Mixed lixiviant for separate recovery of zinc and lead from iron-containing waste materials
Assignee: KOREA ZINC Co (USA) Inc
•
Filing: 1985-01-31
•
Granted: 1986-09-30
•
Expires: 2005-01-31
Abstract
Abstract A process is disclosed for the hydrometallurgical treatment of finely divided iron-containing steel plant dusts containing zinc, lead and such other metal values as calcium, manganese, silicon, magnesium, aluminum, cadmium, copper, and the like. The process is carried out by forming an aqueous slurry of the flue dust with a mixed lixiviant comprising HCl and H 2 SO 4 , the amount of sulfate ion concentration being in excess of the chloride ion concentration and in stoichiometric excess of that required to sulfate substantially all of the lead and calcium present. The amount of chloride ion present as HCl should be sufficient to maintain the pH at about 1 to 4. The leaching is conducted at a temperature ranging from ambient to below the boiling point for a time at least sufficient to effect dissolution of at least zinc and other metal values and form a residue containing iron oxide, calcium sulfate and lead sulfate.
Inventors
- 👤 Willem P. C. Duyvesteyn
- 👤 Mahesh C. Jha
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:58
CPC Classifications
C; C22; C22B; C22B19/00; C22B19/20; C22B19/22; C22B13/00; C22B13/04; C22B17/00; C22B17/04; C22B19/26; C22B26/00; C22B26/20; C22B3/00; C22B3/04; C22B3/06; C22B7/00; C22B7/02; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S75/00; Y10S75/961
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
202 words
A process for the hydrometallurgical treatment of finely divided steel plant flue dusts containing by weight about 20% to 60% iron, about 5% to 40% zinc and about 0.5% to 6% lead as oxides, and also containing at least one other metal value selected from the group consisting of oxides of calcium, manganese, silicon, magnesium, aluminum, cadmium, copper, which comprises, forming an aqueous slurry of said steel plant flue dust with a mixed lixiviant comprising HCl and H 2 SO 4 , the amount of sulfate ion concentration being in excess of the chloride ion concentration and in stoichiometric excess of that required to sulfate substantially all of the lead and calcium present, the amount of chloride ion present as HCl being at least about 6 g/1 sufficient to maintain the pH at about 1 to 4, leaching said steel plant flue dust at a temperature ranging from ambient to below the boiling point for a time at least sufficient to effect dissolution of at least said zinc and said at least one other metal value and form a residue containing at least iron oxide, calcium sulfate and lead sulfate, and then separating said residue from the solution containing said metal values.
Claim 2
Dependent Claim
202 words
A process for the hydrometallurgical treatment of finely divided steel plant flue dusts containing by weight about 20% to 60% iron, about 5% to 40% zinc and about 0.5% to 6% lead as oxides, and also containing at least one other metal value selected from the group consisting of oxides of calcium, manganese, silicon, magnesium, aluminum, cadmium, copper, which comprises, forming an aqueous slurry of said steel plant flue dust with a mixed lixiviant comprising HCl and H 2 SO 4 , the amount of sulfate ion concentration being in excess of the chloride ion concentration and in stoichiometric excess of that required to sulfate substantially all of the lead and calcium present, the amount of chloride ion present as HCl being at least about 6 g/1 sufficient to maintain the pH at about 1 to 4, leaching said steel plant flue dust at a temperature ranging from ambient to below the boiling point for a time at least sufficient to effect dissolution of at least said zinc and said at least one other metal value and form a residue containing at least iron oxide, calcium sulfate and lead sulfate, and then separating said residue from the solution containing said metal values.
Claim 3
Dependent Claim
42 words
The process of claim 1, wherein the amount of hycrochloric acid present is sufficient to maintain the pH at about 2 to 4, and wherein the ratio of the sulfate in concentration to the chloride in concentration is at least about 2:1.
Claim 4
Dependent Claim
41 words
The process of claim 1, wherein the hydrochloric acid concentration ranges from about 24 gpl to about 17 gpl to provide a pH ranging from about 1 to 3 and the sulfuric acid concentration ranges from about 10 to 50 gpl.
Claim 5
Dependent Claim
18 words
The process of claim 1, wherein the temperature of leaching ranges from about 25° C. to 90° C.
Claim 6
Dependent Claim
20 words
The process of claim 1, wherein the aqueous slurry has a pulp density by weight of about 5% to 40%.
References Cited (Backward Citations)
US2264337A
Cited
US3375069A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-29 | 1990-03-31 | 1990-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-29 | 1994-03-31 | 1994-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-29 | 1998-03-31 | 1998-09-30 | $7700.00 | Window Closed / Lapsed |