, methacrylic acid, aconitic acid, citraconic acid, mesaconic acid, tiglic acid, and lower alkylesters thereof and lower alkylesters of acrylic acid.
Claim 9
Dependent Claim
80 words
A surgical cement according to claim 1, in which the poly(carboxylic acid) is the homopolymer of acrylic acid or a copolymer of (a) from 60 to 99.9% by weight of acrylic acid with (b) from 0.1 to 40% by weight of at least one unsaturated monomer selected from the group consisting of itaconic acid, maleic acid, fumaric acid, methacrylic acid, aconitic acid, citraconic acid, glutaconic acid, mesaconic acid, tiglic acid and lower alkylesters thereof and lower alkylesters of acrylic acid.
Claim 10
Dependent Claim
39 words
A surgical cement according to claim 1, in which the viscosity-average molecular weight of the poly(carboxylic acid) is in the range of from 2,000 to 200,000, as determined by the method of Sakamoto, Chemical Abstracts, 58, 13 160C, 1963.
Claim 11
Dependent Claim
24 words
A surgical cement according to claim 1, which further contains at least one other organic acid in an amount up to 10% by weight.
Claim 12
Dependent Claim
38 words
A surgical cement according to claim 10, in which said other organic acid is at least one member selected from the group consisting of glycolic acid, lactic acid, glutamic acid, pantothenic acid, tartaric acid, citric acid, malic acid.
Claim 13
Dependent Claim
79 words
A process for preparing a surgical cement which consists essentially of the steps of preparing a mixture by admixing (a) a component (A) of self-hardening α-tricalcium phosphate powder and (b) a component (B) of a powdered surgically acceptable water-soluble poly(carboxylic acid) and adding a desired amount of water, or by adding aqueous solution of the component (B) to the component (A); then kneading the mixture thus obtained to convert the mixture to a fluidized state or a plastic state.
Claim 14
Dependent Claim
79 words
A process for preparing a surgical cement which consists essentially of the steps of preparing a mixture by admixing (a) a component (A) of self-hardening α-tricalcium phosphate powder and (b) a component (B) of a powdered surgically acceptable water-soluble poly(carboxylic acid) and adding a desired amount of water, or by adding aqueous solution of the component (B) to the component (A); then kneading the mixture thus obtained to convert the mixture to a fluidized state or a plastic state.
Claim 15
Dependent Claim
56 words
A process according to claim 12, in which the amount of the component (A) is in the range of from 23 to 75% by weight, that of the component (B) is in the range of from 2 to 46% by weight and the water is used in an amount ranging from 10 to 69% by weight.
Claim 16
Dependent Claim
32 words
A process according to claim 12, in which the weight ratio of the component (A) to the aqueous solution of the component (B) is in the range of from 0.3:1 to 3.0:1.
Claim 17
Dependent Claim
48 words
A process according to claim 12, in which the self hardening α-tricalcium phosphate powder is obtained by compressing α-tricalcium phosphate powder under press, calcining the compressed α-tricalcium phosphate at a temperature of from 1,200° to 1,500° C. for at least one hour and finely pulverizing the calcined product.
Claim 18
Dependent Claim
51 words
A process according to claim 12, in which the self hardening α-tricalcium phosphate is the powder obtained by compressing amorphous tricalcium phosphate powder under press, calcining the pressed tricalcium phosphate at a temperature of from 1,200° to 1,500° C. for at least one hour and then finely pulverizing the calcined product.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |