Mixed diamine chain extender

Claim 2

A polyurethane formed by reaction of: (a) an organic active hydrogen group-containing compound; (b) an organic polyisocyanate; and (c) a chain extender mixture comprising: (i) a first aromatic diamine having a machine gel time of about 1.0 to about 4.0 seconds in a 50,000 psi modulus RIM formulation reaction: and (ii) a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation reaction of about 1.5 to 15 times the machine gel time of said first aromatic diamine; said polyurethane having non-brittle, rigid green strength after reaction and having a flexural modulus of at least about 50,000 psi at 75° F.

Claim 3

The polyurethane of claim 1 wherein said first aromatic diamine has an alkyl substituent ortho to each amino group.

Claim 4

The polyurethane of claim 2 wherein said first aromatic diamine has an alkyl substituent in each position ortho to at least one amino group.

Claim 5

The polyurethane of claim 3 wherein said first aromatic diamine has an alkyl substituent in each position ortho to both amino groups.

Claim 6

The polyurethane of claim 2 wherein said first aromatic diamine is an alkyl-substituted diaminobenzene.

Claim 7

The polyurethane of claim 5 wherein said alkyl-substituted diaminobenzene is 1-methyl-3,5-diethyl-2,4-diaminobenzene; 1-methyl-3,5-diethyl-2,6-diaminobenzene; or a mixture thereof.

Claim 8

The polyurethane of claim 2 wherein said first aromatic diamine is an alkyl-substituted 4,4'-methylenebisaniline.

Claim 9

The polyurethane of claim 7 wherein said alkylsubstituted 4,4'-methylenebisaniline is 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline.

Claim 10

The polyurethane of claim 1 wherein said second aromatic diamine has at least one alkylthio substituent ortho to at least one amino group.

Claim 11

The polyurethane of claim 9 wherein said second aromatic diamine is 1-methyl-3,5-dimethylthio-2,4-diaminobenzene; 1-methyl-3,5-dimethylthio-2,6-diaminobenzene; or a mixture thereof.

Claim 12

The polyurethane of claim 1 wherein said second aromatic diamine has at least one halo substituent ortho to each amino group.

Claim 13

The polyurethane of claim 11 wherein said second aromatic diamine is 2,2'-dichloro-4,4'-methylenebisaniline.

Claim 14

A process for preparing a RIM polyurethane molded product, said process comprising the steps of: (a) at a temperature of about 15°-100° C., subjecting to static impingement mixing (i) an organic polyisocyanate, (ii) an organic active hydrogen group-containing compound, and (iii) a chain extender mixture comprising a first aromatic diamine having a machine gel time of about 1.0 to 4.0 seconds in a 50,000 psi modulus RIM formulation reaction and a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation reaction of about 1.5 to about 15 times the machine gel time of said first aromatic diamine, whereby a liquid mixture is produced; (b) injecting a shot of said liquid mixture into a closed mold preheated to about 15°-100° C. and forming a polyurethane molded product having rigid, non-brittle green strength and a flexural modulus at 75° F. of at least about 50,000 psi; (c) opening the mold and removing the formed polyurethane molded product; and (d) optionally, postcuring said molded product at 50°-200° C.

Claim 15

A process for preparing a RIM polyurethane molded product, said process comprising the steps of: (a) at a temperature of about 15°-100° C., subjecting to static impingement mixing (i) an organic polyisocyanate, (ii) an organic active hydrogen group-containing compound, and (iii) a chain extender mixture comprising a first aromatic diamine having a machine gel time of about 1.0 to 4.0 seconds in a 50,000 psi modulus RIM formulation reaction and a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation reaction of about 1.5 to about 15 times the machine gel time of said first aromatic diamine, whereby a liquid mixture is produced; (b) injecting a shot of said liquid mixture into a closed mold preheated to about 15°-100° C. and forming a polyurethane molded product having rigid, non-brittle green strength and a flexural modulus at 75° F. of at least about 50,000 psi; (c) opening the mold and removing the formed polyurethane molded product; and (d) optionally, postcuring said molded product at 50°-200° C.

Claim 16

The process of claim 13 wherein said chain extender mixture has a machine gel time in said process of about 2.5 to about 10.0 seconds.

Claim 17

The process of claim 13 wherein the amount of said chain extender mixture is about 5-40 weight percent of the total weight of components (i), (ii), and (iii) and wherein the ratio of isocyanate groups on the one hand to combined active hydrogen groups and amino groups on the other hand is about 0.90 to 1.10.

Claim 18

The process of claim 13 wherein the ratio of amino groups of said chain extender mixture of aromatic diamines to active hydrogen groups of said active hydrogen group-containing compound is at least about 8:1.

Claim 19

The process of claim 13 wherein said first aromatic diamine has an alkyl substituent ortho to each amino group.

Claim 20

The process of claim 17 wherein said first aromatic diamine is a member selected from the group consisting of 1-methyl-3,5-diethyl-2,4-diaminobenzene; 1-methyl-3,5-diethyl-2,6-diaminobenzene; 1,3,5-triethyl-2,6-diaminobenzene; and 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline.

Claim 21

The process of claim 13 wherein said second aromatic diamine has at least one alkylthio substituent ortho to at least one amino group.

Claim 22

The process of claim 13 wherein said second aromatic diamine has at least one halo substituent ortho to each amino group.

Claim 23

The process of claim 20 wherein said second aromatic diamine is 2,2'-dichloro-4,4'-methylenebisaniline.

Claim 24

The process of claim 13 wherein said active hydrogen group-containing compound is an amine terminated polyether.

Claim 25

The process of claim 13 wherein said active hydrogen group-containing compound is an organic polyol having hydroxyl groups and being in the molecular weight range of 400-7000, and wherein also subjected to said static impingement mixing is a catalyst for reaction between said hydroxyl groups and isocyanate groups.

Claim 26

A polyurethane RIM process comprising: (a) at a temperature of about 15°-100° C. subjecting to static impingement mixing two liquid streams, a first stream comprising (i) an organic polyisocyanate or prepolymer or quasi-prepolymer formed from an organic polyisocyanate and an organic active hydrogen group-containing compound; and a second stream comprising (ii) either (1) an organic polyol having a molecular weight of about 400-7000 combined with a catalyst for reaction between hydroxyl groups and isocyanate groups, or (2) an amine terminated polyether or polyester and (iii) a chain extender mixture of a first aromatic diamine selected from 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline; 1-methyl-3,5-diethyl-2,4-diaminobenzene; 1-methyl-3,5-diethyl-2,6-diaminobenzene; 1,3,5-triethyl-2,6-diaminobenzene; and mixtures thereof; and a second chain extender selected from 1-methyl-3,5-dimethylthio-2,4-diaminobenzene; 1-methyl-3,5-dimethylthio-2,6-diaminobenzene; 2,2'-dichloro-4,4'-methylenebisaniline; and mixtures thereof, whereby a liquid mixture is produced, said mixture having a machine gel time in said process of about 2.5 to about 10 seconds; (b) injecting a shot of said liquid mixture into a closed mold preheated to about 15°-100° C.; (c) opening the mold and removing a molded product having rigid, non-brittle green strength and a flexural modulus at 75° F. of at least about 50,000 psi; and (d) optionally postcuring said product at 50°-200° C.; the amount of said chain extender mixture comprising about 5-40 weight percent of the total weight of components (i), (ii), and (iii) and the ratio of isocyanate groups to combined hydroxyl groups and amino groups being about 0.90 to 1.10.

Claim 27

A polyurethane RIM process comprising: (a) at a temperature of about 15°-100° C. subjecting to static impingement mixing two liquid streams, a first stream comprising (i) an organic polyisocyanate or prepolymer or quasi-prepolymer formed from an organic polyisocyanate and an organic active hydrogen group-containing compound; and a second stream comprising (ii) either (1) an organic polyol having a molecular weight of about 400-7000 combined with a catalyst for reaction between hydroxyl groups and isocyanate groups, or (2) an amine terminated polyether or polyester and (iii) a chain extender mixture of a first aromatic diamine selected from 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline; 1-methyl-3,5-diethyl-2,4-diaminobenzene; 1-methyl-3,5-diethyl-2,6-diaminobenzene; 1,3,5-triethyl-2,6-diaminobenzene; and mixtures thereof; and a second chain extender selected from 1-methyl-3,5-dimethylthio-2,4-diaminobenzene; 1-methyl-3,5-dimethylthio-2,6-diaminobenzene; 2,2'-dichloro-4,4'-methylenebisaniline; and mixtures thereof, whereby a liquid mixture is produced, said mixture having a machine gel time in said process of about 2.5 to about 10 seconds; (b) injecting a shot of said liquid mixture into a closed mold preheated to about 15°-100° C.; (c) opening the mold and removing a molded product having rigid, non-brittle green strength and a flexural modulus at 75° F. of at least about 50,000 psi; and (d) optionally postcuring said product at 50°-200° C.; the amount of said chain extender mixture comprising about 5-40 weight percent of the total weight of components (i), (ii), and (iii) and the ratio of isocyanate groups to combined hydroxyl groups and amino groups being about 0.90 to 1.10.

Claim 28

The process of claim 24 wherein said first aromatic diamine is a mixture of 1-methyl-3,5-diethyl-2,4-diaminobenzene and 1-methyl-3,5-diethyl-2,6-diaminobenzene and said second aromatic diamine is a mixture of 1-methyl-3,5-dimethylthio-2,6-diaminobenzene and 1-methyl-3,5-dimethylthio-2,4-diaminobenzene.

Claim 29

The process of claim 24 wherein said first aromatic diamine is 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline and said second aromatic diamine is a mixture of 1-methyl-3,5-dimethylthio-2,6-diaminobenzene and 1-methyl-3,5-dimethylthio-2,4-diaminobenzene.

Claim 30

The process of claim 24 wherein said first aromatic diamine is a mixture of 1-methyl-3,5-diethyl-2,4-diaminobenzene and 1-methyl-3,5-diethyl-2,6-diaminobenzene and said second aromatic diamine is 2,2'-dichloro-4,4'-methylenebisaniline.

Claim 31

The process of claim 24 with about equimolar parts of said first aromatic diamine and said second aromatic diamine.

Claim 32

A chain extender composition comprising a mixture of a first aromatic diamine having a machine gel time of about 1.0 to about 4.0 seconds in a 50,000 psi modulus RIM formulation reaction and a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation of about 1.5 to 15 times that of said first diamine.

Claim 33

A chain extender composition comprising a mixture of a first aromatic diamine having a machine gel time of about 1.0 to about 4.0 seconds in a 50,000 psi modulus RIM formulation reaction and a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation of about 1.5 to 15 times that of said first diamine.

Claim 34

The composition of claim 29 wherein said first diamine is selected from 2,2',6,6'-tetraisopropyl-4,4'-methylenebisaniline; 1-methyl-3,5-diethyl-2,4-diaminobenzene; 1-methyl-3,5-diethyl-2,6-diaminobenzene; 1,3,5-triethyl-2,6-diaminobenzene and wherein said second diamine is selected from 1-methyl-3,5-dimethylthio-2,4-diaminobenzene; 1-methyl-3,5-dimethylthio-2,6-diaminobenzene; 2,2'-dichloro-4,4'-methylenebisaniline;

Claim 35

The composition of claim 29 wherein said first diamine comprises about 30-70 molar percent of said mixture and said second diamine comprises the remainder of said mixture.

Claim 36

An isocyanate-reactive resin stream composition comprising: (i) an organic active hydrogen group-containing compound having a molecular weight of about 400 to 7000; (ii) a first aromatic diamine having a machine gel time of about 1.0 to about 4.0 seconds in a 50,000 psi modulus RIM formulation reaction; and (iii) a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation reaction of about 1.5 to about 15 times the machine gel time of said first aromatic diamine, wherein the ratio of (a) amino groups from said first aromatic diamine and said second aromatic diamine to (b) active hydrogen groups from said organic active hydrogen group-containing compound is at least about 8:1.

Claim 37

An isocyanate-reactive resin stream composition comprising: (i) an organic active hydrogen group-containing compound having a molecular weight of about 400 to 7000; (ii) a first aromatic diamine having a machine gel time of about 1.0 to about 4.0 seconds in a 50,000 psi modulus RIM formulation reaction; and (iii) a second aromatic diamine having a machine gel time in a 50,000 psi modulus RIM formulation reaction of about 1.5 to about 15 times the machine gel time of said first aromatic diamine, wherein the ratio of (a) amino groups from said first aromatic diamine and said second aromatic diamine to (b) active hydrogen groups from said organic active hydrogen group-containing compound is at least about 8:1.