Method of forming suspended gate, chemically sensitive field-effect transistor
Assignee: Standard Oil Co
•
Filing: 1986-05-07
•
Granted: 1987-06-09
•
Expires: 2006-05-07
Abstract
Abstract A method is disclosed for forming a chemically sensitive field-effect transistor having a suspended gate which enables the uniform and reproducible manufacture of such devices. Controlled uniformity and device response is provided by this method which makes the field-effect transistors suitable for use as sensors, alarms and analyzers for gases. A method of regenerating a chemically sensitive field-effect transistor having a suspended gate is also disclosed.
Inventors
- 👤 Stephen C. Pyke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:49
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/32; C23F1/38; G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/414; G01N27/4141; G01N27/4143
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
205 words
A method of forming a chemically sensitive field-effect transistor having a suspended gate comprising: forming in a p-type silicon substrate two spaced-apart diffusion regions of n-type doping polarity; connecting an external electrical contact to each of said diffusion regions; depositing an electrically insulating layer on the substrate and overlying said electrical contacts and the area between them; depositing a fugitive layer containing a material selected from the group consisting of aluminum and silicon on the electrically insulating layer overlying at least the area between said diffusion regions; forming a thin film on the fugitive layer overlying at least the area between said diffusion regions, said thin film containing at least one element selected from the group consisting of refractory and transition metals; depositing a noble metal gate material on the thin-film overlying at least the area between said diffusion regions; removing the fugitive layer from the area between said diffusion regions; and etching with a buffered solution containing a complexing agent for metal ions and metal oxoanions to remove any residual portion of the thin film remaining between said diffusion regions after removal of the fugitive layer to form a suspended gate field-effect transistor having noble metal gate material substantially free of said thin film.
Claim 2
Independent Claim
205 words
A method of forming a chemically sensitive field-effect transistor having a suspended gate comprising: forming in a p-type silicon substrate two spaced-apart diffusion regions of n-type doping polarity; connecting an external electrical contact to each of said diffusion regions; depositing an electrically insulating layer on the substrate and overlying said electrical contacts and the area between them; depositing a fugitive layer containing a material selected from the group consisting of aluminum and silicon on the electrically insulating layer overlying at least the area between said diffusion regions; forming a thin film on the fugitive layer overlying at least the area between said diffusion regions, said thin film containing at least one element selected from the group consisting of refractory and transition metals; depositing a noble metal gate material on the thin-film overlying at least the area between said diffusion regions; removing the fugitive layer from the area between said diffusion regions; and etching with a buffered solution containing a complexing agent for metal ions and metal oxoanions to remove any residual portion of the thin film remaining between said diffusion regions after removal of the fugitive layer to form a suspended gate field-effect transistor having noble metal gate material substantially free of said thin film.
Claim 3
Dependent Claim
22 words
The method of claim 1 including depositing said fugitive layer to a thickness ranging from about 0.05 micrometer to about 0.5 micrometer.
Claim 4
Dependent Claim
12 words
The method of claim 1 including depositing aluminum as said fugitive layer.
Claim 5
Dependent Claim
22 words
The method of claim 1 including depositing said thin film to a thickness ranging from about 0.05 micrometer to about 0.10 micrometer.
Claim 6
Dependent Claim
17 words
The method of claim 1 including depositing a mixture of tungsten and titanium as said thin film.
Claim 7
Dependent Claim
34 words
The method of claim 5 including depositing as said thin film a mixture including about 60 to about 90 atomic weight percent tungsten and from about 10 to about 30 atomic weight percent titanium.
Claim 8
Dependent Claim
14 words
The method of claim 1 including depositing platinum as said noble metal gate material.
Claim 9
Dependent Claim
21 words
The method of claim 1 including etching with said buffered solution having a pH ranging from about 5 to about 11.
Claim 10
Dependent Claim
21 words
The method of claim 1 including etching with said buffered solution having a pH ranging from about 10.2 to about 10.6.
Claim 11
Dependent Claim
16 words
The method of claim 1 including maintaining said buffered solution at a pH of about 10.4.
Claim 12
Dependent Claim
33 words
The method of claim 1 including selecting said complexing agent from the group consisting of ethylenediaminetetraacetic acid and other carboxylates, bipyridines, phenanthrolines, macrocyclic amines, crown ethers, xanthates, dithiocarbamates, beta-diketonates, and their substituted derivatives.
Claim 13
Dependent Claim
26 words
The method of claim 1 including etching with a buffered solution comprising ethylenediaminetetraacetic acid, hydrogen peroxide, and ammonium hydroxide in a volume ratio of about 5:1.5:1.
Claim 14
Independent Claim
43 words
A method of regenerating a chemically sensitive field-effect transistor having a suspended gate comprising disposing said suspended gate in contact with a buffered solution containing a complexing agent for metal ions so as to remove any metal contaminants adhering to said suspended gate.
Claim 15
Independent Claim
43 words
A method of regenerating a chemically sensitive field-effect transistor having a suspended gate comprising disposing said suspended gate in contact with a buffered solution containing a complexing agent for metal ions so as to remove any metal contaminants adhering to said suspended gate.
Claim 16
Dependent Claim
23 words
The method of claim 13 including contacting said gate with a buffered solution having a pH ranging from about 5 to about 11.
Claim 17
Dependent Claim
23 words
The method of claim 13 including contacting said gate with a buffered solution having a pH ranging from about 10.2 to about 10.6.
Claim 18
Dependent Claim
16 words
The method of claim 13 including maintaining said buffered solution at a pH of about 10.4.
Claim 19
Dependent Claim
31 words
The method of claim 13 including selecting said complexing agent from the group consisting of ethylenediaminetetraacetic acid, carboxylates, bipyridines, phenanthrolines, macrocyclic amines, crown ethers, xanthates, dithiocarbamates, beta-diketonates and their substituted derivatives.
Claim 20
Dependent Claim
28 words
The method of claim 13 including contacting said gate with a buffered solution comprising ethylenediaminetetraacetic acid, hydrogen peroxide and ammonium hydroxide in a volume ratio of about 5:1.5:1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-08 | 1990-12-08 | 1991-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-08 | 1994-12-08 | 1995-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-08 | 1998-12-08 | 1999-06-09 | $7700.00 | Window Closed / Lapsed |