Collagen preparation

Claim 2

A collagen preparation comprising collagen-I for human or veterinary therapy obtained by the following consecutive steps: (a) proteolyzing mammalian collagen-I material in presence of ficin and L-cysteine in an aqueous medium at a pH value of 5.5-6.5 and at a temperature of 30° to 50° C., (b) cross-linking the material obtained according to step (a) with at least one aliphatic dialdehyde of 2 to 10 carbon atoms, (c) reducing the material obtained according to step (b) with a reducing bleaching agent and (d) finally sterilizing the material, wherein the texture of the collagen-I material is preserved throughout all steps.

Claim 3

A collagen preparation according to claim 1, wherein skin, corium, fasciae, tendons, blood vessels, tubular hollow organs, pericardia, and interstitial mammal tissue is the mammalian collagen-I material.

Claim 4

A collagen preparation according to claim 1 wherein the collagen-I material is derived from goats, bovine, and bovine fetuses.

Claim 5

A collagen preparation according to claim 1 wherein the aliphatic dialdehyde has 4 to 7 carbon atoms; the reducing is effected with an alkali metal borohydride in an aqueous medium; and treated for some minutes at 80° to 100° C. with hot air saturated with steam to mold the same and, finally sterilizing the so obtained collagen-I material.

Claim 6

The collagen preparation of claim 1 wherein after a collagen material is subjected to the first proteolysis of Step A the desired thickness is achieved by cleaving said collagen parallel to the direction of the fibers, proteolyzing again and continuing the treatment in the remaining steps according to claim 1.

Claim 7

A collagen preparation of claim 1 or 5 where there is a treatment with dilute aqueous sodium chlorite solution after the proteolysis.

Claim 8

A collagen preparation of claim 1, 4 or 5 including washing with running water between the individual process steps.

Claim 9

A collagen preparation of claim 1 obtained by treating mammalian collagen-I with an aqueous solution containing 10 g ficin per liter and 1 g L-cysteine per liter at a pH value of about 6 and at a temperature of about 37° C. for 8 to 24 hours, then sequentially treating with a 1% by weight aqueous sodium chlorite solution for 24 hours, washing with water, treating with a 1 to 10% by weight aqueous glutaric dialdehyde solution for 7 days, washing with water, treating with an aqueous sodium borohydride solution for 24 hours, washing with water and then sterilizing, wherein the washing is performed with running water for 24 hours, respectively.

Claim 10

The collagen preparation of claim 1 formed in the shape of a hollow tube having a defined diameter by coating a smooth surfaced solid bar with said collagen material, and after treating said collagen according to steps (a) to (c) of claim 1, additionally treating with hot air saturated with steam at 80° to 150° C. and about 1.5 bar and sterilizing it.

Claim 11

A collagen preparation according to claim 9 wherein said bar is a glass rod coated with silicone.

Claim 12

A collagen preparation of claim 1 in the shape of a bag like hollow organ having a defined diameter obtained by applying a bovine pericardium to a silicone coated glass flask of a desired diameter and after the reducing step, the shaped pericardium is heated and sterilized.

Claim 13

A collagen preparation of claim 1 starting from rasped corium material or interstitial mammalian tissue to obtain a cotton like or woolly filling material.

Claim 14

A collagen preparation according to claims 1, 4, 5, 8, 9, 11 or 12, which is sterilized by treating the finished collagen preparation for some days with about 50% by weight of aqueous ethyl alcohol, containing about 1% by weight propyleneoxide, then tansferring the preparation into a sterile buffered sodium chloride solution and heating the sodium chloride solution to evaporate the remaining sterilization solution during several hours.

Claim 15

The collagen of claim 1 prepared by the consecutive steps of: (a) proteolyzing mammalian collagen-I material, (b) cross-linking the material obtained according to step (a), (c) reducing the material obtained according to step (b) and (d) finally sterilizing the material, wherein, the material obtained according to step (c) is heated, molded and "welded" where pieces of said material are to be connected and wherein the texture of the collagen-I material is preserved throughout all steps.

Claim 16

The preparation of claim 4 wherein the cross-linking is effected with a 1 to 10% by weight of aqueous glutaric dialdehyde solution.

Claim 17

A method of surgical repair of defective parts of the body of a mammal comprising replacing the defective parts selected from the group consisting of skin, ligaments, tendons, tendon sheaths, hollow organs, blood vessels and mama with a collagen preparation of claim 1.

Claim 18

The preparation of claim 1 wherein the material obtained by step (c) is heated to mold the same.

Claim 19

A collagen-I preparation of claim 1 wherein the material obtained by step (c) is heated to mold and weld pieces of said material to connect them.

Claim 20

A process for preparation of a collagen-I preparation comprising (a) proteolyzing mammalian collagen-I material in presence of ficin and L-cysteine in an aqueous medium at a pH value of 5.5-6.5 and at a temperature of 30° to 50° C., (b) cross-linking the material obtained according to step (a) with at least one aliphatic dialdehyde of 2 to 10 carbon atoms, (c) reducing the material obtained according to step (b) with a reducing bleaching agent and (d) finally sterilizing the material, wherein the texture of the collagent-I material is preserved throughout all steps.

Claim 21

A process for preparation of a collagen-I preparation comprising (a) proteolyzing mammalian collagen-I material in presence of ficin and L-cysteine in an aqueous medium at a pH value of 5.5-6.5 and at a temperature of 30° to 50° C., (b) cross-linking the material obtained according to step (a) with at least one aliphatic dialdehyde of 2 to 10 carbon atoms, (c) reducing the material obtained according to step (b) with a reducing bleaching agent and (d) finally sterilizing the material, wherein the texture of the collagent-I material is preserved throughout all steps.

Claim 22

A collagen-I method of claim 19 wherein the material obtained by step (c) is heated to mold and weld pieces of said material to connect them.

Claim 23

A collagen-I method of claim 19 wherein the material obtained by step (c) is heated to mold the same.