Resist material comprising polymer of allylsilyl compound and pattern forming method using the resist material
Assignee: NEC Corp
•
Filing: 1984-05-22
•
Granted: 1986-01-14
•
Expires: 2004-05-22
Abstract
Abstract A polymer having allyl groups each attached to a silicon atom serves as a resist material which is highly resistive to dry etching such as reactive sputter etching with oxygen and sensitive to electron beams, X-rays and deep UV rays. By the addition of a bis-azide compound known as a photosensitive cross-linking agent the resist material becomes sensitive also to UV and near UV rays. A very suitable polymer is obtained by polymerizing either a triallylsilane or an allylsilylstyrene or by copolymerizing an allylsilylstyrene with another ethylenic compound copolymerizable with styrene. This resist material is used in a pattern forming method of the two-layer type, in which a fine pattern is generated in a thin film of the resist material by lithography and then transferred into an underlying thick organic layer by dry etching of the thick organic layer with the resist pattern as a mask.
Inventors
- 👤 Kazuhide Saigo
- 👤 Masayoshi Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:46
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/075; G03F7/0757; G03F7/0758; C; C08; C08F; C08F30/00; C08F30/04; C08F30/08; G03F7/008; G03F7/012; G03F7/0125
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
66 words
A resist material comprising a polymer produced by polymerization of a monomer having an allylsilyl group, said monomer being a triallylsilane expressed by the formula R--Si(CH 2 --CH═CH 2 ) 3 , where R represents a hydrogen atom, methyl group, ethyl group, propyl group or phenyl group; and a photosensitive cross-linking agent which is a bis-azide compound and amounts to 0.1-50% by weight of said polymer.
Claim 2
Dependent Claim
66 words
A resist material comprising a polymer produced by polymerization of a monomer having an allylsilyl group, said monomer being a triallylsilane expressed by the formula R--Si(CH 2 --CH═CH 2 ) 3 , where R represents a hydrogen atom, methyl group, ethyl group, propyl group or phenyl group; and a photosensitive cross-linking agent which is a bis-azide compound and amounts to 0.1-50% by weight of said polymer.
Claim 3
Dependent Claim
93 words
A resist material according to claim 1, wherein said polymer comprises at least one structural unit selected from the group consisting of the structural units of the formulas (I) and (II), said polymer being produced by carrying out bulk or solvent polymerization of said triallylsilane at a temperature in the range from 60° to 150° C. for a period of 4 to 50 hr using a radical polymerization initiator amounting to 1-10 mole % of said triallylsilane: ##STR8## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or phenyl group.
Claim 4
Dependent Claim
36 words
A resist material according to claim 2, wherein said polymer further comprises a structural unit expressed by the formula (III): ##STR9## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or phenyl group.
Claim 5
Dependent Claim
42 words
A resist material comprising a polymer produced by polymerization of a monomer having an allylsilyl group, said monomer being an allylsilylstyrene expressed by the general formula ##STR10## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or allyl group.
Claim 6
Dependent Claim
42 words
A resist material comprising a polymer produced by polymerization of a monomer having an allylsilyl group, said monomer being an allylsilylstyrene expressed by the general formula ##STR10## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or allyl group.
Claim 7
Dependent Claim
79 words
A resist material according to claim 4, wherein said polymer is produced by carrying out bulk or solution polymerization of said allylsilylstyrene at a temperature in the range from 40° to 150° C. for a period of 2 to 30 hr using a radical polymerization initiator amounting to 0.01-5 mole % of said allylsilylstyrene and comprises a structural unit of the formula (IV): ##STR11## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or allyl group.
Claim 8
Dependent Claim
118 words
A resist material according to claim 4, wherein said polymer is produced by carrying out bulk or solution copolymerization of said allylsilylstyrene and another ethylenic unsaturated monomer, which is copolymerizable with styrene and expressed by the general formula CH 2 ═CH--A, at a temperature in the range from 40° to 150° C. for a period of 2 to 30 hr using a radical polymerization initiator amounting to 0.01-5 mole % of the total of said allylsilylstyrene and said ethylenic unsaturated monomer and has a structure expressed by the formula (V): ##STR12## where R represents a hydrogen atom, methyl group, ethyl group, propyl group or allyl group, and x is smaller than 1 but is not smaller than 0.2.
Claim 9
Dependent Claim
47 words
A resist material according to claim 6, wherein said other monomer is selected from the group consisting of acrylic acid, methyl-, ethyl-, glycidyl-, vinyl- and allyl esters of acrylic acid, methacrylic acid, methyl-, ethyl-, glycidyl-, vinyl- and allyl esters of methacrylic acid, styrene, chlorostyrene, methylstyrene and choloromethylstyrene.
Claim 10
Dependent Claim
37 words
A resist material according to claims 2, 5, or 6, wherein said polymer has a weight average molecular weight in the range from 10000 to 1000000 and is not larger than 3 in the degree of polydispersity.
Claim 11
Dependent Claim
29 words
A resist material according to claims 5 or 6, further comprising a photosensitive cross-linking agent which is a bis-azide compound and amounts to 0.1-50% by weight of said polymer.
Claim 12
Dependent Claim
23 words
A resist material according to claim 9, wherein said bis-azide compound is selected from the group consisting of 4,4-diazidechalcone, 2,6-di-(4'-azidebenzylidene)-cyclohexanone, 2,6-di-(4'-azidebenzylidene)-4-methylcyclohexanone and 2,6-di-(4'-azidebenzylidene)-4-hydroxycyclohexanone.
Claim 13
Dependent Claim
23 words
A resist material according to claim 1, wherein said bis-azide compound is selected from the group consisting of 4,4-diazidechalcone, 2,6-di-(4'-azidebenzylidene)-cyclohexanone, 2,6-di-(4'-azidebenzylidene)-4-methylcyclohexanone and 2,6-di-(4'-azidebenzylidene)-4-hydroxycyclohexanone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-13 | 1989-07-15 | 1990-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-13 | 1993-07-15 | 1994-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-13 | 1997-07-15 | 1998-01-14 | $7700.00 | Window Closed / Lapsed |