Method of applying a hydrophilic coating to a polymeric substrate and articles prepared thereby
Assignee: Becton Dickinson and Co
•
Filing: 1984-05-29
•
Granted: 1986-05-20
•
Expires: 2004-05-29
Abstract
Abstract A method to impart increased lubricity to the surface of a polymeric substrate includes contacting the substrate with a solution of a hydrophilic polymer in a solvent and heating the substrate to evaporate the solvent. The substrate retains a coating of the hydrophilic polymer, which, when dry, has about the same lubricity as the uncoated substrate. When wet, the coating becomes significantly more lubricious than when dry. The invention includes articles which have a lubricious surface when wet prepared by the method of the invention.
Inventors
- 👤 Abraham Schwartz
- 👤 Jane Graper
- 👤 Joel Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 23:23
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/091; A; A61; A61B; A61B42/00; A61L; A61L27/00; A61L27/28; A61L27/34; A61L29/00; A61L29/08; A61L29/085; C08J7/00; C08J7/04; C08J7/0427; C08J7/056; A61F; A61F2/00; A61F2/02; A61F2/24; C08J2339/00; C08J2339/04; C08J2339/08; C08J2439/00; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/31504; Y10T428/31551; Y10T428/31652; Y10T428/31667
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
80 words
A method of coating a polymeric substrate comprising contacting a polymeric substrate with a solution of polyvinyl pyrrolidone in an applying solvent selected from the group of solvents consisting of dimethyl formamide, butanone, methanol, tetrahydrofuran and dimethyl acetamide and evaporating said solvent from said substrate so that the surface of said substrate retains a coating of said polyvinyl pyrrolidone to thereby provide the surface of said coated substrate with lubricity when said coated substrate is contacted with an aqueous-based liquid.
Claim 2
Independent Claim
80 words
A method of coating a polymeric substrate comprising contacting a polymeric substrate with a solution of polyvinyl pyrrolidone in an applying solvent selected from the group of solvents consisting of dimethyl formamide, butanone, methanol, tetrahydrofuran and dimethyl acetamide and evaporating said solvent from said substrate so that the surface of said substrate retains a coating of said polyvinyl pyrrolidone to thereby provide the surface of said coated substrate with lubricity when said coated substrate is contacted with an aqueous-based liquid.
Claim 3
Dependent Claim
27 words
The method in accordance with claim 1 wherein said substrate is a polymer selected from the group consisting of polyvinyl chloride, polyethylene, polypropylene, polytetrafluoroethylene, polyurethane, latex rubber.
Claim 4
Dependent Claim
16 words
The method in accordance with claim 1 wherein said applying solvent is a mixture of solvents.
Claim 5
Dependent Claim
48 words
The method in accordance with claim 1 further comprising washing said substrate with a washing solvent after said evaporating to remove excess polyvinyl pyrrolidone from the surface of said coated substrate and drying said coated substrate to remove said washing solvent from the surface of said coated substrate.
Claim 6
Dependent Claim
27 words
The method in accordance with claim 4 wherein said washing solvent is selected from group of solvents consisting of water, acetone, acetontrile, methanol, ethanol, isopropanol and tetrahydrofuran.
Claim 7
Dependent Claim
32 words
The method in accordance with claim 1 further comprising immersing said polymeric substrate in an immersing solvent before said contacting wherein said substrate is swelled by said immersing solvent before said contacting.
Claim 8
Independent Claim
124 words
A method of rendering the surface of a polymeric substrate more lubricious comprising contacting a polyvinyl chloride substrate having a first surface coefficient of friction with a solution of polyvinyl pyrrolidone in dimethyl formamide, heating said substrate to evaporate said dimethyl formamide whereby the surface of said polyvinyl chloride substrate retains a coating of said polyvinyl pyrrolidone, washing said coated substrate with water to remove excess polyvinyl pyrrolidone, and drying said coated substrate to remove said water from the surface of said coated substrate to provide the surface of said coated substrate with a second surface coefficient of friction lower than said first coefficient of friction to thereby render said coated substrate more lubricious when said coated substrate is contacted with an aqueous-based liquid.
Claim 9
Independent Claim
124 words
A method of rendering the surface of a polymeric substrate more lubricious comprising contacting a polyvinyl chloride substrate having a first surface coefficient of friction with a solution of polyvinyl pyrrolidone in dimethyl formamide, heating said substrate to evaporate said dimethyl formamide whereby the surface of said polyvinyl chloride substrate retains a coating of said polyvinyl pyrrolidone, washing said coated substrate with water to remove excess polyvinyl pyrrolidone, and drying said coated substrate to remove said water from the surface of said coated substrate to provide the surface of said coated substrate with a second surface coefficient of friction lower than said first coefficient of friction to thereby render said coated substrate more lubricious when said coated substrate is contacted with an aqueous-based liquid.
Claim 10
Dependent Claim
15 words
A catheter having a lubricious surface when wet prepared by the method of claim 7.
Claim 11
Dependent Claim
16 words
An examination glove having a lubricious surface when wet prepared by the method of claim 7.
Claim 12
Dependent Claim
101 words
An article consisting of a polymeric substrate selected from the group of substrates consisting of polyvinyl chloride, polyethylene, polypropylene, polytetrafluoroethylene, polyurethane and latex rubber having a coating of polyvinyl pyrrolidone directly on said substrate whereby the surface of said substrate having said polyvinyl pyrrolidone coating and the surface of said substrate without said coating have substantially the same surface coefficient of friction when dry, but the surface of said substrate having said polyvinyl pyrrolidone coating when wet has a coefficient of friction which is lower than the coefficient of friction of said surface of said substrate without said coating when wet.
Claim 13
Dependent Claim
101 words
An article consisting of a polymeric substrate selected from the group of substrates consisting of polyvinyl chloride, polyethylene, polypropylene, polytetrafluoroethylene, polyurethane and latex rubber having a coating of polyvinyl pyrrolidone directly on said substrate whereby the surface of said substrate having said polyvinyl pyrrolidone coating and the surface of said substrate without said coating have substantially the same surface coefficient of friction when dry, but the surface of said substrate having said polyvinyl pyrrolidone coating when wet has a coefficient of friction which is lower than the coefficient of friction of said surface of said substrate without said coating when wet.
Claim 14
Dependent Claim
24 words
The article of claim 10 which is a polyvinyl chloride catheter and having a coefficient of friction when wet of about 0.1 to 0.3.
Claim 15
Dependent Claim
22 words
The article of claim 10 which is a polyvinyl chloride examination glove having a coefficient of friction of about 0.1 to 0.3.
Claim 16
Independent Claim
89 words
A method of coating a polymeric substrate comprising immersing a polymeric substrate in an immersing solvent selected from the group of solvents consisting of benzene, toluene and xylene wherein said substrate is swelled, contacting said substrate with a solution of polyvinyl pyrrolidone in an applying solvent, and evaporating said applying solvent from said substrate so that the surface of said substrate retains a coating of said polyvinyl pyrrolidone to thereby provide the surface of said coated substrate with lubricity when said coated substrate is contacted with an aqueous-based liquid.
Claim 17
Independent Claim
89 words
A method of coating a polymeric substrate comprising immersing a polymeric substrate in an immersing solvent selected from the group of solvents consisting of benzene, toluene and xylene wherein said substrate is swelled, contacting said substrate with a solution of polyvinyl pyrrolidone in an applying solvent, and evaporating said applying solvent from said substrate so that the surface of said substrate retains a coating of said polyvinyl pyrrolidone to thereby provide the surface of said coated substrate with lubricity when said coated substrate is contacted with an aqueous-based liquid.
References Cited (Backward Citations)
US3216983A
Cited
DE1796134A1
Cited
US3695921A
Cited
US4055682A
Cited
US3939049A
Cited
US4087567A
Cited
US4112925A
Cited
US4169163A
Cited
US4100309A
Cited
US4119094A
Cited
US4143423A
Cited
US4381008A
Cited
US4482577A
Cited
US4373009A
Cited
US4459317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-19 | 1989-11-18 | 1990-05-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-19 | 1993-11-18 | 1994-05-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-19 | 1997-11-18 | 1998-05-20 | $7700.00 | Window Closed / Lapsed |